Solidification Cracking Assessment of LTT Filler Materials by Means of Varestraint Testing and μCT
(2020)
Investigations of the weldability of metals often deal with hot cracking, as one of the most dreaded imperfections during weld fabrication. The hot cracking investigations presented in this paper were carried out as part of a study on the development of low transformation temperature (LTT) weld filler materials. These alloys allow to mitigate tensile residual stresses that usually arise during welding using conventional weld filler materials. By this means, higher fatigue strength and higher lifetimes of the weld can be achieved. However, LTT weld filler materials are for example, high-alloyed Cr/Ni steels that are susceptible to the formation of hot cracks. To assess hot cracking, we applied the standardized modified varestraint transvarestraint hot cracking test (MVT), which is well appropriate to evaluate different base or filler materials with regard to their hot cracking susceptibility. In order to consider the complete material volume for the assessment of hot cracking, we additionally applied microfocus X-ray computer tomography (μCT). It is shown that by a suitable selection of welding and MVT parameter the analysis of the complete 3D hot crack network can provide additional information with regard to the hot cracking model following Prokhorov. It is now possible to determine easy accessible substitute values (e.g., maximum crack depth) for the extent of the Brittleness Temperature Range (BTR) and the minimum critical strain Pmin.
The shape of the weld pool in laser beam welding plays a major role to understand the dynamics of the melt and its solidification behavior. The aim of the present work was its experimental and numerical investigation. To visualize the geometry of the melt pool in the longitudinal section a butt joint configuration of 15 mm thick structural steel and transparent quartz glass was used. The weld pool shape was recorded by means of a high-speed video camera and two thermal imaging MWIR and VIS cameras. The observations show that the dimensions of the weld pool vary depending on the depth. The regions close to the surface form a teardrop shaped weld pool. A bulge-region and its temporal evolution were observed approximately in the middle of the depth of the weld pool. Additionally, a transient numerical simulation was performed until reaching a steady state to obtain the weld pool shape and to understand the formation mechanism of the observed bulging phenomena. A fixed keyhole with an experimentally obtained shape was used to represent the full-penetration laser beam welding process. The model considers the local temperature field, the effects of phase transition, thermo-capillary convection, natural convection and temperature-dependent material properties up to evaporation temperature. It was found that the Marangoni convection and the movement of the laser heat source are the dominant factors for the formation of the bulging-region. Good correlation between the numerically calculated and the experimentally observed weld bead shapes and the time-temperature curves on the upper and bottom surface were found.
A long list of criteria determining the hot cracking susceptibility already exists. A main influence on solidification cracking can result from the design of the welded construction, i.e. from the influence of external loads. Using the Controlled Tensile Weldability (CTW) test, an external load hot cracking test, the influence of constant pre-load and different extension rates on the solidification cracking behavior of GTA (Gas Tungsten Arc) welds in an austenitic (AISI 309) and a ferritic (AISI 441) steel were investigated. Compared to specimens welded allowing free shrinkage and welded with an applied constant tensile pre-load, the specimens welded during the application of increasing tensile load show solidification cracks. In the weld seams, a characteristic angle α between the predominantly columnar grains and the fusion line can be observed. Specimens showing solidification cracks show a significantly larger angle α compared to the crack-free specimens. Based on these observations, the characteristic angle α is proposed as a new hot cracking criterion.
In situ crack detection in the mushy zone and the solid weld of a gas tungsten arc (GTA) weld using X-ray imaging during welding is a new research area for NDT inspection. Usually, NDT flaw detection is done after the complete solidification of the weld seam. In this paper, we present the use of real-time radiography with a minifocus X-ray source (YXLON X-ray tube Y.TU 225-D04) and a 75μm pixel size digital detector array (Dexela 1512) for the acquisition of 2D radiographic images by a sequence of exposures with time intervals of 80 ms for hot crack detection during single pass bead-on-plate GTA welding of 3 mm thick plates of aluminium alloy AlMgSi (6060). An analysis of the crack distribution in the weld sample is conducted from the acquired 2D radiographs and its corresponding 3D volumetric reconstruction achieved by linear coplanar digital laminography.
This in situ approach opens new possibilities in the field of hot crack research by having the direct information of both the crack initiation and growth and its correlation to the welding parameters.
One trend in today’s structural design for automobiles is towards application of stainless Steel in addition to traditional carbon Steel. This is mainly due to the advantages offered by stainless steel to the designer, i.e. its high corrosion resistance, heat resistance, strength and formability. Welding of austenitic stainless steel involves a high risk of solidification cracking due to low melting eutectics containing different kinds of impurities and to accumulated strain behind the weld pooi in the mushy zone. As a result, the quality of stainless steel welded joints will greatly be affected which may give cause for safety concerns. The intention of this study was to investigate the hot cracking sensitivity of laser welded fully austenitic stainless steels and to determine the critical local strain and strain rate from the formation of solidification cracks. C02-laser welding experiments were conducted using the steel X8CrMnNi19-6-3 (Nirosta H400). Solidification cracking susceptibility was examined with the help of the Controlled Tensile Weldability (CTW) Test developed by BAM Federal Institute for Materials Research and Testing in Berlin. The critical strain and strain rate of solidification cracking was measured at the surface of the workpiece directed to the laser beam in the close vicinity of the weld pool by using the Digital Image Correlation (DIC) technique and diode laser as the illuminating source.
Hot crack prevention in materials production and processing is an essential prerequisite for welded component safety. The causes of hot cracking can ultimately be attributed to the occurrence of metallurgical effects and to structural loads. More than 140 hot cracking test procedures have hitherto been developed for determining the hot cracking resistance. In principle, they are divided in self-restraint and externally loaded hot cracking tests with diverse process variants. Only some of the hot cracking tests are international standardized. Although various factors are known that encourage or prevent hot cracking, it is often not possible even with defined welding conditions to draw immediate conclusions about the hot cracking resistance of a welded component alone from a metallurgical composition of the base and filler materials. Based on an evaluation of the existing theories relating to hot cracking susceptibility assessment, this study summarizes the major hot cracking test procedures and highlights the application limits of the test procedures by presenting overviews along with explanations. It shows that weld hot cracking tests can generally be used to rank materials, welding consumables, and welding conditions. The evaluation of hot cracking test results and of their transferability among one another and to real components always requires consideration of the close relationships between metallurgy, welding process, and parameters, respectively, and prevailing restraint conditions.
All melting range alloys are subject to the risk of material-, design- and welding process-specific hot cracking during liquid to solid phase transition. The present study was focused specifically on the influence of additional external loads, e.g. resulting from component welding fabrication, on weld pool near displacements and on the associated structural hot cracking behaviour. Respective experimental investigations were conducted using the controlled tensile weldability test enabling defined additional tensile load imposition during welding. Depending on external loading, the local weld pool near transverse displacements dy and transverse displacement rates dy/dt were determined in situ during welding with the help of the digital image correlation technique. The measurements allowed time and spatially resolved identification of hot crack critical transverse displacements and displacement rates.
Due to significant developments over the last decades, laser beam welding has become a well-established industrial process offering high processing speeds and causing low component distortions. But an important issue currently preventing its intense use, especially in the energy or plant construction sector where high alloy steels are applied, concerns hot crack formation. Although considerable advances in understanding hot cracking mechanisms have been made, most of the known influencing factors are metallurgical in character. The thermo-mechanical effects are barely considered or quantified. Up to the present, there exist numerous hot cracking tests that were however conceived for welding methods other than laser beam welding. Considering the special features of the laser welding process, such as high cooling rates and the narrow process zone, results obtained with other welding techniques and test procedures cannot be transferred to laser beam welding. In this study, the laser beam weldability of various stainless steels was examined in terms of their susceptibility to hot cracking by means of the controlled tensile weldability test, which was proven to be suitable for use in conjunction with CO2 laser welding. This test allows the application of tensile strain at a variable fixed cross-head speed transverse to the welding direction. Full and partial penetration bead-on-plate welds were produced. In a first attempt to determine the impact of the applied external strain on the local transient strains and strain rates near the weld pool, an optical system was used to measure the backside surface of partial penetration welds. The results showed the influence of the strain and the strain rates on hot crack formation. Furthermore, a classification of the studied austenitic, duplex and ferritic stainless steels according to the established test criteria (critical strain and cross-head speed) was conducted.
Hot crack assessment during production and processing of metallic materials is an essential prerequisite for the safety of welded structures. The hot cracking investigations presented here were carried out as part of a study aimed at the development of Cr/Ni low transformation temperature filler materials. Low transformation temperature alloys open up the possibility for welding high strength steels. The externally loaded Modified Varestraint Transvarestraint hot cracking test was employed in the experiments described. The hot cracking resistance was evaluated with the help of light microscopy applied at the specimen surface. The proportionality between hot cracking susceptibility and Cr/Ni alloy content was explained by the altered solidification kinetics and by the enlarged solidification interval. The internal crack paths and the three-dimensional structure of the crack net in the material volume were examined using X-ray computer tomography. The total crack lengths for different material depths and circumjacent rectangular volumes, respectively, were be determined. An increasing hot cracking susceptibility with increasing Cr/Ni alloy content was also be established for the specimen volume.
Aluminium alloy 6060 is typical of a family of Al-Mg-Si extrusion alloys, which are considered weldable only
when using an appropriate filler alloy such as 4043 (Al-5Si) or 5356 (Al-5Mg). This study concerns the
thermal analysis and solidification path determination of aluminium alloy 6060 diluted with variable amounts
of 4043. Casting of controlled mixtures of alloys 6060 and 4043 was used to simulate different weld dilutions
in order to facilitate thermal analysis. Thermal analysis and metallography were applied in order to reveal
solidification reactions and phases, and allow calculation of solid fraction versus temperature curves.
Although the liquidus temperature was little affected, different phases formed with increased 4043 dilution,
with a trend toward lower temperature reactions and a larger fraction interdendritic constituent.