Isosorbide, succinyl chloride and isophthaloyl chloride are polycondensed under various reaction conditions. The heating in bulk with or without catalysts as well in an aromatic solvent without catalyst, and polycondensation with the addition of pyridine only yield low molar mass copolyesters. However, heating in chlorobenzene with addition of SnCl2 or ZnCl2 produces satisfactory molar masses. The number average molecular weights (Mn) of most copolyesters fall into the range of 7000–15,000 Da with polydispersities (PD) in the range of 3–9. The MALDI-TOF mass spectra almost exclusively displayed peaks of cyclics indicating that the chain growth was mainly limited by cyclization and not by side reactions, stoichiometric imbalance or incomplete conversion. The glass-transition temperatures increased with the content of isophthalic acid from 75 to 180 °C and the thermo-stabilities also followed this trend.
Various copolyesters of lactide, isosorbide, and terephthalic acid are prepared by a two-step process performed in a 'one-pot' procedure, beginning with an isosorbide-initiated oligomerization of L-lactide followed by polycondensation with terephthaloyl chloride using SnCl2 as a catalyst for both steps. The SEC data show the formation of random copolyesters with high polydispersities as a consequence of the relatively high fraction of cyclics proved by matrix-assisted laser desorption ionization time-of-flight mass spectrometry (MALDI-TOF MS). The glass-transition temperatures (89–180 °C) obey an almost linear trend with the molar composition. The thermostability decreases with increasing lactide content. The successful incorporation of phenyl phosphate results in copolyesters of lower inflammability.
Starting from dibutyltin oxide, four catalysts were synthesized, namely the dibutyltin bisphenoxides of Phenol (SnPh), 4-chlorophenol (SnCP), 4-hydroxybenzonitrile (SnCN) and pentafluorophenol (SnOPF). With the first three catalysts polymerizations of L-lactide at 160 °C in bulk yielded large fraction of linear chains having phenylester end groups at short reaction times. At longer times the fraction of cycles considerably increased at the expense of the linear chains, when SnCN was used as catalyst. With SnOPF only cyclic polylactides were obtained at low Lac/Cat ratios (< 400) with weight average molecular weights (Mw) up to 90 000 Da, whereas for high Lac/Cat ratios mixtures of cyclic and linear chains were found. Polymerizations in solution enabled variation of the molecular weight. Polymerizations of meso-lactide at temperatures down to 60 °C mainly yielded even-numbered linear chains supporting the postulated ROPPOC mechanism.
Various catalysts and polycondensation mechanisms (ROPPOC/REP/ROP)were presented and discussed with regard to the Formation of cyclic and linear polylactides. It could be shown that depending on the structure of the catalyst even- and od numbered cyclics were selectively formed. These data were supported by various analytical techniques like MALDI-TOF mass spectrometry and Size Exclusion Chromatography.
Poly(alkylene isophthalate)s were prepared by different methods, either in solution or in bulk. The SEC measurements were evaluated in such a way that all oligomers were included. In solution (monomer conc. 0.10.7 mol/L) large fractions of rings were formed and high dispersities (up to 12) were obtained, which disagree with theoretical predictions. Polycondensations in bulk did neither generate cyclics by 'back-biting' nor by end-to-end cyclization, when the maximum temperature was limited to 210 °C. The dispersities of these perfectly linear polyesters were again higher than the theoretical values. Regardless of the synthetic method monomeric cycles were never observed. Furthermore, SEC measurements performed in tetrahydrofuran and in chloroform and SEC measurements performed in three different institutes were compared. Finally, SEC measurements of five samples were performed with universal calibration and a correction factor of 0.71 ± 0.02 was found for normal calibration with polystyrene.
Using SnCl2, ZnCl2, Zn-lactate or Zr-acetylacetonate as catalysts ʟ-lactide was oligomerized in bulk with isosorbide as initiator. The ratio isosorbide/lactide was varied from 8/2 to 2/8. The resulting oligomers were in situ polycondensed with isophthaloyl chloride in various aromatic solvents. In chlorobenzene homogeneous reaction mixtures were obtained, whereas molten copolyesters precipitated from toluene and xylene. The obtained average molecular weights indicated high polydispersities. According to MALDI-TOF MS the low molar mass reaction products (<4 kDa) almost exclusively consisted of cyclics with a composition depending on the feed ratio. The glass-transition temperatures (Tg) varied between the values of poly(ʟ-lactide (64 °C) and poly(isosorbide isophthalate) (180 °C). Four polyesters prepared from 5-tert-butyl isophthalic acid displayed higher Tg values. Differential thermoanalysis evidenced that the thermostability decreases with higher fractions of lactide, but processing from the melt seems to be feasible up to temperatures of 260 °C without risking degradation.
Hydrolytic condensation of different methacrylate groups containing alkoxy silanes yielded resins which showed interesting properties as a matrix for dental composites. For this purpose, resins of low viscosity are desired resulting in composites with a high amount of inorganic fillers. Our investigations demonstrated that the viscosity of the obtained polycondensates was predominantly influenced by the kind of organic spacer between the methacrylate group and the silicon atom. In addition, the viscosity also significantly changed in dependence of the kind of structure units built. NMR spectroscopic investigations as well as size exclusion chromatography (SEC) and matrix-assisted laser desorption/ionization time-of-flight (MALDI-TOF) mass spectrometry showed that the formed structures depended both on the kind of catalyst used for hydrolysis/condensation and the bulkiness of the organic substituent at the silicon atom.
Using 22 metal triflates as catalysts, ε-caprolactone is polymerized at 22 °C in bulk. Only five relatively acidic triflates prove active. Three triflates, including the neutral Sm3+, are active using water as initiator. A very low content of cyclics is found in all the experiments. With Ce3+ and Ce4+, polymerizations are performed in CH2Cl2 and in bulk at 2 °C and 22 °C. Low dispersities (down to 1.1) are obtained. At 22 °C, Ce4+ and, even better, Ce3+ also catalyze syntheses of CO2H- and CH2OH-terminated polycaprolactones, whereby higher dispersities and larger fractions of cyclics are obtained. Further polymerizations and polycondensations are catalyzed with protic acids. The results can be explained by a proton-catalyzed activated monomer mechanism.
Poly(ether sulfone)s were prepared by polycondensation of silylated 4-tert-butylcatechol and 4,4?-difluorodiphenylsulfone in N-methylpyrrolidone. The feed ratio and the reaction time were varied to study the influence of stoichiometry and conversion on molecular weight and extent of cyclization. Molecular weights and molecular weight distributions (MWD)s were characterized by SEC measurements calibrated with polystyrene. Light scattering confirmed that calibration with polystyrene gives reasonable results and revealed a tendency towards a bimodal MWD for the samples rich in cycles. The MALDI-TOF mass spectrometry indicated that the extent of cyclization increased with higher conversion and with optimization of the stoichiometry. This interpretation was confirmed by 1H NMR endgroup analyses. For the samples with the highest molar masses only mass peaks of cycles were found, which were detectable up to 20 000 Da before and up to 27 000 Da after fractionation. Via the pseudo-high dilution method low molar mass poly(ether sulfone) containing more than 95 mol% of cycles were prepared, and even these low molar mass samples had broad MWDs. DSC measurements indicated that the glass transition temperatures depend on the structure of the endgroups and increase with higher fractions of cycles.
Numerous polycondensations of isosorbide and suberoyl chloride or other aliphatic dicarboxylic acid dichlorides were performed with pyridine as a catalyst and HCl acceptor. The reaction conditions were varied to optimize both the molecular weight and the fraction of cyclic oligo- and polyesters. Furthermore, we attempted to obtain the cyclic monomer by catalyzed back-biting degradation of the molten cyclic polyesters above 220 °C in vacuo. The polyesters were characterized by viscosity and size exclusion chromatographic measurements as well as matrix-assisted laser desorption/ionization time-of-flight mass spectrometry. In selected cases, mixtures of linear and cyclic polyesters were treated with a hot solution of partially methylated ß-cyclodextrin in methanol. This treatment allowed for a selective extraction of the linear chains up to approximately 5000 Da.
Various dibutyltin derivatives were polycondensed with aliphatic ,-dicarboxylic acids having chain lengths from 4 (succinic acid) to 22 carbon atoms. White crystalline products were obtained from all experiments, and the structure of the products was independent of the synthetic method. Viscosity measurements revealed low molecular weights (n 1 500 Da) in all cases. Vapor pressure osmometry (VPO) measurements and matrix-assisted laser desorption time-of-flight (MALDI-TOF) mass spectrometry proved that cyclic dimers and trimer were formed from dicarboxylic acids having 6 to 16 carbons, but mainly the monomeric cycle from docosane dioic acid. Heating to 250°C did not change the structure. Therefore, the results indicate that the macrocycles are the result of a thermodynamically controlled ring-closing polycondensation. This means that linear high-molecular weight poly(dibutyltin dicarboxylate)s cannot exist above room temperature.
Using three different catalysts, water-initiated polymerizations of ε-caprolactone were conducted in bulk with variation of the monomer/water ratio. The resulting CH2OH and CO2H- terminated polylactones were subjected in situ to azeotropic polycondensations. With Bi-triflate and temperatures, the polycondensations were not much successful and involved side reactions. With ZnCl2, and especially SnCl2, considerably higher molar masses were achieved. The substitution of toluene for chlorobenzene for refluxing gave better results. The polycondensations broadened the molar mass distribution of the ROP-based prepolymers, and polydispersities between 1.4–1.8 were obtained. The MALDITOF mass spectra revealed that the polycondensations significantly enhanced the fraction of rings due to efficient 'end-biting' reactions. By comparison with copolymerization experiments and Sn methoxide-initiated polymerizations, it was demonstrated that equilibration reactions, such as the formation of rings by 'back-biting,' did not occur.
Poly(ester urethane)s derived from lactide, isosorbide, terephthalic acidm abd various diisocyanates
(2014)
Isosorbide-initiated oligomerizations of ʟ-lactide were preformed in bulk using SnCl2 as catalyst. The resulting telechelic OH-terminated oligoesters were in situ subjected to simultaneous polycondensation and polyaddition with mixtures of terephthaloyl chloride and diisocyanates. Most polymerizations were conducted with 4,4'-diisocyanatodiphenyl methane and 2,4-diisocyanato toluene. The consequences of excess diisocyanate and four different catalysts were studied. The isosorbide/lactide ratio and the terephthalic acid/diisocyanate ratio were varied. Number average molecular weights up to 15 kDa with polydispersities around 3–5 were obtained. Depending on the chemical structure of the copolyester and on the feed ratio, incorporation of urethane groups may reduce or enhance the glass-transition temperature, but the thermal stability decreases dramatically regardless of composition.
Polymerizations of L-lactide catalyzed either by neat SnCl2 or by SnCl2 + difunctional cocatalysts were conducted in bulk at 180, 160 and 140 °C with variation of the Lac/Cat ratio and time. With neat SnCl2 poly(L-lactide) having weight average molecular weights (uncorrected Mw’s) up to 190 000 g mol−1 were obtained mainly consisting of linear chains. Addition of salicylic acid or 1,1-bisphenol yielded a higher fraction of cyclic polylactides but lower molecular weights. Furthermore, SnCl2 was compared with Bu2SnCl2 and various other metal chlorides and the best results were obtained with SnCl2. With ethyl L-lactate as initiator SnCl2-catalyzed ROPs were performed at 120 °C and the lac/initiator ratio was varied. All these experiments were conducted under conditions allowing for comparison with ROPs catalyzed with neat Sn(II)-2-ethyhexanoate. Such a comparison was also performed with ε-caprolactone as monomer.
L-Lactide was polymerized with tin(II)acetate, tin(II)2-ethyl hexanoate, diphenyltin dichloride and dibutyltin bis(pentafluorophenoxide) at 130 °C in bulk. When an alcohol was added as initiator, linear chains free of cycles were formed having a degree of polymerization (DP) according to the lactide/initiator (LA/In) ratio.
Analogous polymerizations in the absence of an initiator yielded high molar mass cyclic polylactides.
Quite similar results were obtained when ε-caprolactone was polymerized with or without initiator.
Several transesterification experiments were conducted at 130 °C, either with polylactide or poly(ε-caprolactone) indicating that several transesterification mechanisms are operating under conditions that do not include formation of cycles by back-biting. Furthermore, reversible polycondensations (revPOCs) with low or moderate conversions were found that did not involve any kind of cyclization. Therefore, These results demonstrate the existence of revPOCs, which do neither obey the theory of irreversible polycondensation as defined by Flory nor the hypothesis of revPOCs as defined by Jacobson and Stockmayer. A new concept encompassing any kind of revPOCs is formulated in the form of a “polycondensation triangle”.
Polycondensations of 1,6-hexane diol and sebacic acid were conducted in bulk with addition of a lanthanide triflate as acidic catalyst. With exception of promethium triflate all lanthanide triflates were studied. A particularly low molecular weight was obtained with neodym triflate and the best results with samarium triflate. With Sm(OTf)3 weight average (Mw) values up to 65 kDa (uncorrected SEC data) were achieved after optimization of the reaction conditions. Comparison of these results with those obtained from bismuth, magnesium, and zinc triflates, on the one hand, and comparison with the acidities of all catalysts, on the other, indicates that the esterification mechanism involves complexation of monomer by metal ions. Preparation of multiblock copoly(ether ester)s failed due to insufficient incorporation of poly(tetrahydrofuran) diols.
Different strategies for the synthesis of polylactides were presented with special focus on Ring-opening Polymerization (ROP) and simultaneous ROP and Polycondensation (ROPPOC) mechanism. The mechanism of the formation of cyclic Polyesters is discussed in detail and established theories about the formation of cycles in polycondensation reactions are critically reviewed.