Filtern
Dokumenttyp
- Vortrag (10) (entfernen)
Sprache
- Englisch (10)
Referierte Publikation
- nein (10) (entfernen)
Schlagworte
- Acoustic emission (10) (entfernen)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (7)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (4)
- 2 Prozess- und Anlagensicherheit (3)
- 2.1 Sicherheit von Energieträgern (3)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (3)
- 9 Komponentensicherheit (3)
- 9.6 Additive Fertigung metallischer Komponenten (3)
- 8.4 Akustische und elektromagnetische Verfahren (2)
- 8.6 Faseroptische Sensorik (2)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
Eingeladener Vortrag
- nein (10)
During the past 20 years, innovative developments in concrete technology have enabled the production of ultra-high performance fibre reinforced concretes (UHPFC) for the protection and preservation of concrete structures. The main characteristics of UHPFC comprise high compressive and flexural strength as well as high ductility compared to normal strength, normal weight concrete (NSC). This paper focuses on the analysis of crack formation and crack propagation in UHPFC under tensile loading under quasistatic conditions by using acoustic emission (AE) and optical deformation analysis (ODA).
AE is a non-destructive technique to monitor the development of micro structural damage processes caused by external forces. In this context, AE allows for a continuous monitoring of changes in the microstructure (cracks) over time and the corresponding localisation by appropriate algorithms. The AE measurements were performed along with ODA at the surface of the samples in order to analyse the deformation behaviour of the samples and the crack propagation.
For the tests, a UHPFC reference mixture was developed and tested with three different volume percentages of steel fibres (1.0 V.-%, 2.0 V.-%, and 3.0 V.-%). This paper shows that the application of AE is a suitable method to analyse the crack propagation in UHPFC specimens under tensile loading and to localise the crack initiation. Furthermore, insights into the failure mechanism of the fibres are offered by the analysis of the signals of the AE measurements, which allows for a better understanding of UHPFC and its general performance.
Pipelines and industrial piping systems are particularly relevant regarding technical safety, availability and maintenance. Large flow rates of hazardous substances imply that even smallest leakages can lead to high environmental impacts. Therefore, and to ensure the availability of infrastructure, an early detection and localization of potentially hazardous degradations to the walls (e.g. cracks, pittings, sedimentation, etc.) of the containments is necessary. However, in many cases it is not feasible to equip pipelines with a large number of point sensors at reasonable expense.
The principle of distributed fibre optic sensing relies on one single optical fibre, which simultaneously acts as a spatially continuous sensor as well as the signal transducer. Therefore, extensive structures can be provided with this type of sensor with comparatively low efforts.
As a consequence, monitoring oil and gas pipelines using distributed fibre optic sensors is on the upswing. Besides the established methods to measure temperature and strain, distributed acoustic sensing (DAS) has lately received considerable attention as a means to detect and localize third party threats to pipelines (approach of vehicles, digging, mechanical manipulation).
The so far not utilized potential of DAS as a means for continuous condition monitoring of pipes by detecting and localizing acoustic signals that point to certain damage scenarios, is currently under investigation in an interdisciplinary research project at BAM (AGIFAMOR, Ageing Infrastructures – Fibre Optic Monitoring of Pipes).
In order to qualify distributed acoustic fibre optic sensors for this application area, we especially focus on detecting and identifying the relevant acoustic emissions of interesting degradations as well as on the optimal way of application of the optical fibres to the specimen to achieve an optimal signal transmission of acoustic signals.
Accumulation of fibre breaks under time-dependent loads in CFRP materials of pressure vessels
(2017)
For the moment, there is no existing method to quantify the time-dependent effect on carbon fibre pressure vessels or composite pressure vessels (CPV) in general. Hence, BAM started to investigate how to proof this phenomenon. Several researches has been done and discovered that it is possible for aged pressure vessels to have higher burst pressure value than a new vessels. However, the scientific explanation behind is still an on-going research. Whether the existing model can be used or using another measurement method to gain more data is still in question. Therefore, it is required to find a suitable method to explain such phenomenon and even develop furthermore to give a strength criterion for certain types of pressure vessels
Acoustic emission testing
(2018)
Four-point bending tests were carried out to analyze the acoustic characteristics of damage development in pipe segments made of steel, grade S355J2H, being 2.5 m long with an outer diameter of 168 mm and 16 mm wall thickness. To induce stable crack growth, the pipe segments were pre-damaged by a 90°circumferential notch in the middle of the pipe length. While the pipe was quasi-statically loaded, microscopic damage and plastic deformation accumulated to form a macroscopic crack that grew through the pipe wall until leakage. For acoustic emission (AE) monitoring, four broadband sensors of type VS 900 M were mounted close to the notch. Continuous AE signal detection was performed by the non-threshold method. Advantages and disadvantages of the non-threshold AE monitoring compared to a commonly employed method analyzing only signals exceeding a predefined threshold are discussed. The results of AE analysis are compared to additional information on the crack growth detected by the direct current potential drop (DCPD) technique. These studies were carried out in the course of the interdisciplinary research project AGIFAMOR, Ageing infrastructures - distributed acoustic monitoring of pipes at BAM.
Feasibility study: Continuous monitoring of pipes using distributed acoustic and fibre optic sensors
(2018)
The feasibility study „AGIFAMOR. Ageing infrastructures – distributed acoustic monitoring of pipes” is an interdisciplinary research project at BAM internally financed from 2015 to 2018. Therefore, the quite young fibre optic sensing technology of distributed acoustic sensing (DAS) was investigated to possibly be extended towards a global condition monitoring system for pipelines operating in real time.
DAS is a highly dynamic fibre optic sensing technology based on the method of coherent optical time domain reflectometry (C-OTDR). DAS allows capturing strain changes in the range of kHz. For the experimental work, the most suitable application yielding an optimum sensitivity was proven by wrapping a standard single-mode silica fibre around the pipe.
The DAS sensitivity was investigated regarding the detection of 1) incidents that initiate propagation of acoustic waves in the pipe wall, 2) changes inside the pipeline causing altered flow and 3) damage development in the pipe wall. Therefore, several testing setups in laboratory as well as in real scale were realized. For comparison purposes, experiments were accompanied by acoustic emission analyses and by measurements with accelerometers.
DAS was found to be very sensitive to gas ignition and its propagation across the pipe. Furthermore, the ability of DAS to detect and localize acoustic signals associated with pipeline leakage was demonstrated. The detection of crack formation and propagation within the pipe wall by means of DAS was studied during bending tests on several pipe segments, but was not proven so far with certainty. As expected, these studies turned out as the most difficult challenge due to the random occurrence and transient nature of microscopic damage phenomena.
Acoustic emission and ultrasonic monitoring of a prestressed concrete bridge in its final years
(2021)
Many European bridges built in the 1950s, 60s and 70s must be re-placed in the next decade due to structural deficiencies, insufficient load capacity or other issues. However, the existing bridges must be used for another couple of years even if flaws and damages already have been detected.
In Germany, several prestressed concrete bridges have been instrumented with acoustic emission detection systems to detect wire breaks and to provide early warning signs before failure. To evaluate and interpret the consequences of wire breaks additional instrumentation and accompanying measures as finite element modeling are required.
At a bridge in southern Germany we have complemented such a system with active ultrasonic monitoring. Repeated ultrasonic measurements are evaluated with a very sensible algorithm called coda wave interferometry. This method, inspired by seismology, has been shown to deliver early warning signs in lab experiments. Large volumes of concrete can be monitored with a limited network of ultrasonic transducers. We will report on the installation, capabilities, and lim-itations as well as first results.
Typically, the near-eutectic Al-Si alloys consist of highly interconnected three-dimensional network of the eutectic Silicon (Si) and intermetallics embedded into Aluminium (Al) matrix. For further improvement of the mechanical properties of such alloys, often, one single ceramic reinforcement phase, e.g. silicon carbide (SiC) or aluminium oxide (Al2O3) in the form of fibres or particles is added. However, hybrid reinforcements (fibres and particles) can further improve wear resistance and fracture toughness, and additionally, reduce anisotropy of the material. The engineering of metal matrix composites (MMC) for specific application requirements benefits from a comprehensive knowledge of the failure behaviour. Therefore, damage evolution under compression was investigated on:
- pure near-eutectic AlSi12CuMgNi matrix alloy
- type I: matrix reinforced with random-planar oriented Al2O3 short fibres (15 vol.%)
- type II: matrix reinforced with random-planar oriented Al2O3 short fibres (7 vol.%) and additional SiC particles (15 vol.%)
The analysis of damage mechanism was carried out in two rather independent but complementary studies. First, selected sister samples of every material were exposed to quasi-static compression (traverse control). The compression tests were interrupted at different strain levels. Miniature cylinders with a diameter of 1mm were extracted from the pre-strained samples and investigated by synchrotron computed tomography (SX-µCT) with a spatial resolution of about 0.7 µm. For the pure matrix alloy, microcracks are confined to the intermetallic particles and to the eutectic Si, hence no damage was observed in the Aluminium. The composite type II revealed a more effective strain accumulation (less damage) than type I at low plastic strain (up to 5 %), but a more catastrophic damage development due to cracking of the SiC clusters at higher strain levels.
The second approach to study the damage initiation and accumulation in the materials subjected to compressive load was Acoustic Emission (AE) analysis. In this case the in-situ monitoring of the acoustic emission signal was performed during compression tests on specimens with dimension of several mm. For all three material types, AE activity set at 2% strain. Differences in AE behaviour of the three materials was proven based on AE hitrate, signal peak amplitudes as well as weighted peak frequencies (WPF). Future work focuses on combination of AE and SX-µCT aiming for more detailed knowledge on damage mechanism of metal matrix composites.
Due to increasing ageing, deterioration and loading , several prestressed concrete bridges bulit in the 1950ies and 1960ies need monitoring. Recently several bridges have sucesssfully equipped with acoustic emission sensing system. BAM works together with several universities on an add onn: Active ultrasonic monitoring combined with coda wave interferometry will help to detect subtle changes and precursors fo failure earlier than other methods.
The project "SealWasteSafe" of the Bundesanstalt für Materialforschung und -prüfung (Berlin) deals with sealing structures applied for underground disposal of nuclear waste from two perspectives: material improvement for application in sealing constructions and feasibility study regarding multi-sensor approaches to ensure quality assurance and long-term monitoring.
One specimen of 150 l made of alkali-activated material, which was found innovative and suitable for sealing constructions based on preliminary laboratory studies, and another one made of conventional salt concrete, are manufactured with an integrated multi-sensory setup for quality assurance and long-term-monitoring. The specimens were left in their cast form and additionally thermally insulated to simulate the situation in the repository. The multi-sensory concept comprises RFID technology embedded in the specimens suppling material temperature and moisture measurements, integrated distributed fibre optic sensing allowing strain measurement and acoustic emission testing for monitoring crack formation. Overall, the suitability and the functionality of the sensors embedded into and attached to strongly alkaline (pH > 13 for the AAM) and salt corrosive (NaCl) environment was proven for the first 672 h.
First RFID measurement succeeded after 626 h for the alkali-activated material and after 192 h for the conventional salt concrete. Strain measurement based on fibre optic sensing turned out the alkali-activated material (> 1 mm/m) undergoing approximately twice the compression strain as the salt concrete (< 0.5 mm/m). In contrast, the acoustic emission first and single hits representing crack formation in numbers, was found for alkali-activated material half of that detected at the salt concrete.