Filtern
Erscheinungsjahr
- 2018 (17) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (17)
Sprache
- Englisch (17)
Referierte Publikation
- ja (17) (entfernen)
Schlagworte
- Mechanochemistry (8)
- In situ (4)
- XRD (4)
- In situ studies (2)
- MOF (2)
- Amyloid (1)
- BET (1)
- Barium (1)
- Beschichtung (1)
- Bioimaging (1)
Organisationseinheit der BAM
- 6 Materialchemie (17)
- 6.3 Strukturanalytik (17)
- 1 Analytische Chemie; Referenzmaterialien (2)
- 1.0 Abteilungsleitung und andere (1)
- 1.1 Anorganische Spurenanalytik (1)
- 1.2 Biophotonik (1)
- 1.8 Umweltanalytik (1)
- 4 Material und Umwelt (1)
- 4.2 Material-Mikrobiom Wechselwirkungen (1)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (1)
Proline has been widely used for various cocrystallization applications, including pharmaceutical cocrystals. Combining enantiopure and racemic flurbiprofen and proline, we discovered 18 new crystal structures. Liquid-assisted grinding proved highly efficient to explore all the variety of crystal forms. A unique combination of stateof-the-art characterization techniques, comprising variable temperature in situ X-ray diffraction and in situ ball-milling, along with other physicochemical methods and density functional theory calculations, was indispensable for identifying all the phases. Analyzing the results of in situ ball-milling, we established a stepwise mechanism for the formation of several 1:1 cocrystals via an intermediate 2:1 phase. The nature of the solvent in liquidassisted grinding was found to significantly affect the reaction rate and, in some cases, the reaction pathway.
Equipping ZIF particles with a polyelectrolyte membrane provides functional groups at their interface, enabling further conjugations necessary for applications such as targeted drug delivery. Previous approaches to coat ZIF particles with polyelectrolytes led to surface corrosion of the template material. This work overcomes previous limitations by performing a Layer-by-Layer (LbL) polyelectrolyte coating onto ZIF-8 and ZIF-67 particles in nonaqueous environment. Using the 2-methylimidazolium salt of polystyrensulfonic acid instead of the acid itself and polyethyleneimine in methanol led to intact ZIF particles after polyelectrolyte coating. This was verified by electron microscopy. Further, zetapotential and atomic force microscopy measurements confirmed a continuous polyelectrolyte multilayer built up. The here reported adaption to the well-studied (LbL) polyelectrolyte selfassembly process provides a facile method to equip ZIF particles with a nanometer thin polyelectrolyte multilayer membrane.
Water vapor sorption surface areas and sorption energies of untreated
and thermally modified Norway spruce [Picea abies (L.) Karst.], sycamore maple (Acer pseudoplatanus L.) and European ash (Fraxinus excelcior L.) were investigated by means of dynamic vapor sorption (DVS) measurements and excess surface work (ESW) evaluation method, respectively. Adsorption and desorption experiments in the hygroscopic range and desorption tests from water saturation were conducted.
Thermodynamically, ESW is the sum of the surface free energy and the isothermal isobaric work of sorption. From the amount adsorbed in the first Minimum a specific surface area similar to the BET surface area can be obtained. The results show that untreated spruce has a significantly higher specific water vapor Sorption surface and sorption energy compared to both hardwoods maple and ash. Thermal modification of the woods leads to a significant reduction of water vapor Sorption surface and sorption energy. The determined surface area and energy are higher in desorption direction than in adsorption direction, whereby the highest values in Desorption direction from water saturation, especially for maple and ash, were obtained.
The surface areas calculated by means of the ESW method are similar to the surface areas calculated by means of the BET method, particularly in adsorption direction.
We present an in situ triple coupling of synchrotron X-ray diffraction with Raman spectroscopy, and thermography to study milling reactions in real time. This combination of methods allows a correlation of the structural evolution with temperature information. The temperature information is crucial for understanding both the thermodynamics and reaction kinetics. The reaction mechanisms of three prototypical mechanochemical syntheses, a cocrystal formation, a C@C bond formation (Knoevenagel condensation), and the formation
of a manganese-phosphonate, were elucidated. Trends in the temperature development during milling are identified. The heat of reaction and latent heat of crystallization of the product contribute to the overall temperature increase. A decrease in temperature occurs via release of, for example, water as a byproduct.
Solid and liquid intermediates are detected. The influence of the mechanical impact could be separated from temperature effects caused by the reaction.
A series of Ca-based coordination polymers were prepared mechanochemically by milling Ca(OH)2 with phthalic acid (H2oBDC), isophthalic acid (H2mBDC), and terephthalic acid (H2pBDC). The hydrated compounds [Ca(oBDC)(H2O)], [Ca(mBDC)(H2O)3.4], and [Ca(pBDC)(H2O)3] were prepared for the first time via mechanochemical routes. The refined structures were validated by extended X-ray absorption data. The new dehydrated compound [Ca(oBDC)] (1-H2O), obtained after the thermal post-treatment of 1 in a reversible phase transition process, was determined ab initio based on the powder X-ray diffraction (PXRD) data. The materials were thoroughly characterized using elemental analysis, thermal analysis, and spectroscopic methods: magic-angle spinning NMR and attenuated total reflection-infrared spectroscopy. The specific surface areas and sorption properties of the hydrated and dehydrated samples were determined using the isotherms of gas sorption and dynamic vapor sorption measurements.
New Ca- and Sr-based coordination polymers (CPs) were mechanochemically synthesized by milling metal hydroxide samples (M = Ca, Sr) with tetrafluorophthalic acid (H2oBDC-F4) and isophthalic acid (H2mBDC). [Ca(oBDC-F4)(H2O)2] (1) exhibits a small surface area which is slightly increased after removing the crystal water. On the other hand, the hydrated sample of the nonfluorinated [Sr(mBDC)(H2O)3.4] (2) reveals a small BET surface area which remains unchanged even after the release of crystal water via thermal treatment. The new compounds 1 and 2 are similar to their Sr- and Ca-analogs, respectively. These findings are confirmed by thermal analysis, MAS NMR, and ATR-IR measurements, in addition to the Le Bail refinements for the measured powder X-ray data of 1 and 2. Ca- and Sr-CPs based on perfluorinated dicarboxylic systems and their nonfluorinated analogs diverse in structural and chemical properties depending on the geometries of the organic linkers and the presence of fluorine atoms. The fluorinations of organic ligands lead to the formation of fluorinated CPs with higher dimensionalities compared to their nonfluorinated counterparts. Conversely, the thermal stabilities of the latter are higher than those of the fluorinated CPs.
A series of new Ba-based coordination polymers (CPs) were mechanochemically synthesized by milling Ba-hydroxide samples with perfluorinated and fluorine-free benzene-dicarboxylic acids, including tetrafluoroisophthalic acid (H2mBDC-F4), tetrafluorophthalic acid (H2oBDC-F4), isophthalic acid (H2mBDC) and phthalic acid (H2oBDC). The new fluorinated CPs: [Ba(mBDC-F4)$0.5H2O] (1) and [Ba(oBDC-F4)·1.5H2O] (2) are compared to their nonfluorinated counterparts: [Ba(mBDC)·2.5H2O] (3), and [Ba(oBDC)·1H2O] (4). These materials are thoroughly characterized using powder X-ray diffraction. The products obtained by milling are all hydrated but vary in their water contents. Compositions and local structures are investigated by elemental analysis, thermal analysis, MAS NMR and attenuated total reflectioninfrared spectroscopy. These materials exhibit high thermal stabilities but small surface areas that remain unchanged even after thermal treatments.
Anewbariumcoordination polymer, BaF-benzenedicarboxylate (BaF(p-BDC)0.5), with fluorine directly coordinated to the metal cation, was prepared by mechanochemical synthesis routes. Phase-pure BaF-benzenedicarboxylate was synthesized by milling starting either from barium hydroxide or from Barium acetate as sources for barium cations. In both cases, the second reactant was 1,4-benzenedicarboxylic acid (H2(p-BDC)). Ammonium fluoride was used as fluorinating agent directly at milling. This is the first mechanochemical synthesis of coordination polymers where fluorine is directly coordinated to the metal cation.
Following the second possibility, barium acetate fluoride (Ba(OAc)F) is formed as ntermediate product after milling, and the new coordination polymer is accessible only after washing with water and dimethyl sulfoxide. The new compound BaF(p-BDC)0.5 was characterized by X-ray powder diffraction, FTIR-, and 19F, 1H-13C CP MAS NMR spectroscopies, DTA-TG, and elemental Analysis.
Studies on the mechanochemical Knoevenagel condensation of fluorinated benzaldehyde derivates
(2018)
The mechanochemical Knoevenagel condensation of three fluorinated benzaldehyde derivates and malononitrile was investigated. The reactions were performed under solvent- and catalyst-free conditions and resulted in highly crystalline products after crystallization from a viscous phase in the milling jar.
The quality of the obtained crystals was sufficient for single-crystal X-ray diffraction circumventing a recrystallization step. To gain more information on the reaction, progress was investigated in situ using time-resolved Raman spectroscopy. The results show a direct conversion of the reactants.
Maghemite and magnetite show superparamagnetic behavior when synthesized in a nanostructured form. The material’s inducible magnetization enables applications ranging from contrast enhancing agents for magnetic resonance imaging to drug delivery systems, magnetic hyperthermia, and separation. Superparamagnetic iron oxides with templated porosity have been synthesized so far only in the form of hard-templated powders, where silicon retained from the template severely degrades the material’s magnetic properties. Here, for the first time, the synthesis of superparamagnetic iron oxides with soft-templated mesopore structure is reported. The synthesis of nanostructured maghemite and magnetite films succeeds using micelles of amphiphilic block-copolymers as templates. A thermal treatment of the initially formed mesoporous ferrihydrite in nitrogen produces maghemite, which can be partly reduced to magnetite via thermal treatment in hydrogen while retaining the templated mesopore structure. The resulting materials feature a unique combination of high surface area, controlled pore diameter, and tunable magnetic properties.