Filtern
Dokumenttyp
- Vortrag (14) (entfernen)
Sprache
- Englisch (9)
- Deutsch (4)
- Mehrsprachig (1)
Referierte Publikation
- nein (14) (entfernen)
Schlagworte
- 316L (14) (entfernen)
Organisationseinheit der BAM
- 5 Werkstofftechnik (9)
- 8 Zerstörungsfreie Prüfung (7)
- 9 Komponentensicherheit (7)
- 5.1 Mikrostruktur Design und Degradation (6)
- 5.2 Metallische Hochtemperaturwerkstoffe (6)
- 8.5 Röntgenbildgebung (5)
- 9.4 Integrität von Schweißverbindungen (5)
- 8.4 Akustische und elektromagnetische Verfahren (2)
- 9.3 Schweißtechnische Fertigungsverfahren (2)
Eingeladener Vortrag
- nein (14)
The present study deals with the experimental characterization of short crack propagation in SLM (selective-laser-melting) manufactured stainless steel. More specifically, the determination of cyclic R-curves is discussed. This describes the dependency of the crack propagation threshold on crack growth during the short crack propagation stage. For metals, the threshold, starting at a material-intrinsic value, increases until it reaches a value independent of the crack length due to crack closure phenomena which build up at that stage. The cyclic R-curve, when used in the frame of a cyclic R curve analysis, characterizes the resistance of a material to fatigue crack growth and the ability to arrest a physically short crack. Thus, it is the link between classical fatigue and fracture mechanics. In the high-cycle-fatigue range, the short crack propagation stage dominates the overall lifetime, i.e., the number of cycles until failure. Below the fatigue limit crack arrest of hitherto propagable micro-cracks will occur. The effort for the experimental characterization of the short fatigue crack propagation behavior and the cyclic R-curve is very high compared to experiments on long crack propagation. A very exact measurement of crack extension is required, since small increments need to be depicted. Pre-cracking must leave a closure free initial crack, since closure must be build up only by the cyclic R-curve. The closure-free status is achieved by compression pre-cracking. The aim of the present study is an insight into the influence of an AM process on the short crack propagation threshold. Cyclic R-curves are experimentally determined at different load-ratios for 316L austenitic steel specimens produced by SLM and conventional manufacturing. Residual stresses are measured in the crack plane and their influence on the cyclic R-curve is discussed.
Additive Fertigung hat in den letzten Jahren aufgrund der hohen Flexibilität stark an Bedeutung gewonnen. Insbesondere in der Luft- und Raumfahrttechnik werden hohe Anforderungen an die Qualitätskontrolle additiv gefertigter Bauteile gestellt. Teile die mit dem selektiven Laserschmelzen (SLM) hergestellt werden, bilden schon währen des Fertigungsprozesses Poren oder Risse aus. Aus diesem Grund ist die zerstörungsfreie Prüfung jedes Bauteils notwendig. Erste Versuche haben gezeigt, dass die ex-situ Wirbelstromprüfung von SLM-Bauteilen mit hochauflösenden MR Sonden möglich ist und dass Fehler im Bereich von einiger µm detektiert werden können. In dem Vortrag wird eine automatisierte in-situ Wirbelstromprüfung von SLM-Bauteilen vorgestellt. Für die Prüfung wird eine Vielzahl hochauflösender MR Sensoren verwendet, um die benötige hohe Ortsauflösung bei gleichzeitig kurzer Prüfzeit zu erreichen. Zusätzlich werden klassische Methoden der Signalverarbeitung verwendet, um die Kosten und die Komplexität des Systems trotz hoher Prüffrequenz zu minimieren. Das vorgestellte System kann in der Zukunft helfen automatisiert Prüfberichte zu generieren, den SLM-Prozess zu kontrollieren oder automatisiert Fehlstellen auszuheilen.
Additive Fertigung hat in den letzten Jahren aufgrund der hohen Flexibilität stark an Bedeutung gewonnen. Insbesondere in der Luft- und Raumfahrttechnik werden hohe Anforderungen an die Qualitätskontrolle additiv gefertigter Bauteile gestellt. Teile die mit dem selektiven Laserschmelzen (SLM) hergestellt werden, bilden schon währen des Fertigungsprozesses Poren oder Risse aus. Aus diesem Grund ist die zerstörungsfreie Prüfung jedes Bauteils notwendig. Erste Versuche haben gezeigt, dass die ex-situ Wirbelstromprüfung von SLM-Bauteilen mit hochauflösenden MR Sonden möglich ist und dass Fehler im Bereich von einiger µm detektiert werden können. In dem Vortrag wird eine automatisierte in-situ Wirbelstromprüfung von SLM-Bauteilen vorgestellt. Für die Prüfung wird eine Vielzahl hochauflösender MR Sensoren verwendet, um die benötige hohe Ortsauflösung bei gleichzeitig kurzer Prüfzeit zu erreichen. Zusätzlich werden klassische Methoden der Signalverarbeitung verwendet, um die Kosten und die Komplexität des Systems trotz hoher Prüffrequenz zu minimieren. Das vorgestellte System kann in der Zukunft helfen automatisiert Prüfberichte zu generieren, den SLM-Prozess zu kontrollieren oder automatisiert Fehlstellen auszuheilen.
Microstructure ageing of stainless steel AISI 316L manufactured by selective laser melting (SLM)
(2019)
Additive manufacturing (AM) processes, such as SLM, offer a variety of advantages compared to conventional manufacturing. Today AM parts are still comparatively less cost-effective if they are manufactured in large quantities. To make the AM parts more cost-efficient, the AM process has to be improved. It requires a good understanding of microstructure formation, microstructure-property-relations and ageing processes affected by different loads.
In this work the ageing behavior of SLM manufactured AISI 316L stainless steel is evaluated. The microstructure effected by mechanical, thermal and corrosive loads are investigated and compared to as-built microstructure. Tensile tests are used for mechanical ageing. For thermal and corrosive loads the typical application conditions of 316L apply. The methods of microstructure investigation include SEM, TEM, CT and EBSD. The main object of this work is the description of microstructure and ageing processes of AM parts.
Additive manufacturing (AM) offers diverse advantages compared to conventional manufacturing. In this work the microstructure of austenitic steel 316L, manufactured with Selective Laser Melting (SLM), was analyzed and compared to microstructure of 316L hot rolled material. Methods used for analysis are microprobe, optical microscopy and electron backscatter diffraction.
Additively manufactured metallic materials have already started to find application in safety-relevant components. However, this has only happened for certain materials and specific applications and loading conditions, since there is still an extensive lack of knowledge as well as of historical data regarding their mechanical behaviour. This contribution aims to address this lack of understanding and historical data concerning the creep behaviour of the austenitic stainless steel 316L manufactured by Laser-Powder-Bed-Fusion (L-PBF) and the low-cycle-fatigue behaviour of the titanium alloy Ti-6Al-4V manufactured by Laser-Metal-Deposition (LMD). Furthermore, it aims to assess their mechanical behaviour against their conventional counterparts. With that in mind, specimens from conventional and additive materials are tested and their mechanical behaviour analysed based on characteristic curves. To understand the damage behaviours the materials are characterized by destructive and non-destructive techniques before and after failure.
Diese Untersuchung beschäftigt sich mit der Charakterisierung von Kurzrisswachstum in mittels Laser-Pulverbett-Verschmelzen (LPBF - Laser Powder Bed Fusion) hergestelltem rostfreien austenitischen Stahl. Spezifischer wird die Ermittlung zyklischer R-Kurven untersucht. Diese beschreiben den Aufbau des Widerstands gegen Ermüdungsrisswachstum - d.h. des Schwellenwertes - aufgrund von Rissschließeffekten bei physikalisch kurzen Rissen. Mit Hilfe der zyklischen R-Kurven kann die Fähigkeit eines Bauteils, physikalisch kurze Risse zu arretieren, charakterisiert werden. Wir verfügen damit über eine Schnittstelle zwischen klassischer Ermüdung und Bruchmechanik. Das ist gerade auch für additiv gefertigte (AM – Additive Manufacturing) Materialien von Interesse. Diese weisen prozessintrinsische Defekte auf, die als Initiierungsstellen kurzer Ermüdungsrisse agieren. Im Rahmen der experimentellen Untersuchungen wurden zyklische R-Kurven für konventionellen und LPBF AISI-316L-Stahl ermittelt. Insbesondere wurde der Einfluss verschiedener Wärmebehandlungen (WB1: 450°C, WB2: 800°C und WB3: 900°C) auf das Wachstumsverhalten physikalisch kurzer Risse im LPBF-Material untersucht. Aufgrund hoher Eigenspannungen war die Ermittlung des Kurzrisswachstumsverhaltens bei WB1 nicht möglich. Für WB2 und WB3 ergaben sich sehr unterschiedliche zyklische R-Kurven. Untersuchungen der Eigenspannungen, der Bruchfläche (insbesondere der Rauheit) und der Mikrostruktur sollen die Ursachen für das unterschiedliche Verhalten erklären. Die Ergebnisse werden mit den Verhältnissen in konventionellem Material verglichen.
Fracture mechanics is a key to fatigue assessment in AM metal components. Short fatigue cracks are initiated at defects and pronounced surface roughness intrinsic to AM. The subsequent crack-propagation is strongly influenced by microstructural interactions and the build-up of crack-closure. The aim of the present study is to give an insight into short-crack propagation in AM-metals. Fatigue crack propagation resistance curves were determined experimentally for AISI 316L manufactured by Laser Powder Bed Fusion (L-PBF) which was heat treated at three different temperatures. Differences in the build-up of the fatigue-crack propagation threshold in between the L-PBF specimens and compared to wrought material are due to the residual stress states, a pronounced roughness of the crack-faces in the L-PBF specimens and phase transformation in the vicinity of the crack-tip, resulting in increased crack-closure. This, together with crack-branching found along the crack path, enhances the resistance to the propagation of fatigue cracks.
Eine kritische Aufgabe im Rahmen der Etablierung von Prozess-Struktur-Eigenschafts-Performance-Beziehungen bei der additiven Fertigung (AM) von Metallen ist die Ermittlung von zuverlässigen und gut dokumentierten Kennwerten zum Materialverhalten sowie das Schaffen von Wissen über die Struktur-Eigenschafts-Korrelation. Schließlich ist dies die Grundlage für die Entwicklung gezielterer Prozessoptimierungen und zuverlässigerer Lebensdauer-Vorhersagen. In diesem Zusammenhang zielt dieser Beitrag darauf ab, Daten und Erkenntnisse über das Kriechverhalten des austenitischen Edelstahls 316L zu liefern, der mittels Laser-Powder-Bed-Fusion (L-PBF) hergestellt wird. Um dieses Ziel zu erreichen, wurden Proben aus konventionellem warmgewalztem sowie AM-Material gemäß den bestehenden Normen für konventionelles Material geprüft und vor und nach dem Versagen mikrostrukturell charakterisiert. Die Probekörper wurden aus einzelnen Blöcken des AM-Materials gefertigt. Die Blöcke wurden mit einer Standard-Scan- und Aufbaustrategie hergestellt und anschließend wärmebehandelt. Das Kriechverhalten wird anhand der Kriechlebensdauer und ausgewählter Kriechkurven und Kennwerte beschrieben und vergleichend bewertet. Der Einfluss von Defekten und Mikrostruktur auf das Materialverhalten wird anhand von zerstörenden und zerstörungsfreien Auswertungen an ausgewählten Proben analysiert. Der AM-Werkstoff zeigt kürzere Kriechlebensdauern, erreicht das sekundäre Kriechstadium deutlich schneller und bei geringerer Dehnung und weist eine geringere Kriechduktilität im Vergleich zu seinem konventionellen Gegenstück auf. Das Kriechschädigungsverhalten des AM-Werkstoffs ist eher mikrostruktur- als defektgesteuert und ist durch die Bildung intergranularer Kriechrisse gekennzeichnet. Als kritische Merkmale werden die Versetzungsdichte sowie die Versprödung der Korngrenzen identifiziert. Die Mikro-Computertomographie (µCT) erweist sich als Alternative zur Metallographie, um die Kriechschädigung zu analysieren.