The process window and range of functional properties of NbC is wide, because micro-hardness, hot hardness, sliding wear resistance, elastic modulus and toughness can be tailored by the C/Nb ratio, because Nb4C3, Nb6C5 and other short and long range ordered phases occur in the region of homogeneity of NbCx (0,75≤ x ≤1.0) in the binary Phase diagram, and by the type of binder. Further improvements enable the addition of secondary carbides. Supporting results from literature and different grades with varying C/Nb ratio or binder types were illuminated. Thus, the NbC system offers to producers a wider process window, than WC. The impact of these tailored properties on sliding wear and cutting performance was illuminated by tribological and machining results. NbC can be synthesized by carbothermal conversion of Nb2O5 or be metallurgically grown in melts and leached out as coarse NbC cubes. NbC provides comparably lower friction in many relevant tribo-contacts and displays low wear. NbC and Nb2O5 have so far no REACH classification related to human toxicology and are not listed as substances of very high concern contrary to WO3 and Co3O4.
The aim of the study presented in this paper is to highlight the potential of niobium carbide cutting tool inserts for machining and to compare their performance to commercially available tungsten carbide inserts. In this work, a comparison between a conventional Wc-Co insert and NbC-Co inserts was carried out under hard machining conditions on specimens made of 100Cr6 bearing steel grade (SAE 52100).
In the present work it was shown that the addition of VC or a combination of VC + Ti(C0.7N0.3) was efficient in reducing the NbC grain growth during liquid phase sintering, when compared to NbC-Ni equivalents. A finest NbC grain size of 1.48 µm was obtained in the NbC-15 Ti(C0.7N0.3)-10 Ni-7.5 VC cermet, exhibiting a hardness of 1486 +/- 7 kg/mm2 and a fracture toughness of 8.7 +/- 0.1 MPa m 1/2.
This paper indicates that the tribological behavior under dry sliding of a Fe3Al-niobium carbide (NbC) composite prepared by pyrometallurgical synthesis was compared to NbC-based hard metals bonded by cobalt or Fe3Al. The dry sliding wear resistance (0,1-7/10 m/s) of the present Fe3Al-NbC with ∼60% NbC was close to those known of NbC-based hard metals. No grain pull-outs or fragmentations of the NbC grains were seen in the wear tracks, as a metallurgical interphase was formed between matrix and NbC grains.
The effects of rapid pulse electric current sintering (PECS), substitution of WC by NbC and Co by Ni, and carbide additives (TiC and Mo2C) on the microstructure, elastic modulus, B3B transverse rupture strength (TRS) and high temperature sliding wear on WC-Co, WC-Ni, NbC-Co and NbC-Ni cermets were studied. High temperature sliding wear tests were carried out using a ball-on-disk tribometer, with a 10 N force, at a sliding speed of 1.34 m/s for 0.8 km (10 min) and 2.4 km (30 min), using 100Cr6 (AISI 52100) steel balls at 400 °C and 0% humidity. Additions of TiC and Mo2C to NbC-12Ni improved the sliding wear resistance, with TiC having the greater effect, reducing the sample wear rate by over 30% from 15.1×10−6mm3/N·m to 9.4×10−6mm3/N·m after sliding distance of 2.4 km. Generally, the LPS samples had lower wear volumes than the corresponding SPS samples, due to higher K1c and TRS.