The dynamic glass transition (α relaxation, structural relaxation) of ultrathin polysulfone films prepared between aluminum electrodes is investigated by dielectric relaxation spectroscopy. As a main result, it is found that the glass transition temperature Tg does not depend on the thickness of the polymeric layer down to a thickness of 10 nm. For thicknesses lower than 10 nm, an increase of Tg is observed. A more detailed analysis of the temperature dependence of the relaxation rates reveals that the Vogel temperature increases and the fragility decreases systematically with decreasing film thickness d. Further, the dielectric strength Δε decreases with decreasing d. This is discussed by the formation of a surface layer of adsorbed polysulfone segments having a reduced molecular mobility with regard to the time scale characteristic of the glassy dynamics of bulk polysulfone. Plotted versus inverse film thickness Δε decreases linearly with 1/d and becomes zero for an extrapolated length scale of 10 nm. From that it is concluded that the thickness of the adsorbed boundary layer is about 5 nm. Contact-angle measurements were carried out to confirm the strong interaction between aluminum and polysulfone. It is also shown that preparation details like annealing conditions strongly influence the glass transition of supported ultrathin films.
Interference fringes in the far-infrared spectra of thin films are the result of the coherent adding up of waves and can influence the spectral interpretation by concealing smaller features. A number of methods have been developed in order to eliminate such oscillating features from the transmittance spectrum. The paper critically evaluates the total transmission-reflection technique and applies the method to quantify the spectra of different polymer films.
Broadband dielectric spectroscopy (BDS), capacitive scanning dilatometry (CSD) and differential ac-chip calorimetry (DACC) were used to examine the glass transition and segmental dynamics of ultrathin poly(bisphenol A carbonate) (PBAC) films. An increase of Vogel temperature (T0) as well as glass transition temperature (Tg) with decreasing film thickness was observed when the thickness is less than 20 nm. Moreover, the segmental relaxation time at a fixed temperature was found to increase for the aluminium (Al) capped PBAC films (<20 nm) in the BDS measurements, whereas in the DACC measurements no thickness dependency of the segmental dynamics was detected within the experimental error limit for the supported PBAC films (10-55 nm). These properties are discussed in terms of the thin film geometry and the relevant interfacial interaction between the polymer and the substrate.