The contribution describes a newly developed software tool for crack identification and selection in Modified Varestraint Transvarestraint (MVT) testing. From the digital crack information, in addition to the classical results, such as Total Crack Length (TCL) and Maximum Crack Length (MCL), advanced evaluations can be applied, taking into account the loading and welding parameters. A numerical parameter study is conducted to demonstrate how the isolated variation of individual welding and loading parameters, affects the crack lengths that can potentially be expected based on the machine specifics. An alternative crack criterion is presented that evaluates the crack formation in relation to the machine behavior. Some examples demonstrate the possibilities and limitations of the approach. The criterion can be used to compare and transfer the results of different varestraint test variants.
The use of Low Transformation Temperature (LTT) filler materials is an innovative way to reduce welding residual stresses. The generation of compressive residual stresses in the weld and heat-affected zone can lead to an improvement of the fatigue life of high-strength welds. However, high-alloy filler metals can be prone to solidification cracking. Two important LTT alloys were evaluated under variable welding and loading parameters using the Modified Varestraint/Transvarestraint (MVT) test. Initially conflicting results were interpreted using a newly developed image-based crack detection routine [1]. Based on the melt pool dimensions, the shape of the isotherms is reconstructed, and the theoretical crack growth along numerically determined crystallization paths is considered in relation to the cracks observed. Decreasing welding speeds with simultaneously higher heat input promote crack formation with increasing strain rate.
It was found that there is a systematic dependence of the crack growth on the welding parameters as well as on the load. Decreasing welding speeds with simultaneously higher heat input promote crack formation with increasing strain rate.
Based on the results, a new crack criterion was finally selected which allows an extended assessment of the material behavior during the MVT-test. The threshold introduced can quantify the dependencies of the crack formation on the welding and testing parameters, which could not be comprehensively described with the conventional evaluation. In principle, the evaluation routine can also be transferred to other Varestraint or externally loaded hot cracking tests.