Filtern
Erscheinungsjahr
- 2023 (93) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (93) (entfernen)
Sprache
- Englisch (89)
- Deutsch (3)
- Mehrsprachig (1)
Schlagworte
- Additive manufacturing (10)
- Machine learning (6)
- X-ray computed tomography (6)
- Non-destructive testing (5)
- Concrete (4)
- LIBS (4)
- Microstructure (4)
- Thermography (4)
- Electron backscatter diffraction (EBSD) (3)
- Mechanical Engineering (3)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (93) (entfernen)
Paper des Monats
- ja (9)
An observation of the fracture process in front of the crack tip inside a dentin sample by means of ex-situ X-ray computed tomography after uniaxial compression at different deformation values was carried out in this work. This ex-situ approach allowed the microstructure and fracturing process of human dentin to be observed during loading. No cracks are observed up to the middle part of the irreversible deformation in the samples at least visible at 0.4μm resolution. First cracks appeared before the mechanical stress reached the compression strength. The growth of the cracks is realized by connecting the main cracks with satellite cracks that lie ahead of the main crack tip and parallel its trajectory. When under the stress load the deformation in the sample exceeds the deformation at the compression strength of dentin, an appearance of micro-cracks in front of the main cracks is observed. The micro-cracks are inclined (~60°) to the trajectory of the main cracks. The further growth of the main cracks is not realized due to the junction with the micro-cracks; we assume that the micro-cracks dissipate the energy of the main crack and suppressed its growth. These micro-cracks serve as additional stress accommodations, therefore the samples do not break apart after the compression test, as it is usually observed under bending and tension tests.
In this work, the thermal properties of ternary Li₃ₓCo₇₋₄ₓSb₂₊ₓO₁₂ solid solutions are studied for different concentrations in the range 0 ≤ x ≤ 0.7. Samples are elaborated at four different sintering temperatures: 1100, 1150, 1200 and 1250 °C. The effect of increasing the content of Li⁺ and Sb⁵⁺, accompanied by the reduction of Co²⁺, on the thermal properties is studied. It is shown that a thermal diffusivity gap, which is more pronounced for low values of x, can be triggered at a certain threshold sintering temperature (around 1150 °C in this study). This effect is explained by the increase of contact area between adjacent grains. Nevertheless, this effect is found to be less pronounced in the thermal conductivity. Moreover, a new framework for heat diffusion in solids is presented that establishes that both the heat flux and the thermal energy (or heat) satisfy a diffusion equation and therefore highlights the importance of thermal diffusivity in transient heat conduction phenomena.
AbstractLithium‐ion cells connected in series are prone to an electrical safety risk called overdischarge. This paper presents a comprehensive investigation of the overdischarge phenomenon in lithium‐ion cells using operando nondestructive imaging. The study focuses on understanding the behavior of copper dissolution and deposition during overdischarge, which can lead to irreversible capacity loss and internal short‐circuits. By utilizing synchrotron X‐ray computed tomography (SXCT), the concentration of dissolved and deposited copper per surface area is quantified as a function of depth of discharge, confirming previous findings. The results also highlight for the first time a nonuniform distribution pattern for copper deposition on the cathode. This research provides insights for safer battery cell design.
Laser powder bed fusion of metallic components (PBF-LB/M) is gaining acceptance in industry. However, the high costs and lengthy qualification processes required for printed components create the need for more effective in-situ monitoring and testing methods. This article proposes multispectral Optical Tomography (OT) as a new approach for monitoring the PBF-LB/M process. Compared to other methods, OT is a low-cost process monitoring method that uses long-time exposure imaging to observe the build process. However, it lacks time resolution compared to expensive thermographic sensor systems. Monochromatic OT (1C-OT) is already commercially available and observes the building process layer-wise using a single wavelength window in the NIR range. Multispectral OT (nC-OT) utilizes a similar setup but can measure multiple wavelength ranges per location simultaneously. By comparing the classical 1C-OT and nC-OT approaches, this article examines the advantages of nC-OT (two channel OT and RGB-OT) in reducing the false positive rate for process deviations and approximating maximum temperatures for a better comparison between different build processes and materials. This could ultimately reduce costs and time for part qualification. The main goal of this contribution is to assess the advantages of nC-OT compared to 1C-OT for in-situ process monitoring of PBF-LB/M.
Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods, or jackets. These components are typically constructed using submerged arc welding (SAW) with high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen-assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicates the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam/layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with over 20 passes and a seam length of 1000 mm. Additional welded stiffeners simulated the effect of a high restraint, to achieve critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of up to 48 h after the completion welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modeling allowed the qualitative estimation of the hydrogen diffusion in the weld. No noticeable HAC occurrence was identified and confirms the high cracking resistance of the investigated material. Finally, the applicability of the MWT concept should be critically discussed.
A novel DAS setup based on geometric phases in coherent heterodyne detection is applied for the first time to the characterisation of the Earth’s subsurface. In addition, an optimisation of the proposed setup in terms of its spatial resolution is also presented for the first time. The surface waves are generated by strong blasts of 25 kg of explosives at a dedicated test site. A 10 km dark fiber link in the vicinity of the test site connected to the test setup records the resulting strain signals. The spike-free and low-noise strain data thus obtained minimize post-processing requirements, making the setup a candidate for real-time seismic monitoring. An analysis of the dispersion characteristics of the generated surface waves is performed using a recently reported optimised seismic interferometric technique. Based on the dispersion characteristics, the shear wave velocities of the surface waves as a function of the depth profile of the Earth’s crust are determined using an optimised evolutionary algorithm.
Human factors (HFs) are a frequently mentioned topic when talking about the reliability of non-destructive testing (NDT). However, probability of detection (POD), the commonly used measure of NDT reliability, only looks at the technical capability of an NDT system to detect a defect.
After several decades of research on the influence of HFs on NDT reliability, there is still no commonly accepted approach to rendering HFs visible in reliability assessment. This paper provides an overview of possible quantitative and qualitative methods for integrating HFs into the reliability assessment. It is concluded that reliability assessment is best carried out using both quantifiable and non-quantifiable approaches to HFs.
The digitalization of quality control processes and the underlying data infrastructures for safety relevant components, such as hydrogen pressure vessels, plays a significant role in the transition towards Industry 4.0. In the current safety regulations for hydrogen pressure vessels, there is no established concept for structural health monitoring. The development of a reliable structural health monitoring methodology for monitoring the structural integrity of pressure vessels enables a fast-forward transition from personnel- and costintensive recurring inspections, a.k.a. periodic maintenance, to predictive maintenance. In the work presented; we investigated the application of ultrasonic guided wave propagation to monitor and assess the condition of Type IV composite overwrapped pressure vessel (COPV). A sensor network of fifteen piezo-electric wafers is placed on the carbon fibre reinforced composite cylinder. Five different artificial damage configurations are created by gluing two different weight blocks on three different locations. The database containing measured guided wave data sets is enriched by two different boundary conditions. We utilized an open-source software, openBIS labnotebook, to store and analyse experimental datasets. The guided wave ultrasonic signals were investigated and analysed by using commonly used ultrasonic features (e.g., amplitude, frequency, time of flight) as well as non-traditional time-series features (kurtosis, skewness, variance). The features were used to calculate damage index and the detection performance for the results has been evaluated. The results suggest that both traditional and non-traditional features assume significant importance in artificial damage detection. The future works will additionally involve the impacts of operational conditions, such as periodic pressure variations temperature loadings as well as material degradations.