Eingeladener Vortrag
- nein (9)
In October 2011 the European Commission (EC) published a "Recommendation on the definition of na-nomaterial" (2011/696/EU), to promote consistency in the interpretation of the term "nanomaterial" for legislative and policy purposes in the EU. The EC NM Definition includes a commitment to its review in the light of experience and of scientific and technological developments. This review is ongoing in 2017 and as a contribution to the review the Joint Research Centre of the European Commission (JRC) has already developed a series of three scientific-technical reports with the title: “Towards a review of the EC Recommendation for a definition of the term nanomaterial” which provides to the EC policy services sci-ence-based options on how the definition could be revised or supported with additional guidance.
The overarching nature and wide scope of the EC NM Definition, as it does not exclude a priori any particulate material regardless the state, form and size, creates many analytical challenges in its imple-mentation for all stakeholders, including enterprises and regulators.
The NanoDefine project has as core objective to support the implementation of the EC NM Definition. In an earlier report1 key aspects of the EC NM Definition were addressed, with the goal to improve the implementability of the EC NM Definition. Based on further developments and results obtained in NanoDefine project that first report was updated and is presented here. The key aspects are discussed based on the results of four years of research performed within the framework of the project. As a result this report assesses how well the requirements of the EC NM Definition can be fulfilled with currently available analytical possibilities. It presents recommendations and options on a revision of the EC NM Definition to improve the implementability of the definition based on currently available analytical possi-bilities, according to the state of the art in 2017. Of the technical issues considered in this report, the following seem to deserve the most attention in terms of clarification of the definition and/or provision of additional implementation guidance: 'external dimension', ‘number based particle size distribution‘, ‘polydispersity‘ and ‘upper size limit‘, the term ‘particle’, the ‘means to prove that a material is not a nanomaterial‘ and ‘the role of the volume specific sur-face area (VSSA)‘, and "particulate materials'.
The overall objective of project Improved traceability chain of nanoparticle size measurements is to improve the traceability chain for nanoparticle size measurements. The main impact will be achieved by manifold contributions to standard documents for CEN/TC 352 “Nanotechnologies”, which directly addresses the research needs of CEN, CENELEC and ETSI mandated by EC to develop standards for methods and reference materials to accurately measure the size and size distribution of nanoparticles. This will take place in collaboration with ISO/TC229 ‘Nanotechnologies’, ISO/TC24/SC4 ‘Particle characterization’ and ISO/TC201 ‘Surface analysis’/ SC9 ‘Scanning probe microscopy’.
The synthesis of TiO2 was studied in an original
hydrothermal process that uses triethanolamine titanium complex Ti(TeoaH)2 as a Ti precursor and triethanolamine (TeoaH3) as a shape controller to obtain bipyramidal anatase nanoparticles.
Backed-up by experimental evidence, i.e., time profiles for Ti(IV) species concentrations together with crystal shape and particle size distributions measured by dynamic light scattering and electron microscopy, a mathematical model was built. The model includes chemical reactions responsible for TiO2 generation in solution and the subsequent anatase nucleation and crystal growth. The oriented attachment mechanism was adopted to explain the build-up of crystals with equilibrium anatase structure (Wulff structure) and time-varying shape factor. This complex mathematical model was solved writing and validating an in-house
software using the Matlab (Natick, MA, USA) environment. The process was simulated for a batch time of 50 h, and the results, in terms of main species concentration and crystal size distributions, are in rather good agreement with the experimental measurements.
Self-assembly of TiO2 nanoparticles in multiple layers by layer-by-layer deposition has been selected of different deposition procedures usually applied for fabrication of TiO2 thin films with defined and homogeneous thickness on supports of interest for the large-scale applications. The substrates tested were: conductive (FTO) glass, silica glass and titanium alloy. The selected film fabrication technique consists of the deposition of alternating layers of oppositely charged, i.e. functionalized, TiO2 nanoparticle layers with wash steps in between. The controlled assembly of TiO2 nanoparticles on the supports surface requires both a proper functionalization of the supports to promote the adhesion of the TiO2 film to the substrates and proper functionalization of TiO2 nanoparticles to allow attachment to substrate and subsequent reaction between different NP layers. The current study focusses on the analytical control of the functionalization of the substrates with 3-Aminopropyltriethoxysilane (APTS) and glutaraldehyde (GA) by means of surface sensitive methods, XPS, Auger Electron Spectroscopy (AES) and ToF-SIMS. Chemical composition of surface of functionalized substrates shows differences in the degree and type of modification in dependence on substrate.
The synthesis of TiO2 nanoplatelets with fluorine-containing reactants is carried out using Ti (IV) butoxide as precursor and concentrated HF as shape controller, the final product requires a working up in order to eliminate or at least to reduce the amount of residual fluorides, which is realized here by well-defined thermal treatment.
Qualitative investigation of the bulk elemental composition by means of EDX of TiO2 nanoparticles (NPs) has identified fluorine in case of the as-synthesized samples. EDX spectra of thermally treated products exhibit either a fluorine content close to the limit of detection. The latter holds also true for the reference sample, TiO2 NPs of bipyramidal shape and prepared by a different synthesis route. For differentiation whether fluorine is present in the bulk or at the surface of the TiO2 nanoplatelets, top-surface sensitive AES and ToF-SIMS has been applied. Secondary ions of fluorine are detected in ToF-SIMS spectra of all samples, but could be roughly quantified by measurement of same reference sample as for EDX, namely TiO2 nano-bipyramids. This revealed that the amount of fluorine within1 nm depth beneath the surface is reduced in the thermally treated specimen compared to the raw product down to a content about as low as in the reference sample. AES allows analyzing analysis of the first few nanometers from the top-surface of individual NPs by point analysis. An F KLL peak has been detected at the surface of samples of as-prepared TiO2 nanoplatelets under optimized measurement conditions, but was not detectable after their calcination, which is in agreement with ToF-SIMS results. Moreover, high resolution AES on single TiO2 nanoplatelets elucidated that the surface atomic layers surrounding the TiO2 nanopaltelet contain fluorides before thermal treatment of the NPs.
Evaluation of particle sizing techniques for implementation of the EC Definition of a nanomaterial
(2017)
Many techniques are available for measuring particle size distribution. For ideal materials (spherical particles, well dispersed) it is possible to evaluate the Performance of these methods. The performance of the analytical instrumentation for the purpose of classifying materials according to EC Definition is unknown. In this work the performance of commercially available particle sizing techniques on representative NanoDefine set of real-world testing materials (RTM) and quality control materials (QCM) for the implementation of the Definition is evaluated.
Electrospray ionization constitutes a promising deposition technique for high-resolution imaging. Particle distribution on TEM grids takes place homogeneously and no losses occur. Suspension must be appropriate (stabilizer may induce artefacts). ESI parameters need to be optimized for each material.
Volume specific surface area (VSSA) by BET: concept and demonstration on industrial materials
(2017)
Volume specific surface area (VSSA) as measured by BET constituites a simple and reliable solution to (most) powders. Porous, coated, polydisperse/multimodal materials are to be treated with care, i.e. doubled by analysis with electron microscopy or more advanced BET analysis (e.g. t-plot)for each material in part.
Parameters of TiO2 coatings can greatly influence their final performance in largescale applications such as photocatalytic measurements, orthopedic and/or dental prostheses, cell cultures, and dye-sensitized solar cells. From different film deposition procedures, self-assembly of TiO2 NPs in multiple layers was selected for systematic characterization. EDX, AES and ToF-SIMS analysis have been carried out in order to evaluate the functionalization of several types of TiO2 NPs differing in size, shape and surface area.
The potential of electrospray deposition, for the controlled preparation of particles for imaging in electron microscopes, is evaluated on various materials: from mono-modal suspensions of spherical particles to multimodal suspensions and to real-world industrial materials. It is shown that agglomeration is reduced substantially on the sample carrier, compared with conventional sample preparation techniques. For the first time, it is possible to assess the number concentration of a tri-modal polystyrene suspension by electron microscopy, due to the high deposition efficiency of the electrospray. We discovered that some suspension stabilizing surfactants form artifact particles during electrospraying. These can be avoided by optimizing the sprayed suspension.