Filtern
Dokumenttyp
Sprache
- Englisch (3)
Referierte Publikation
- ja (3)
Schlagworte
- Polycarbonate blends (3) (entfernen)
Various inorganic additives belonging to four different groups: layered materials, metal hydroxides, metal oxides/carbonate and metal borates are investigated in bisphenol A polycarbonate/silicon rubber/bisphenol A bis(diphenyl phosphate) (PC/SiR/BDP) to improve flame retardancy. The pyrolysis, reaction to small flame and fire behaviour of the blends are characterised and structure–property relationships discussed. Among the added layered materials, talc functions as an inert filler with potential for commercialisation, whereas organically modified montmorillonite (LS) enhances decomposition. PC/SiR/BDP + talc and PC/SiR/BDP + LS reinforce the char and induce a flow limit. The different dispersion and location of boehmite (AlO(OH)) nano-particles and Mg(OH)2 micro-particles determine the impact on performance. PC/SiR/BDP + Mg(OH)2 shows additional hydrolysis and thus reduced flame retardancy. AlO(OH) is embedded in SiR and thus behaves as an inert filler. Both additives worked as smoke suppressants. Using selective filling with nano-particles is proposed as an interesting route for flame retardancy in PC/SiR blends. Adding metal oxides and carbonate (MgO, CaCO3 and SiO2) changes the decomposition pathways of PC/SiR/BDP, worsening the fire performance of PC/SiR/BDP. CaCO3 harbours the potential to intumescence, even though an early collapse of the char structure occurred. Adding hydrated metal borates, CaB, MgB and ZnB, changes the pyrolysis and flame retardancy action. Smoke suppression occurs; LOI is improved as well as UL 94 classification. ZnB performs better than MgB and CaB. The comprehensive study, also based on systematic material variation, delivers valuable guidelines for future development of flame-retarded multi-component PC blends.
In this first of two papers, the thermal decomposition of bisphenol A bis(diphenyl phosphate)-flame retarded polycarbonate (PC) blends with different impact modifiers was studied. The impact modifiers were an acrylonitrile-butadiene-styrene (ABS), a poly(n-butyl acrylate) (PBA) rubber with a poly(methyl methacrylate) (PMMA) shell and two silicone-acrylate rubbers consisting of PBA with different amounts of polydimethylsiloxane (PDMS) and different shells (PMMA and styrene-acrylonitrile, SAN). The focus of this work was to study the impact of the acrylate and silicon-acrylate rubbers with respect to pyrolysis and flame retardancy in comparison to common ABS. Thermogravimetry (TG) was performed to investigate the pyrolysis behaviour and reaction kinetics. TG in combination with FTIR identified the pyrolysis gases. Solid residues were investigated by FTIR-ATR. PC/ABS shows two-step decomposition, with PC decomposing independently from ABS at higher temperatures. Pure acrylate rubber destabilises PC due to interactions between the rubber and PC, which leads to earlier decomposition of PC. Using silicone-acrylate rubbers led to similar results as PC/ABS with respect to pyrolysis, reaction kinetics and analysis of the solid residue; hence the exchange of ABS for the silicone-acrylate rubbers is possible.
In this second of a series of two papers, the fire behaviour of halogen-free flame retarded polycarbonate (PC) blends with different impact modifiers was studied. The impact modifiers were acrylonitrile-butadiene-styrene (ABS), a poly(n-butyl acrylate) rubber (PBA) with a poly(methyl methacrylate) (PMMA) shell and two silicone-acrylate rubbers consisting of PBA with different amounts of polydimethylsiloxane (PDMS) and different shell materials (PMMA and styrene-acrylonitrile, SAN). The flame retardant was bisphenol A bis(diphenyl phosphate) (BDP). Flammability was determined by LOI and UL 94. The burning behaviour under forced flaming conditions was studied by cone calorimeter under different external irradiations and by pyrolysis combustion flow calorimeter measurements. The exchange of ABS with the pure acrylate rubber worsened flammability, while similar results were obtained in cone calorimeter measurements. The exchange of ABS with the silicone-acrylate rubbers is promising, particularly with higher amounts of PDMS. In flammability tests strongly enhanced LOI values were obtained and therefore silicone-acrylate rubbers look like promising alternatives for ABS.