Additive manufacturing (AM) of metals and in particular laser powder bed fusion (LPBF) enables a degree of freedom in design unparalleled by conventional subtractive methods. To ensure that the designed precision is matched by the produced LPBF parts, a full understanding of the interaction between the laser and the feedstock powder is needed. It has been shown that the laser also melts subjacent layers of material underneath. This effect plays a key role when designing small cavities or overhanging structures, because, in these cases, the material underneath is feed-stock powder. In this study, we quantify the extension of the melt pool during laser illumination of powder layers and the defect spatial distribution in a cylindrical specimen. During the LPBF process, several layers were intentionally not exposed to the laser beam at various locations, while the build process was monitored by thermography and optical tomography. The cylinder was finally scanned by X-ray computed tomography (XCT). To correlate the positions of the unmolten layers in the part, a staircase was manufactured around the cylinder for easier registration. The results show that healing among layers occurs if a scan strategy is applied, where the orientation of the hatches is changed for each subsequent layer. They also show that small pores and surface roughness of solidified material below a thick layer of unmolten material (>200 µm) serve as seeding points for larger voids. The orientation of the first two layers fully exposed after a thick layer of unmolten powder shapes the orientation of these voids, created by a lack of fusion.
For a deep process understanding of the laser powder bed fusion process (PBF-LB/M), recording of the occurring surface temperatures is of utmost interest and would help to pave the way for reliable process monitoring and quality assurance. A notable number of approaches for in-process monitoring of the PBF-LB/M process focus on the monitoring of thermal process signatures. However, due to the elaborate calibration effort and the lack of knowledge about the occurring spectral directional emissivity, only a few approaches attempt to measure real temperatures. In this study, to gain initial insights into occurring in the PBF-LB/M process, measurements on PBF-LB/M specimens and metal powder specimens were performed for higher temperatures up to T = 1290 °C by means of the emissivity measurement apparatus (EMMA) of the Center for Applied Energy Research (CAE, Wuerzburg, Germany). Also, measurements at ambient temperatures were performed with a suitable measurement setup. Two different materials—stainless steel 316L and aluminum AlSi10Mg—were examined. The investigated wavelength λ ranges from the visible range (λ-VIS = 0.40–0.75 µm) up to the infrared, λ = 20 µm. The influence of the following factors were investigated: azimuth angle φ, specimen temperature TS, surface texture as for PBF-LB/M surfaces with different scan angles α, and powder surfaces with different layer thicknesses t.
In this chapter, the current state-of-the-art of in situ monitoring and in situ NDE methods in additive manufacturing is summarized. The focus is set on methods, which are suitable for making statements about the quality and usability of a component currently being manufactured. This includes methods which can be used to determine state properties like temperature or density, other physical properties like electrical or thermal conductivity, the microstructure, the chemical composition, the actual geometry, or which enable the direct detection of defects like cracks, voids, delaminations, or inclusions. Thus, optical, thermographic, acoustic, and electromagnetic methods, as well as methods being suitable for investigating particle and fume emission are presented. The requirements of in situ monitoring methods with a focus on thermographic methods are discussed by considering different additive manufacturing processes like laser powder bed fusion (PBF-LB/M) and direct energy deposition (DED-LB/M). Examples of the successful implementation and applications of such monitoring methods at BAM are given. The in situ monitoring and NDE methods are compared against post-process NDE methods. The advantages and challenges of in situ methods concerning real-time data analysis and the application of AI algorithms are addressed and discussed.
For a deep process understanding of the laser powder bed fusion process (PBF-LB/M), recording of the occurring surface temperatures is of utmost interest and would help to pave the way for reliable process monitoring and quality assurance. A notable number of approaches for in-process monitoring of the PBF-LB/M process focus on the monitoring of thermal process signatures. However, due to the elaborate calibration effort and the lack of knowledge about the occurring spectral directional emissivity, only a few approaches attempt to measure real temperatures. In this study, to gain initial insights into occurring in the PBF-LB/M process, measurements on PBF-LB/M specimens and metal powder specimens were performed for higher temperatures up to T = 1290 °C by means of the emissivity measurement apparatus (EMMA) of the Center for Applied Energy Research (CAE, Wuerzburg, Germany). Also, measurements at ambient temperatures were performed with a suitable measurement setup. Two different materials—stainless steel 316L and aluminum AlSi10Mg—were examined. The investigated wavelength λ ranges from the visible range (λ-VIS= 0.40–0.75 µm) up to the infrared, λ = 20 µm. The influence of the following factors were investigated: azimuth angle φ, specimen temperature TS, surface texture as for PBF-LB/M surfaces with different scan angles α, and powder surfaces with different layer thicknesses t.
The capability to produce complexly and individually shaped metallic parts is one of the main advantages of the laser powder bed fusion (PBF LB/M) process. Development of material and machine specific process parameters is commonly based on results acquired from small cubic test coupons of about 10 mm edge length. Such cubes are usually used to conduct an optimization of process parameters to produce dense material. The parameters are then taken as the basis for the manufacturing of real part geometries. However, complex geometries go along with complex thermal histories during the manufacturing process, which can significantly differ from thermal conditions prevalent during the production of simply shaped test coupons. This may lead to unexpected and unpredicted local inhomogeneities of the microstructure and defect distribution in the final part and it is a root cause of reservations against the use of additive manufacturing for the production of safety relevant parts. In this study, the influence of changing thermal conditions on the resulting melt pool depth of 316L stainless steel specimens is demonstrated. A variation of thermo-graphically measured intrinsic preheating temperatures was triggered by an alteration of inter layer times and a variation of cross section areas of specimens for three distinct sets of process parameters. Correlations between the preheating temperature, the melt pool depth, and occurring defects were analyzed. The limited expressiveness of the results of small density cubes is revealed throughout the systematic investigation. Finally, a clear recommendation to consider thermal conditions in future process parameter optimizations is given.
The capability to produce complexly and individually shaped metallic parts is one of the main advantages of the laser powder bed fusion (PBF LB/M) process. Development of material and machine specific process parameters is commonly based on results acquired from small cubic test coupons of about 10 mm edge length. Such cubes are usually used to conduct an optimization of process parameters to produce dense material. The parameters are then taken as the basis for the manufacturing of real part geometries. However, complex geometries go along with complex thermal histories during the manufacturing process, which can significantly differ from thermal conditions prevalent during the production of simply shaped test coupons. This may lead to unexpected and unpredicted local inhomogeneities of the microstructure and defect distribution in the final part and it is a root cause of reservations against the use of additive manufacturing for the production of safety relevant parts. In this study, the influence of changing thermal conditions on the resulting melt pool depth of 316L stainless steel specimens is demonstrated. A variation of thermo-graphically measured intrinsic preheating temperatures was triggered by an alteration of inter layer times and a variation of cross section areas of specimens for three distinct sets of process parameters. Correlations between the preheating temperature, the melt pool depth, and occurring defects were analyzed. The limited expressiveness of the results of small density cubes is revealed throughout the systematic investigation. Finally, a clear recommendation to consider thermal conditions in future process parameter optimizations is given.
Die additive Fertigung von Metallen hat inzwischen einen Reifegrad erreicht, der einen Einsatz in vielen Industriezweigen ermöglicht oder in greifbare Nähe rückt. Die Vorteile liegen vor allem in der Möglichkeit der Fertigung komplexer Bauteile, die sich konventionell nicht oder nur sehr aufwändig produzieren lassen, sowie in der Fertigung von hochindividualisierten Bauteilen in kleinen Stückzahlen. Allerdings ist der additive Fertigungsprozess hoch komplex und fehleranfällig. Um eine insbesondere für sicherheitsrelevante Bauteile notwendige Qualitätskontrolle zu gewährleisten, ist aktuell aufwändige nachgelagerte ZfP der einzelnen Bauteile notwendig. Alternativen könnten die In-situ-Prozessüberwachung und -prüfung bieten, die aktuell aber noch keinen ausreichenden Entwicklungsstand erreicht haben. Industrielle Fertigungsanlagen bieten keine oder nur geringe Flexibilität und Zugänglichkeit, um umfangreiche Untersuchungen auf diesem Gebiet zu ermöglichen. Daher haben wir an der BAM ein System für den Prozess des selektiven Laserschmelzens (PBF-LB/M) entwickelt, genannt SAMMIE. Es bietet eine komplett offene Systemarchitektur mit voller Kontrolle über den Prozess und flexiblem Zugang zur Baukammer, z.B. optisch sowohl direkt als auch koaxial zum Fertigungslaser. In diesem Beitrag stellen wir das System vor und zeigen erste experimentelle Ergebnisse der In-situ-Überwachung und -prüfung: Thermografische Schmelzbadüberwachung, optische Tomografie und In-situ-Laserthermografie. SAMMIE ermöglicht uns grundlegende Untersuchungen, die helfen werden, die In-situ-Prozessüberwachung und -prüfung weiterzuentwickeln, neue Erkenntnisse über die additive Fertigung zu gewinnen und die Sicherheit und Zuverlässigkeit des Prozesses zu verbessern.