Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (110)
- Beitrag zu einem Tagungsband (67)
- Zeitschriftenartikel (58)
- Beitrag zu einem Sammelband (42)
- Buchkapitel (5)
- Forschungsbericht (5)
- Posterpräsentation (2)
- Handbuch (1)
- Sonstiges (1)
Sprache
- Englisch (152)
- Deutsch (123)
- Französisch (11)
- Mehrsprachig (5)
Referierte Publikation
- nein (291) (entfernen)
Schlagworte
- Wear (31)
- Friction (29)
- Niobium carbide (28)
- DLC (22)
- NbC (19)
- Slip-rolling (14)
- Ester (10)
- Hardness (10)
- Machining (10)
- Cutting tools (9)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (110)
The effects of rapid pulse electric current sintering (PECS), substitution of WC by NbC and Co by Ni, and carbide additives (TiC and Mo2C) on the microstructure, elastic modulus, B3B transverse rupture strength (TRS) and high temperature sliding wear on WC-Co, WC-Ni, NbC-Co and NbC-Ni cermets were studied. High temperature sliding wear tests were carried out using a ball-on-disk tribometer, with a 10 N force, at a sliding speed of 1.34 m/s for 0.8 km (10 min) and 2.4 km (30 min), using 100Cr6 (AISI 52100) steel balls at 400 °C and 0% humidity. Additions of TiC and Mo2C to NbC-12Ni improved the sliding wear resistance, with TiC having the greater effect, reducing the sample wear rate by over 30% from 15.1×10−6mm3/N·m to 9.4×10−6mm3/N·m after sliding distance of 2.4 km. Generally, the LPS samples had lower wear volumes than the corresponding SPS samples, due to higher K1c and TRS.
The use of high niobium alloyed cast iron alloys is a relatively new approach in which the niobium addition intends to improve the properties of the material by the precipitation of hard niobium carbides during solidification. Steels can be replaced by ductile cast iron in some rolling applications, such as gears and cams, in order to reduce material costs. The aim of this work is to evaluate ductile iron alloyed with 1 weight percent (wt.%) niobium for the as cast specimens and with 1.8 wt.% and 2.4 wt.% niobium for the austempered specimens under lubricated slip-rolling tests using mixed/boundary conditions in an Amsler-type machine. Austempered ductile iron (ADI) alloyed with 1 wt.% chromium, or Carbidic ADI, was tested for comparison. For the as cast conditions, the niobium addition resulted in an increase of wear resistance owing to the low contact pressure of these tests. However, for the austempered specimens, the best performance was found for unalloyed ADI. The main factor acting in the initiation and propagation of cracks in ductile iron is the presence of the graphite nodules. The coarse carbides also contributed to the initiation of cracks and spalling of the material.
The sales of niobium carbide (NbC) have grown in the last years, but NbC is still a hidden carbide and mainly used as grain growth inhibitor in hard metals. In the present work it was shown that the progress in the key properties, like HV30, KIC and strength, followed by machining and tribological results of the respective NbC grades.