Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (31)
- Beitrag zu einem Tagungsband (27)
- Beitrag zu einem Sammelband (7)
- Vortrag (2)
- Handbuch (1)
Sprache
- Englisch (68) (entfernen)
Schlagworte
- Corrosion (17)
- Pitting corrosion (12)
- Stainless steel (11)
- Electrochemical noise (8)
- Korrosion (7)
- Atmospheric corrosion (6)
- Concrete (6)
- Self-corrosion (6)
- X-ray tomography (6)
- Concrete parameters (5)
- Corrosion testing (5)
- Reinforcement (5)
- Chloride Induced Corrosion (4)
- Nichtrostender Stahl (4)
- Passive layer (4)
- Cement (3)
- Duplex stainless steels (3)
- Galvanostatic Pulse (3)
- KorroPad (3)
- Steel in Concrete (3)
- Stress corrosion cracking (3)
- Surface condition (3)
- Zinc coatings (3)
- Austenitic stainless steels (2)
- Beständigkeit (2)
- Cathodic protection (2)
- Chlorides (2)
- Chromate (2)
- Corrosion Risk (2)
- Corrosion protection (2)
- Corrosion resistance (2)
- Duplex (2)
- Electrochemical measurements (2)
- Electrochemical tests (2)
- Embedded Sensors (2)
- Ferritic stainless steels (2)
- Gel-type electrolytes (2)
- Grease (2)
- Grinding (2)
- Hydrogen evolution (2)
- Hydrogen-induced stress corrosion cracking (2)
- Korrosionsprüfung (2)
- Manganese alloyed stainless steels (2)
- Metallographic section (2)
- Moisture Content (2)
- Monitoring (2)
- Mortar (2)
- Portable Equipment (2)
- Prestressed systems (2)
- Prestressing steel (2)
- Reinforced and Prestressed Concrete Structures (2)
- Reinforcing steel (2)
- Surface treatment (2)
- Wax (2)
- Zinc (2)
- Zinkdeckschichten (2)
- 3D x-ray (1)
- A. Stainless steel (1)
- Abrasive belt (1)
- Agar (1)
- Aluminium (1)
- Analytical Chemistry (1)
- Atmospheric exposure (1)
- Atmosphärische Korrosion (1)
- Austenitic (1)
- Austenitic Stainless Steel (1)
- Austenitic stainless steel (1)
- B. Potentiostatic (1)
- Betonstahl (1)
- Black Steel (1)
- Black steel (1)
- C. Passivity (1)
- C. Pitting corrosion (1)
- Carbon steel (1)
- Cathodic Protection (1)
- Cathodic process (1)
- Cathodic reaction (1)
- Chlorid-induced corrosion (1)
- Chloride (1)
- Chloride induced corrosion (1)
- Civil engineering (1)
- Contaminated mortar (1)
- Corrosion Monitoring (1)
- Corrosion Rate (1)
- Corrosion monitoring (1)
- Corrosion rate (1)
- Corrosion risk (1)
- Corrosivity category (1)
- CrNi-Stahl (1)
- Critical pitting temperature (1)
- Dauerhaftigkeit (1)
- Deckschichtbildung (1)
- Design for durability (1)
- Drop Evaporation Test (1)
- Duplexstahl (1)
- EPR (1)
- EPR test (1)
- Electrochemical Impedance Spectroscopy (1)
- Electrochemical Noise (1)
- Electrochemical potentiodynamic reactivation (1)
- Electrochemistry (1)
- Exposure tests (1)
- FT-IR (1)
- Failure (1)
- Ferritic (1)
- Free weathering (1)
- Galvanic corrosion (1)
- Galvanized construction elements (1)
- Galvanized elements (1)
- Galvanized rebar (1)
- Galvanized steel (1)
- Gel electrolytes (1)
- Gelartige Elektolyte (1)
- Gelartige Elektrolyte (1)
- General Chemical Engineering (1)
- Geothermal (1)
- Geothermie (1)
- HSCC (1)
- Hard coatings (1)
- High alkaline environment (1)
- Hot Cracking (1)
- Humidity (1)
- ISO 9223 (1)
- Indoor swimming pools (1)
- Intercrystalline corrosion (1)
- Korrosionsbeständigkeit (1)
- Laser Welding (1)
- Layer formation (1)
- Lean duplex (1)
- Macrocell corrosion model (1)
- Manganese alloyed (1)
- Marine atmosphere (1)
- Maritime Atmosphäre (1)
- Maritime atmosphere (1)
- Mass loss (1)
- Ni-Base Alloy (1)
- Ni-Basislegierung (1)
- Ni-alloy (1)
- Passivation (1)
- Pitting Corrosion (1)
- Polarization (1)
- Portable equipment (1)
- Potential mapping (1)
- Potentialfeldmessung (1)
- Prestressed concrete (1)
- Pull-out tests (1)
- Re-passivation (1)
- Rebar (1)
- Reinforced Concrete (1)
- Reinforced and prestressed concrete structures (1)
- Reinforcement Corrosion (1)
- Reinforcement corrosion (1)
- Repassivation (1)
- Salinization (1)
- Salt-spray testing (1)
- Spannungsrisskorrosion (1)
- Sprayed zinc layer (1)
- Stainless steels (1)
- Stanless steel (1)
- Steel (1)
- Steel reinforcement (1)
- Steel surface (1)
- Stress corrosion Cracking (1)
- Surface (1)
- Surface finish (1)
- Surface protection system (1)
- Surface treatments (1)
- Thermal-Sprayed Zinc (1)
- Ti-alloy (1)
- TiMgN (1)
- Unalloyed steel (1)
- Versalzung (1)
- Verzinkt (1)
- Video monitoring (1)
- Wasserstoff (1)
- Werkstoffauswahl (1)
- corrosion invetsigations (1)
- gel-type electrolytes (1)
- zinc coatings (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (2)
Agar gel pads have been used for electrochemical measurements for some time. For zinc in particular, a standard method for measuring the stability of the corrosion product layer is being established. The main interpretation factor is the corrosion product layer resistance RL, as it is easy to determine and interpret. A high corrosion product layer resistance indicates a high level of protection. However, it is not yet known how low the corrosion product layer resistance is for freshly produced zinc samples. As zinc is highly active, it reacts immediately with the environment to form a corrosion product layer, which affects the corrosion product layer resistance. The addition of zinc acetate to the agar gel pads prevents the formation of a surface layer and destroys existing ones.
This makes it possible to measure an almost corrosion product-free zinc surface. This is important in defining the range of corrosion product layer resistance for a protective surface.
Pitting corrosion is one of the most common mechanisms of local passivity breakdown on stainless steels. Electrochemical methods have preferentially been applied for the evaluation of pitting corrosion resistance of stainless steels in laboratory. Nevertheless, some of them are not reliable enough and in general the application of electrochemical methods in the field becomes difficult because of a required deep understanding of corrosion phenomena and measurement technology. A new approach for the evaluation of the pitting corrosion susceptibility of stainless Steel surfaces in the laboratory as well as in the field is frequently demanded by representatives of the metalworking industry. Therefore, the KorroPad-test was invented and patented as part of a research project at the BAM Federal Institute for Materials Research and Testing in Germany.
Electrochemical noise (EN) enables corrosion research and monitoring in real time and with high sensitivity. In the case of submicroscopic nucleation events of pitting corrosion it has been observed that the cathodic process plays a decisive role in the mechanism as well as in the origin of EN signals, which depend not only on the metallic dissolution reaction but also on the electron-consuming process. EN signals arising from the nucleation process of localized corrosion on stainless steels can only be recorded due to the inhibition effect on the cathodic process achieved by the spontaneous formation of the passive layer. In consequence, passive layer stability becomes a significant factor in influencing EN signals. The way in which the passive layer stability affects the acquisition and analysis of EN signals arising from pitting corrosion on stainless steels is discussed in detail.
The present work describes the combination of electrochemical investigations by using a gel‐type electrolyte with Fourier‐transformed infrared spectroscopy to investigate partially extremely thin corrosion product films on titanium‐zinc. The gel pad method enables the determination of corrosion relevant parameters such as the potential and the linear polarization resistance without altering the corrosion product layers, which are extremely prone to re‐dissolution when freshly formed. Complementary infrared spectroscopy enables the determination of main compounds of even very thin surface layers of few tenth of nanometers with a certain lateral resolution. It was found that zinc forms mostly zinc carboxy‐hydroxides such as hydrozincite, under various exposure conditions. The protective properties of these hydrozincite layers depend on the structure of the corrosion product film rather than on its thickness. In mid‐term exposure tests, shallow corrosion pits were found even in the absence of corrosive agents such as chloride.
Systematic laboratory and field exposure tests allow to compare nine different stainless steels (three ferritic, three austenitic, and three duplex grades) for civil engineering applications. The influence of surface finish was also taken into account by choosing five different industry-specific features. The three duplex stainless steels revealed excellent corrosion resistance under most of the test conditions. Especially for applications in civil engineering the lean duplex steels offer distinct advantages. The manganese-alloyed 1.4376 and the ferritic steel 1.4509 cannot be recommended as alternative materials as they did not perform satisfactorily.