Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (17) (entfernen)
Schlagworte
- Roughness (17) (entfernen)
Organisationseinheit der BAM
- 1 Analytische Chemie; Referenzmaterialien (4)
- 1.9 Chemische und optische Sensorik (4)
- 6 Materialchemie (4)
- 6.1 Oberflächen- und Dünnschichtanalyse (4)
- 1.8 Umweltanalytik (2)
- 5 Werkstofftechnik (2)
- 5.1 Mikrostruktur Design und Degradation (1)
- 5.4 Multimateriale Fertigungsprozesse (1)
- 5.6 Glas (1)
- 9 Komponentensicherheit (1)
Sand erosion of solar glass: Specific energy uptake, total transmittance, and module efficiency
(2018)
Surface roughness, R Z , normal transmittance, Τ N , total transmittance, Τ T , and photovoltaic (PV) module efficiency, η S , were measured for commercial solar glass plates and PV test modules identically sandblasted with different loads of quartz sand (200 – 400 μ m), impact inclination angles, and sand particle speed. Measured data are presented versus the specific energy uptake during sand blasting, E (J/m2). Cracks, adhering particles, and scratch ‐ like textures probably caused by plastic flow phenomena could be observed after sand blasting. Their characteristic size was much smaller than that of sand particles.
After blasting and subsequent cleaning, the glass surface was still covered with adhering glass particles. These particles, cracks, and scratch ‐ like textures could not be removed by cleaning. For sand blasting with α = 30° inclination angle and E = 30 000 J/m2, normal transmittance, total transmittance, and relative module efficiency decreased by 29%, 2% and ∽ 2%, respectively. This finding indicates that diffusive transmission of light substantially contributes to PV module efficiency and that the module efficiency decrease caused by sand erosion can be better estimated from total than by normal transmittance measurements.
The roughness as a property of core–shell (CS) microparticles plays a key role in their functionality. Quantitative evaluation of the roughness of CS microparticles is, however, a challenging task with approaches using electron microscopy images being scarce and showing pronounced differences in terms of methodology and results. This work presents a generalized method for the reliable roughness determination of nonplanar specimens such as CS particles from electron microscopic images, the method being robust and reproducible with a high accuracy. It involves a self-written software package (Python) that analyzes the recorded images, extracts corresponding data, and calculates the roughness based on the deviation of the identified contour. Images of single particles are taken by a dual mode scanning electron microscopy (SEM) setup which permits imaging of the same field-of-view of the sample with high resolution and surface sensitive in SE InLens mode as well as in transmission mode (TSEM). Herein, a new type of polystyrene core–iron oxide shell–silica shell particles is developed to serve as a set of lower micrometer-sized study objects with different surface roughness; the analysis of their images by the semiautomatic workflow is demonstrating that the particles’ profile roughness can be quantitatively obtained.
CS particles show unique properties by merging individual characteristics of the core and the shell materials. An alteration particularly in their surface roughness affects the final performance of the particles in the targeted application. Quantitative evaluation of the roughness of CS microparticles is, however, a challenging task employing microscopic techniques being scarce and showing large differences in terms of methodology and results.
In our previous work, we have reported a systematic study with a reliable analysis tool, which evaluates profile roughness quantitatively, for individual core-shell microparticles using electron microscopy (EM) images of both types, Scanning Electron Microscopy (SEM) and transmission mode SEM (or TSEM). The SEM images contain two-dimensional (2D) information, therefore, provide profile roughness data only from the projection in the horizontal plane (in other words, from the “belly”) of a spherical particle. The present study offers a practical procedure to give access to more information by tilting the sample holder and hence allowing images of a single particle to be recorded at different orientations under the same view angle. From the analysis of these images, extended information on surface roughness of the particle can be extracted. Thus, instead of obtaining 2D information from a single SEM image, three-dimensional (3D) information is obtained from 2D projections recorded at different particle orientations.
A particle roughness analysis tool, based on electron microscopy images (SEM and TEM). The influence of various parameters on the calculated roughness was also investigated: the setting of the proper threshold, accelerating voltage, etc. The samples were gradually tilted to extend imaging information of more than only one projection. Furthermore, the measurement uncertainty of the profile roughness of particles associated to various orientations was estimated.
Main focus was on the deposition of carbon nanofibers (CNFs) onto the hard nanocomposite (nc-Ti1 - xAlxN)/(a-Si3N4) (nACo®) coating surface and the investigation of the structure and tribological properties of CNFs. The alcohol chemical vapor deposition (ACCVD) method was employed to prepare CNFs and the deposition temperatures were 600 and 700 °C, respectively. Prior to the CNF deposition, Ni catalyst was deposited onto the nACo® surface using the magnetron sputtering. The influence of the deposition temperature on the carbon nanofibers structure was investigated by Raman spectroscopy and scanning electron microscopy (SEM). The higher order degree of CNF structure is observed with increasing deposition temperature. Tribological tests were carried out under fretting contact conditions against Al2O3 ball. It is shown that the coefficient of friction (COF) decreases from 1.0 to 1.2 for the clean nACo® surface to 0.2–0.4 for the CNF layers deposited on the nACo® surface. The roughness of the nACo® surface was varied and a higher durability of the CNF layers deposited on the rougher nACo® surface is found.
Zero wear (Null Verschleiß)
(2013)
In situ Acoustic Emission for wear life detection of DLC coatings during slip-rolling friction
(2006)
Different diamond-like carbon (DLC) coatings on a steel substrate (100Cr6) were tested under slip-rolling friction conditions against uncoated counter bodies of the same steel. The initial maximum Hertzian pressure was varied in a range of P0 = 1.52.3 GPa. The friction tests were carried out under dry conditions and with an unadditivated paraffin oil as lubricant. It could be shown that the thickness of the coatings affects the respective wear life. Further, a very important factor for the wear life of a coating under lubricated slip-rolling conditions is the roughness of the surface of the respective counterbody. The wear life tests were monitored by recording in situ the Acoustic Emission (AE) signals. Some causes for a high AE activity could be identified.
Adhesion measurements are presented which were carried out with an atomic force microscope between polymer balls attached to a cantilever and a silicon wafer under ultra high vacuum conditions. In using a silicon surface with a defined structure a correlation between adhesion force and contact area was found. This correlation could partly be explained by the Johnson-Kendall-Roberts model, if a change of the surface energy is assumed as a result of the structuring. For a constant geometric contact area an additional structuring leads to a decrease of the adhesion force.
Coupons of X5CrNiCuNb16-4 with different surface roughness that may be utilized as injection pipe with 16% Chromium and 0.05% Carbon (1.4542, AISI 630) were exposed for 3000 h to CO2-saturated saline aquifer water simulating the conditions in the Northern German Basin at ambient pressure and 60 °C. Additionally, corrosion fatigue experiments (ambient pressure, technically clean CO2, saline aquifer water of Stuttgart Aquifer) were performed using specimen of X46Cr13 (1.4043, AISI 420C) with regard to the influence of the roughness of technical surfaces on the number of cycles to failure at different stress amplitudes. Specimen of Duplex stainless steel X2CrNiMoN22-3-2 (1.4462) for corrosion fatigue experiments were provided with technical surfaces after machining as well as polished surfaces. Results were obtained at load amplitudes ranging from 175 MPa to 325 MPa in the geothermal brine of the Northern German Basin at 98 °C. The main precipitation phases on the surface as well as within pits reveal carbonates or hydroxides such as siderite (FeCO3) and ferrous hydroxide goethite (FeOOH) independent of the original surface roughness. Corrosion rates for polished and technical surfaces were below 0.005 mm/year compared to corrosion rates of 0.035 mm/year after shot peening. Specimen with technical surfaces tested at high stress amplitudes (>275 MPa) lasted longer (cycles to failure: P50% at Sa 300 MPa=5x105) than specimen with polished surfaces (cycles to failure: P50% at Sa 300 MPa=1.5x105). This behavior is emphasized by the slope coefficient (technical surfaces k = 19.006, polished surfaces k=8.78) meaning earlier failure for polished at high stress amplitude Sa. Although rather low scatter ranges (technical surface: TN=1:1.35, polished surface: TN=1.1.95) indicate no change in failure mechanism it may be assumed that at low stress pitting is the initiating crack growth process whereas at high stress amplitudes the formation of micro cracks is reason for crack propagation and failure.
Contact formation and development are the basis of friction and wear modelling and understanding. Unanimously topography formation and development in friction contacts are regarded of highest importance for understanding and modelling friction processes. The frequently found running in behaviour of sliding contacts is—aside from the build up of reaction and transfer layers-at least partly caused by the topography development due to friction processes until a stable equilibrium state is reached.
Experimental results of friction and topography measurements are presented which demonstrate the mutual modification of friction and contact topography.
A special experimental set up with an AFM allowed to correlate the measured friction forces with the contact position and the topography at this point. In this way, friction force transitions and changes can be assigned to topography changes due to abrasion, adhesion and wear particle agglomeration.
Contact surfaces with artificial regular structures have been prepared to avoid problems with topography and friction correlation due to the statistical nature of roughness on technical contact surfaces. The friction effects of roughness were simulated by etched ditches of defined width, depth and distance on silicon or metal surfaces. This allowed to explain the mutual influences of topography and friction. The effect of a single asperity and of the 'roughness structures' could be demonstrated.
Topography measurements with an AFM correlated with the friction force could help to understand friction changes without changing any parameter.
Core-shell (CS) particles with a polymeric core and a silica shell play an important role in the materials and (bio)analytical sciences. Besides the establishment of reliable synthesis procedures, comprehensive particle characterization is essential for batch-to-batch reproducibility and objective performance assessment across architectures, protocols, and laboratories. Particle characterization with respect to size, size distribution, shell thickness and texture, surface area and roughness or materials composition is commonly conducted with different analytical methods, often on different samples. Our approach uses a dual-mode TSEM/SEM set-up with an EDX detector to obtain a complementary data set with sufficient statistical confidence of one and the same sample on a single instrument. Our protocol reveals information about size, size distribution and shell thickness of the various particles employed from overview images, while an increased field of view (FOV) and high-resolution EDX analysis yields detailed information on shell texture and elemental composition. An image analysis tool was developed to derive and quantify the profile roughness of CS particles from individual beads. Comparison with surface roughness data from AFM showed a similar trend in roughness across the series of particles. Reliable classification into smooth and rough is proposed and roughness changes within different particle batches were tracked systematically.
In this article we demonstrate the use of atomic force microscopy (AFM) measurements for the study of macroscopic wear scars. By stitching AFM images acquired over the wear scar, the detailed structure of the scar can be characterized even when the scar is much wider than the typical maximum scan range of the AFM (50–100 µm). The results obtained by AFM are compared with those yielded by white light interferometry (WLI). The comparison validates the WLI measurements; at the same time, it shows decisive differences in the resolutions of these two methods. As a consequence, AFM measurements are necessary whenever a precise characterization of the structure of the scar is required. However, since stitching of AFM images is rather time-consuming, white light interferometry is recommended as a faster method whenever experiments are aimed at just a gross characterization of the scar and the measurement of mean quantities (e.g. the wear volume).
Laser powder bed fusion (LPBF) of Ni-based superalloys shows great potential for high temperature applications, for example, as a burner repair application for gas turbines where the thin-walled structure is important. It motivates this work to investigate the evolution of microstructure and the anisotropic mechanical behavior when plate-like specimens are built with a thickness from 4 mm down to 1 mm. By performing texture analysis using neutron diffraction, a clear transition in fiber texture from <011> to <001> is indicated when the specimen becomes thinner. The residual stress shows no thickness dependence, and at the subsurface the residual stress reaches the same level as the yield strength. Due to the rough as-built surface, a roughness compensation method for mechanical properties of thin-walled structures is outlined and demonstrated. Tensile tests from room temperature up to 700 ◦C have been carried out. Anisotropic mechanical behavior is found at all temperatures, which is strongly related to the anisotropic texture evolution. Stronger texture evolution and grain rotations are discovered when the tensile loading is applied along the building direction. The mechanical behavior has been compared to a wrought material, where the high dislocation density and the subgrain structure of the LPBF material result in a higher yield strength. Combining the statistical texture analysis by neutron diffraction with mechanical testing, EBSD grain orientation mapping and the investigation of dislocation structures using transmission electron microscopy, this work illustrates the significance of texture for the thin-wall effect and anisotropic mechanical behavior of LPBF materials.