Filtern
Dokumenttyp
- Vortrag (34)
- Zeitschriftenartikel (14)
- Beitrag zu einem Tagungsband (9)
- Forschungsbericht (2)
- Sonstiges (1)
Schlagworte
- Korrosion (34)
- Nichtrostender Stahl (12)
- Corrosion (10)
- Deckschichtbildung (7)
- Zink (6)
- Atmosphärische Korrosion (5)
- KorroPad (5)
- Korrosionsschutz (5)
- Corrosion testing (4)
- Gelartige Elektrolyte (4)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (60) (entfernen)
Eingeladener Vortrag
- nein (34)
Agar gel pads have been used for electrochemical measurements for some time. For zinc in particular, a standard method for measuring the stability of the corrosion product layer is being established. The main interpretation factor is the corrosion product layer resistance RL, as it is easy to determine and interpret. A high corrosion product layer resistance indicates a high level of protection. However, it is not yet known how low the corrosion product layer resistance is for freshly produced zinc samples. As zinc is highly active, it reacts immediately with the environment to form a corrosion product layer, which affects the corrosion product layer resistance. The addition of zinc acetate to the agar gel pads prevents the formation of a surface layer and destroys existing ones.
This makes it possible to measure an almost corrosion product-free zinc surface. This is important in defining the range of corrosion product layer resistance for a protective surface.
Die Versalzung und Verunreinigung von Metalloberflächen durch chloridhaltige Aerosole hat eine große Bedeutung für das Korrosionsverhalten von beschichteten Metalloberflächen im maritimen Bereich und bei Offshore-Anwendungen. So ist z. B. zu klären, ob und in welchem Maße eine Versalzung der Oberfläche Einfluss auf die Haftung und Dauerhaftigkeit von Beschichtungen hat. Dafür sind Detailfragen zu klären, etwa mit welcher Versalzung nach welchem Zeitraum zu rechnen ist oder wie für systematische Untersuchungen eine definierte und reproduzierbare Versalzung im Labor nachgestellt werden kann. Der Beitrag widmet sich diesen Fragestellungen. Es werden Ergebnisse eines Feldversuches auf Helgoland gezeigt und ein einfaches Verfahren zur definierten Beladung von Metalloberflächen mit Chloriden im Labormaßstab vorgestellt.
Der maßgebliche Korrosionsschutz von nicht rostendem Stahl in Beton basiert, anders als bei unlegiertem Betonstahl, auf der Ausbildung einer Chromoxidschicht. Die Chromoxidschicht ist in alkalischem und in carbonatisiertem Beton beständig, sodass nicht rostende Stähle in einem passiven Zustand vorliegen.
Die Initiierung von Lochkorrosionserscheinungen ist dagegen auch an nicht rostenden Stählen in Beton möglich. Der korrosionsauslösende Chloridgehalt ist neben dem Gehalt an Legierungselementen (insbesondere dem Chromgehalt) und der Oberflächenbeschaffenheit auch vom Konzentrationsverhältnis von OH“ zu CI“ im Elektrolyten abhängig. Daher ist prinzipiell zu erwarten, dass in karbonatisierten Betonen geringere Chloridgehalte Korrosion initiieren können als in Betonen mit höheren pH-Werten. Dies gilt in besonderem Maße für nicht rostende Betonstähle mit geringen Chromgehalten, wie z. B. Produkte aus dem Werkstoff 1.4003 (X2CrNi12) mit seiner im Vergleich zu den Standardausteniten geringen Beständigkeit. Um den kritischen korrosionsauslösenden Chloridgehalt am Beispiel eines am Markt verfügbaren ferritischen Chromstahls zu bestimmen, wurden an der Bundesanstalt für Materialforschung und -prüfung (BAM) umfangreiche Untersuchungen zu beschleunigten Korrosionsversuchen in alkalischen und karbonatisierten Mörteln durchgeführt. Mittels Laser-induced Breakdown Spectroscopy (LIBS) konnten die korrosionsauslösenden Chloridgehalte im Phasengrenzbereich Betonstahl-Mörtel ermittelt werden.
The present work describes the combination of electrochemical investigations by using a gel‐type electrolyte with Fourier‐transformed infrared spectroscopy to investigate partially extremely thin corrosion product films on titanium‐zinc. The gel pad method enables the determination of corrosion relevant parameters such as the potential and the linear polarization resistance without altering the corrosion product layers, which are extremely prone to re‐dissolution when freshly formed. Complementary infrared spectroscopy enables the determination of main compounds of even very thin surface layers of few tenth of nanometers with a certain lateral resolution. It was found that zinc forms mostly zinc carboxy‐hydroxides such as hydrozincite, under various exposure conditions. The protective properties of these hydrozincite layers depend on the structure of the corrosion product film rather than on its thickness. In mid‐term exposure tests, shallow corrosion pits were found even in the absence of corrosive agents such as chloride.
In maritimer Exposition können Zinkbauteile Nutzungsdauern von 50 Jahren erreichen. Dabei werden Expositionen mit Spritzwasserbelastung durch Meerwasser nicht betrachtet. Normative Betrachtungen und Korrosionsprognosen basierend auf Einjahreswerten liefern hier grundlegend falsche Ergbnisse, da sie eine signifikant höhere Belastung der Atmosphäre mit SO2 voraussetzen.
In maritimer Exposition können Zinkbauteile Nutzungsdauern von 50 Jahren erreichen. Dabei werden Expositionen mit Spritzwasserbelastung durch Meerwasser nicht betrachtet. Normative Betrachtungen und Korrosionsprognosen basierend auf Einjahreswerten liefern hier grundlegend falsche Ergbnisse, da sie eine signifikant höhere Belastung der Atmosphäre mit SO2 voraussetzen.
In maritimer Exposition können Zinkbauteile Nutzungsdauern von 50 Jahren erreichen. Dabei werden Expositionen mit Spritzwasserbelastung durch Meerwasser nicht betrachtet. Normative Betrachtungen und Korrosionsprognosen basierend auf Einjahreswerten liefern hier grundlegend falsche Ergebnisse, da sie eine signifikant höhere Belastung der Atmosphäre mit SO2 voraussetzen.
Die grundlegenden Korrosionsprozesse sind mit wenigen chemischen Formeln beschrieben, aber Korrosion ist immer eine Systemeigenschaft zwischen dem Werkstoff, dem Medium in dem er eingesetzt wird und den konstruktiven Bedingungen. Das macht es zu einem komplexen System, indem alle Einflussfaktoren ganzheitlich berücksichtigt werden müssen.
Anhand der Wirksumme ist eine Abschätzung des legierungsabhängigen Einflusses auf den Korrosionswiderstand gegen chloridhaltige Medien möglich. Die berechneten Werte sind nur bei optimaler Wärmebehandlung und Verarbeitung zutreffend.
Die Anwendung einer einfachen Formel unter Berücksichtigung von Chrom, Molybdän und Stickstoff ist in der Regel völlig ausreichend. Das daraus abgeleitete Ranking von Werkstoffen ist für diverse technische Regelwerke und zur Unterstützung der Werkstoffauswahl geeignet.
Für die Warenein-/Ausgangskontrolle ist die alleinige Feststellung der Wirksumme unzureichend. Ergänzende Korrosionsuntersuchungen/-prüfungen zur Beschreibung des Korrosionswiderstandes sind dafür notwendig. Gleiches gilt für die Beurteilung von Schadensfällen. Hier sind Verarbeitung, Einsatzbedingungen und die Konstruktion von ausschlaggebender Bedeutung.