Downsizing (power-to-weight ratio) and higher speeds lead to a rise in Hertzian contact pressures in combination with an increase in surface or oil temperatures. Under such conditions, commonly used bearing steels, such as 100Cr6, reach their limits, creating a demand for alternative slip-rolling resistant steel alloys. The present work therefore compares the slip-rolling performance of various steel types with Maraging- and PM-type steel alloys such as e.g. CSS-42L™, ASP2012, BIMAX42+, in the Hertzian contact pressure range up to P0max of 4 GPa. Through-hardened 100Cr6H (AISI 52100), case-hardened 20MnCr5 (AISI 5120H) and nitrogen alloyed Croni-dur30 (AMS 5898) still compete in terms of slip-rolling and wear resistance and load carrying capacity, whereas Maraging- and PM-type steel alloys offer superior strength and toughness properties.
The use of high niobium alloyed cast iron alloys is a relatively new approach in which the niobium addition intends to improve the properties of the material by the precipitation of hard niobium carbides during solidification. Steels can be replaced by ductile cast iron in some rolling applications, such as gears and cams, in order to reduce material costs. The aim of this work is to evaluate ductile iron alloyed with 1 weight percent (wt.%) niobium for the as cast specimens and with 1.8 wt.% and 2.4 wt.% niobium for the austempered specimens under lubricated slip-rolling tests using mixed/boundary conditions in an Amsler-type machine. Austempered ductile iron (ADI) alloyed with 1 wt.% chromium, or Carbidic ADI, was tested for comparison. For the as cast conditions, the niobium addition resulted in an increase of wear resistance owing to the low contact pressure of these tests. However, for the austempered specimens, the best performance was found for unalloyed ADI. The main factor acting in the initiation and propagation of cracks in ductile iron is the presence of the graphite nodules. The coarse carbides also contributed to the initiation of cracks and spalling of the material.
The running-in phase of mechanical systems is critical from a tribological standpoint, though poorly understood. Microcracks accelerate material failure and wear during this phase of heightened friction. With this in mind, the ultimate goal of this current work is to transfer the running-in phase into the final step of the mechanical finishing process through the targeted pre-conditioning of novel, high toughness steel bearings without thermo-chemical treatments and compare these to conventional, case-hardened steels. This pre-conditioning involved the targeted implementation of two specific lubricant packages, the first with CaCO3 as the active ingredient and the second with MoDTC as the active ingredient, to generate chemically reactive tribolayers (tribofilms) on twin disk testing rigs. Pre-conditioning was carried out up to 104 load cycles (approximately 25 min). The films generated in pre-conditioning were analyzed by SEM-EDX with Element-Mapping, Raman spectroscopy, and XPS to elucidate their molecular composition and concentration on the sample surfaces. The combination of these methods of analysis gave a clear indication that 104 cycles were sufficient to generate stable chemical tribofilms. CaO and CaCO3 were the main components of the tribofilm from the first lubricant package, while MoS2, MoO2 and MoO3 were the main components from the second lubricant package. Tribofilm-protected samples were then subjected to slip-rolling endurance testing (T=+120 °C, 10,000,000 cycles, approximately 19 days in a factory fill engine oil) to determine any changes in friction behavior or wear performance. Some significant reductions in coefficients of friction at the end of endurance testing were observed, though in certain cases, no definitive improvement was observed. In contrast, very strong reductions in wear were observed across the entire spectrum of materials and testing loads. In some cases, sample surface wear reduction from pre-conditioning via tribofilms reached over 90%. The observed improvements to friction behavior and wear performance are indicative of a technically simple, cost- and energy-efficient pre-conditioning method that may prove to be competitive with existing thermochemical treatments for steel alloys.
The automotive industry places significant importance on downsizing components to achieve greater efficiency. The goal of reducing CO2 emissions has led to the development of lightweight materials that are also able to enhance performance. In light of these aspirations, the aim of this study is to characterize two novel, high-performance steels, as well as a 'classical' gear steel for comparison with each other and currently applied materials. The gear steel underwent carburization and subsequent deep freezing treatments in an attempt to yield discrete sample groups with respect to residual austenite. The high-performance steels were heat treated as recommended by their respective manufacturers, and were not carburized. Elemental analyses were conducted by multiple methods to ensure accurate results. Residual austenite contents of the steels and the depth profiles of residual stresses were determined by X-ray diffraction (XRD). Hardness profiles were taken from the testing surfaces into the material core. The carburization of 20MnCr5 led to higher hardness and the greater concentration of carbon in the carburization zone more representative of a hardened SAE E52100, or 100Cr6/102Cr6, than of a non-carburized 20MnCr5. Residual austenite contents ranging from approximately 6–14 vol% were generated, though effectively providing only two, rather than the desired four discrete sample groups. Residual stresses from machining and carburization were measured directly at the sample surface, and from carburization alone below the surface. The high-performance steels fulfilled manufacturer expectations in terms of elemental content, hardness between 50 and 55 HRC and strongly martensitic microstructure character. Finally, slip-rolling endurance testing (T=+120 °C, 10,000,000 cycles, approximately 19 days in a factory fill engine oil) was carried out on all materials, whereby coefficient of friction distributions during testing and wear coefficients after testing were calculated. Testing was performed up to and including P0Mean=1.94 GPa (P0Max=2.91 GPa, FN=2000 N). Ultimately, the non-carburized high-performance steels showed competitive wear performance and better friction behaviour than the carburized 20MnCr5, which has been attributed to their work hardening capability.
Slip-rolling resistant thin film ta-C coatings for up to 3.000 MPa of Hertzian contact pressure
(2009)
Le secteur automobile doit faire face actuellement à de nouveaux challenges au niveau de la construction allégée, des économies de carburant et des coûts. Ces exigences motivent la mise au point de tribosystèmes pouvant résister à des pressions de contact de plus en plus élevées avec de faibles coefficients de frottement. L'optimisation de systèmes existants par l'application de revêtements de surface performants représente une alternative intéressante. Ce texte présente les performances de couches minces dans des conditions d'essais de slip-rolling (roulement à composante de glissement) en présence de lubrifiants liquides. Après une première sélection à température ambiante, les revêtements les plus performants ont été testés à 120 °C. Il s'agit de revêtements DLC en carbone hydrogéné (a-C:H) et en carbone tétraédrique (ta-C) de dernières générations ainsi qu'un nouveau système « revêtement/substrat ». Certains des revêtements DLC développés récemment sont résistants en slip-rolling au moins jusq'à 10 millions de cycles à 120 °C dans l'huile moteur sous des pressions hertziennes de contact de P0max = 2600 / 2940 MPa. De plus, le nouveau système revêtement Zr(C,N)x/substrat peut résister au moins à 1 million de cycles sous des pressions hertziennes initiales de contact allant jusqu'à P0max = 3500 MPa et à des températures de lubrifiant d'au moins 120 °C. -----------------------------------------------------------------------------------------------------------------------------------------------
The light-weight approach and fuel economy targets in today's automotive engineering require tribosystems, which can withstand higher contact pressures associated with low coefficients of friction. The application of surface coatings represents one approach among others. This paper presents thin film coatings performances in a bench mark test procedure exerting slip-rolling conditions in the presence of liquid lubricants. After a first selection at room temperature, the most resistant coatings were evaluated at 120 °C. These are newly developed DLC coatings (a-C:H & ta-C) as well as a novel coating-substrate system. Some of the newly developed DLC-coatings are slip-rolling resistant for at least up to 10 million cycles at 120 °C oil temperature) under Hertzian contact pressures of P0max = 2600 / 2940 MPa. Furthermore, this novel Zr-based thin film coating can withstand at least 1 million cycles under initial Hertzian contact pressures of up to P0max = 3500 MPa and oil temperatures of at least 120 °C associated with low coefficients of friction under mixed/boundary conditions.