Performance of calcium phosphate cements in the augmentation of sheep vertebrae - An ex vivo study
(2021)
Oil-based calcium phosphate cement (Paste-CPC) shows not only prolonged shelf life and injection times, but also improved cohesion and reproducibility during application, while retaining the advantages of fast setting, mechanical strength, and biocompatibility. In addition, poly(L-lactideco-glycolide) (PLGA) fiber reinforcement may decrease the risk for local extrusion. Bone defects (diameter 5 mm; depth 15 mm) generated ex vivo in lumbar (L) spines of female Merino sheep (2–4 years) were augmented using: (i) water-based CPC with 10% PLGA fiber reinforcement (L3); (ii) Paste-CPC (L4); or (iii) clinically established polymethylmethacrylate (PMMA) bone cement (L5). Untouched (L1) and empty vertebrae (L2) served as controls. Cement performance was analyzed using micro-computed tomography, histology, and biomechanical testing. Extrusion was comparable for Paste-CPC(-PLGA) and PMMA, but significantly lower for CPC + PLGA. Compressive strength and Young’s modulus were similar for Paste-CPC and PMMA, but significantly higher compared to those for empty defects and/or CPC + PLGA. Expectedly, all experimental groups showed significantly or numerically lower compressive strength and Young’s modulus than those of untouched controls. Ready-to-use Paste-CPC demonstrates a performance similar to that of PMMA, but improved biomechanics compared to those of water-based CPC + PLGA, expanding the therapeutic arsenal for bone defects. O, significantly lower extrusion of CPC + PLGA fibers into adjacent lumbar spongiosa may help to reduce the risk of local extrusion in spinal surgery.
The mechanical properties of unstabilised earthen building materials are distinctively influenced by changes in material moisture content. However, this moisture-dependency often remains unconsidered in the calculation of the load-bearing capacity of earth constructions. This paper aims to derive a convenient way to sufficiently consider the impact of different material moisture contents on the mechanical properties of unstabilised earth masonry. Therefore, the influence of relative humidity and temperature on the strength and deformation characteristics of unstabilised earth blocks, earth mortar and earth masonry is evaluated by conducting compression tests under various climate conditions. The results show that the compressive strength and the modulus of elasticity are linearly correlated with the relative humidity, whereas changes in temperature at constant relative humidity have no significant influence. To account the distinct moisture-dependency, a general applicable modification factor for unstabilised earthen materials is provided, which enables the adjustment of the compressive strength and the modulus of elasticity in dependency of arbitrary hygroscopic material moisture contents.
block and mortar types is analysed with particular regard to the influence of varying relative humidity. The uniaxial compressive strength and deformation characteristics of unstabilised earth blocks and mortars as well as of unstabilised earth block masonry are studied in detail and compared to conventional masonry to evaluate whether the structural design can be made accordingly. An increase of 30 % points in relative humidity leads to a reduction of the masonry´s compressive strength between 33 % and 35 % whereas the Young´s modulus is reduced by 24–29 %. However, the ratio between the Young´s modulus and the characteristic compressive strength of earth block masonry ranges between E33/fk = 283–583 but is largely independent of the relative humidity. The results show that the mechanical properties of the investigated unstabilised earth block masonry are sufficient for load-bearing structures, yielding a masonry compressive strength between 2.3 MPa and 3.7 MPa throughout the range of moisture contents
investigated. In general, the design concept of conventional masonry can be adapted for unstabilised earth masonry provided that the rather low Young´s modulus as well as the moisture dependence of both, compressive strength and Young´s modulus, are sufficiently taken into
account.
Aim of this study is to provide information about moisture dependent material behaviour of unstabilised loadbearing earth blocks and mortars. Compressive strength and Young’s modulus were investigated after conditioning in varying relative humidity reaching from 40 % up to 95 %. The material composition and physical properties were investigated to understand the influence of relative humidity onto the mechanical properties. A normalisation of strength and stiffness by the values obtained at 23 ◦C and 50 % relative humidity reveals a linear dependence of compressive strength and Young’s modulus that is regardless of the material composition.
Thus, it is possible to describe the influence of relative humidity onto the load-bearing behaviour of unstabilised earth masonry materials in a generally valid formulation.
Several studies show that thermal and hydrothermal treatment can further improve the excellent properties of UHPC in terms of mechanical strength and durability. While for the thermal treatment the increase in strength is attributed to an intensified pozzolanic and hydraulic reaction, for the hydrothermal treatment previous studies accredited it mostly to the formation of tobermorite. In the presented study thermal and hydrothermal treatment of UHPC samples was systematically varied and the phase formation analysed related to the strength development of a reference sample cured for 28 days in water. For the thermal treatment the results show that the strength increase depends on the protection against desiccation and can be ascribed to an improved pozzolanic reaction of the siliceous fillers. To achieve a significant enhancement of strength, a pre-storage time of few days and a long dwell time at elevated temperature/pressure are required. For the hydrothermal treatment already heating the specimens up to 185 °C in saturated steam followed by an immediate cooling leads to a substantial increase in compressive strength. Pre-storage time did not affect the result as far as a minimum of several hours is guaranteed. The improved performance is due to an increase in the pozzolanic and hydraulic reaction. Surprisingly, tobermorite was only found within a very thin layer at the surface of the sample, but not in the bulk. Sulphate and aluminium stemming from the decomposition of the ettringite are bound in the newly formed phases hydroxylellestadite and hydrogarnet.
The aim of RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ is to identify and validate methodologies for testing the durability of alkali-activated concretes. To underpin the durability testing work of this committee, five alkali-activated concrete mixes were developed based on blast furnace slag, fly ash, and flash-calcined metakaolin. The concretes were designed with different intended performance levels, aiming to assess the capability of test methods to discriminate between concretes on this basis. A total of fifteen laboratories worldwide participated in this round robin test programme, where all concretes were produced with the same mix designs, from single-source aluminosilicate precursors and locally available aggregates. This paper reports the mix designs tested, and the compressive strength results obtained, including critical insight into reasons for the observed variability in strength within and between laboratories.
Within the presented research project, experimental and numerical investigations were performed to develop a thin-shelled, modular, mobile element system made of a micro-reinforced ultra-high-performance ductile concrete (DUCON®). Material parameters were experimentally determined to adapt the material model within the numerical analysis applying the Drucker-Prager relationship. Afterwards, for validation of the numerical models, quasi-static and high-velocity impact tests were performed on plate-like structures. Finally, a suitable geometry of transportable barrier elements will be designed, which provides a maximum of resistance against impact by a minimum of weight and a maximum of mobility.
Rice husk as (RHA) is an eco-friendly material, which can be used as a supplementary cementitious material (SCM) in cement and concrete. Due to the high water demand for the material, superplasticizers (SPs) are essential to improve the performance. However, the interaction between the SPs and RHA systems is limited. This paper investigates the interaction of the binders with three SPs, i.e. two polycarboxylate ethers (PCEs) and one lignosulphonate (LS). The investigations are performed on blended systems of mortar containing various percentages of RHA and limestone powder (LSP). LSP is used in this research to improve the workability of the mortar. The results from the zeta potential (ZP) shows that the SPs are extremely dependent on the pH of the suspension. At higher pH values such as in a cementitious system, the ZP becomes less negative indicating that the ions in the suspension interact with the carboxyl groups in the backbone of the polymers thus reducing the surface charges of the SP. The mini-slump flow shows that the workability of the blended mortar systems is significantly improved with the addition of SPs. LS systems with increasing RHA is observed to have similar workability as the control mix over time. The compressive strength test results show increased strength for all mortar specimens with added RHA and LSP at later ages.
The main aim of the research was the development of a first valid database for material parameters of earth block masonry (EBM) with particular regard to statistical characteristics. A solid database is needed for the determination of the materials partial safety factor. Therefore, compressive strength tests were carried out with two types of earth blocks and two types of prefabricated earth mortar.
The evaluation has shown that the mean variation of the compressive strength was remarkably less than expected, which indicates high quality standards of the components earth block and mortar with regard to industrial production. Using the reliability method, a partial safety factor for EBM subjected to compression was determined on the basis of these test results. The findings have shown that a common calculation method for EBM based on partial safety factors following the valid masonry construction standard is feasible.
The paper presented here deals with rheological and hardening properties during the setting reaction, and density and compressive strength after the final setting of a figuline composite consisting of Ca2KNa(PO4)2 and 2wt% medium gel strength gelatin. Compared to the composite with monomodal particle size distribution (d50=7.18µm; span=3.9) and its properties during and after setting reaction, the goal of this work is to increase the resulting product compressive strength by mixing different particle sizes in order to obtain bi- and trimodal distributions. For the bimodal powder mixtures the ratio in diameter (dcourse/dsmall) was chosen with 7/1 and volume ratio dcourse/dsmall was 70/30%. For the trimodal powder mixtures the ratio in diameter (dcourse/dmedium/dsmall) was chosen with 70/7/1 and volume ratio dcourse/dmedium/dsmall was set to 44/28/28%.After establishing an adequate crushing and sieving process the tap density and powder density of each fraction was determined. Subsequently, the different particle sizes were mixed and the densities and the Hausner ratio were determined again. The mixtures show an increase in both densities especially the tap density increased significantly. Rheological investigations show that the graphs of storage and loss moduli of the multimodal powder mixtures respectively are similar. The characteristic setting times show a slight decrease compared with the monomodal composite but not significantly different data. When comparing the resulting compressive strength of cylindrical samples, which were stored direct after reaching the initial setting time under physiological conditions, the studies illustrated in all cases for the multimodal mixtures a significant increase in compressive strength and a higher density.