Drop-out of molten material was avoided by EM pressure
Compensation of the hydrostatic pressure of up to 20 mm thick
aluminum and stainless steel (experiment and FEM)
Mitigation of the weld bead dynamics
Significant changes in the velocity distributions in the weld pool
Weld pool geometry shape changes due to Hartmann effect
Significant porosity reduction
Surface quality improvements
Drop-out of molten material was avoided by EM pressure
Compensation of the hydrostatic pressure of up to 20 mm thick
aluminum and stainless steel (experiment and FEM)
Mitigation of the weld bead dynamics
Significant changes in the velocity distributions in the weld pool
Weld pool geometry shape changes due to Hartmann effect
Significant porosity reduction
Surface quality improvements
The influence of two different weld imperfections (gap/crack) on the fatigue behaviour of spot welded joints was tested
Surface cracks havenoinfluenceon thefatiguelife
Samples with cracks in the electrode indentation /HAZ where tested
Stiffness curves are not significantly influenced by surface cracks
3D FE-Simulation demonstrate no changes of stress due to surface imperfections
Mechanische Eigenschaften der laserhybridgeschweißten Schweißverbindungen von hochfesten niedriglegierten Stählen erfüllen die Anforderungen der geltenden Normen
Eindringtiefe des Zusatzwerkstoff bis ca. 12 mm
Halborbitales Schweißen an 36” Rohren mit einer Wandstärke von 16 mm bei einer Schweißgeschwindigkeit von bis zu 2,2 m/min und Laserleistung von 19 kW technisch möglich
Rissfreie Schweißverbindungen an Präzisionsrohren können durch eine geeignete Schweißparameterauswahl mittels Laser-Hybridverfahren hergestellt werden
Surface modification of mild steel was undertaken using two covered electrodes and two tubular electrodes. The two covered electrodes are DIN 8555: E6-UM-60 and E10-UM-60GR; however, the two tubular electrodes are E10-GF-60GR1 and E10-GF-60GR2. Chemical analysis for the weld metal and XRD of the flux covering for covered electrodes and flux core for tubular electrodes were conducted. The most important factor in determining the wear resistance is the microstructure of the deposit layers. In similar carbon equivalent electrodes E10-UM-60GR and E10-GF-60GR1, electrode E10-GF-60GR1 (tubular) shows larger carbides area fraction and better wear resistance than electrode E10-UM-60GR (covered). This could be attributed to a lower dilution associated with tubular electrode compared with covered electrode. The two tubular electrodes showed higher wear resistance than the covered electrodes which is mainly due to the larger Fe-Cr carbide precipitation area fraction.
The accurate prediction of the thermal energy generation and distribution in friction stir welding process is of great significance for the optimization of the process parameters and the understanding of the underlying mechanisms. In this study, a new method of integrative calculation and measurement is proposed to obtain the more reasonable values of the frictional coefficient and the slip rate, which are both used to characterize the heat generation rate at the tool-workpiece contact interfaces. A three-dimensional model is established to fully couple the energy generation, heat transfer and material flow in friction stir welding of aluminum alloys. The energy produced by both interfacial friction and plastic deformation are taken into consideration. The analysis accuracy of the thermal energy generation and distribution is improved, and the distribution features of thermal energy density in the vicinity of the tool are elucidated. The predicted peak temperature values at some locations are in agreement with the experimentally measured ones.