Filtern
Dokumenttyp
Sprache
- Englisch (319)
- Deutsch (2)
- Mehrsprachig (1)
Referierte Publikation
- ja (322) (entfernen)
Schlagworte
- Additive manufacturing (35)
- Laser beam welding (31)
- Microstructure (23)
- Wear (21)
- Welding (21)
- Friction (16)
- Hydrogen (16)
- Mechanical properties (16)
- Residual stress (16)
- Residual stresses (15)
Organisationseinheit der BAM
- 9 Komponentensicherheit (322) (entfernen)
Paper des Monats
- ja (10)
In order to satisfy the growing requirements towards lightweight design and resource efficiency in modern steel constructions, e.g., mobile cranes and bridges, high-strength steels with typical yield strength ≥ 690 MPa are coming into use to an increasing extent. However, these steels require special treatment in welding. The susceptibility for degradation of the mechanical properties
in the presence of hydrogen increases significantly with increasing yield strength. In case of missing knowledge about how and the amount of hydrogen that is uptaken during welding, hydrogen-assisted cracking (HAC) can be a negative consequence.
Moreover, modern weld technology like the modified spray arc process enables welding of narrower weld seams. In this context,
a reduced number of weld beads, volume, and total heat input are technical and economical benefits. This work presents the influence of welding parameters on the diffusible hydrogen content in both (1) single-pass and (2) multi-layer welds. Different
hydrogen concentrations were detected by varied contact tube distance, wire feed speed, arc length, and varied arc type (transitional
arc and modified spray arc). The results show that all welding parameters have significant influence on the diffusible hydrogen concentration in the single-pass welds. By increasing the number of weld beads in case of multi-layer welding, the
hydrogen concentration has been reduced. Whereby, differences in hydrogen concentrations between both arc types are present.
Partial penetration welding with fiber laser on 20mm thick plates was carried out in horizontal position to study the role of secondary heating in modeling of high power fiber laser welding. Experiments were carried out using 18.8kW laser with 1.5 m/min welding speed at Ar assist gas flow rates of 0, 17, 29, and 40 l/min, all four cases show similar bead shape with bright emission of vapor plume. Numerical simulations were performed using volume of fluid method by considering three different models as models A–C. Model A considers only Fresnel reflection inside the keyhole using real time tracking of free surface. Model B considers vapor recondensation flux inside keyhole along with model A. Finally, model C is used, which considers vapor plume heating at 4100K temperature along with models A B. Secondary heating by recondensation and vapor plume is vital in modeling of high power fiber laser welding; especially, the upper part of the bead is more influenced due to secondary heating. Tungsten particles are also used to visualize the flow pattern of melt pool.
Analytical flaw assessment
(2018)
The paper provides a review on analytical flaw assessment methods with the focus on fracture under monotonic loading and fatigue crack propagation. The first topic comprises linear elastic as well as elastic-plastic fracture mechanics approaches. It essentially follows their historical development. Topics which are separately discussed are reference/Limit loads, the treatment of secondary stresses, strength mismatch, constraint, unstable crack propagation (monotonic R-curve analyses) and statistical aspects. With respect to fatigue crack propagation the analytical treatment of crack closure and constraint and the Determination of the cyclic elastic-plastic crack driving force is discussed. Finally, cyclic Rcurve analyses are briefly addressed.
Research and development of WC grades is 90 years ahead of niobium carbide-based hard materials, which showed already as light-weight and unexplored material a very high potential for many technical applications, especially for wear protection and machining. NbC evoluted recently from lab scale to pilot scale, especially in areas where established WC-based materials are causing economic, environmental or technical concerns. Benchmark trials of NbC-based hard metals indicated already a favorable performance in machining of steel components.
In an increasing number of modern steel applications, high-strength structural steel grades are demanded to meet specifications regarding a high load-bearing capacity and a low operating weight. Lightweight design rules enhance the safety requirements, especially for welded joints. Besides a higher cracking risk for high-strength steel welds, the formation of tensile residual stresses might lead to fracture due to overloading or premature failure if not adequately considered. In this study, a stress-strain analysis was conducted at component-related structures from S960QL using digital image correlation while preheating, welding and cooling adjacent to the weld seam. X-ray diffraction analysis of the local residual stresses in the weld seam showed a good comparability with global analyses using either a DIC system or a special testing facility, which allowed in situ measurements of welding loads. By analysing two different seam geometries, it could be shown that lower multi-axial stresses arise if a narrower weld groove is used. Comparative analyses revealed a direct correlation of the local residual stresses in the weld with transverse shrinkage restraint, whereas the residual stress level in the HAZ is significantly affected by the bending restraint of the weld construction and the occurring bending stresses, respectively.
A three-dimensional multi-physics numerical model was developed for the calculation of an appropriate equivalent volumetric heat source and the prediction of the transient thermal cycle during and after fusion welding. Thus the modelling process was separated into two studies. First, the stationary process simulation of full-penetration keyhole laser beam welding of a 15 mm low-alloyed steel thick plate in flat position at a welding speed of 2 m/min and a laser power of 18 kW was performed. A fixed keyhole with a right circular cone shape was used to consider the energy absorbed by the workpiece and to calibrate the model. In the calculation of the weld pool geometry and the local temperature field, the effects of phase transition, thermo-capillary convection, natural convection and temperature-dependent material properties up to evaporation temperature were taken into account. The obtained local temperature field was then used in a subsequent study as an equivalent heat source for the computation of the transient thermal field during the laser welding process and the cooling stage of the part. The system of partial differential equations, describing the stationary heat transfer and the fluid dynamics, were strongly coupled and solved with the commercial finite element software COMSOL Multiphysics 5.0. The energy input in the transient heat transfer simulation was realised by prescription of the nodes temperature. The prescribed nodes reproduced the calculated local temperature field defining the equivalent volumetric heat source. Their translational motion through the part was modelled by a moving mesh approach. An additional remeshing condition and helper lines were used to avoid highly distorted elements. The positions of the elements of the polygonal mesh were calculated with the Laplace’s smoothing approach. Good correlation between the numerically calculated and the experimentally observed weld bead shapes and transient temperature distributions was found.
Hydrogen-assisted cracking is a critical combination of local microstructure, mechanical load and hydrogen concentration. Welded microstructures of low-alloyed creep-resistant Cr-Mo-V steels show different hydrogen trapping kinetics. This influences the adsorbed hydrogen concentration as well as the diffusion by moderate or strong trapping. A common approach to describe hydrogen traps is by their activation energy that is necessary to release hydrogen from the trap. In the present study, Cr-Mo-V steel T24 (7CrMoVTiB10-10) base material and TIG weld metal were investigated. Electrochemically hydrogen charged specimens
were analyzed by thermal desorption analysis (TDA) with different linear heating rates. The results show two different effects. At first, the microstructure effect on trapping is evident in terms of higher hydrogen concentrations in the weld metal and increased activation energy for hydrogen release. Secondly, it is necessary to monitor the real specimen temperature. A comparison between the adjusted heating rate and the real specimen temperature shows that the calculated activation energy varies by factor two. Thus, the trap character in case of the base material changes to irreversible at decreased temperature. Hence, the effect of the experimental procedure must be considered as well if evaluating TDA results. Finally, realistic temperature assessment is mandatory for calculation of activation energy via TDA.
One of the main factors affecting the use of lasers in the industry for welding thick structures is the process accompanying solidification cracks. These cracks mostly occurring along the welding direction in the welding center, and strongly affect the safety of the welded components. In the present study, to obtain a better understanding of the relation between the weld pool geometry, the stress distribution and the solidification cracking, a three-dimensional computational fluid dynamic (CFD) model was combined with a thermo-mechanical model. The CFD model was employed to analyze the flow of the molten metal in the weld pool during the laser beam welding process. The weld pool geometry estimated from the CFD model was used as a heat source in the thermal model to calculate the temperature field and the stress development and distributions. The CFD results showed a bulging region in the middle depth of the weld and two narrowing areas separating the bulging region from the top and bottom surface. The thermo-mechanical simulations showed a concentration of tension stresses, transversally and vertically, directly after the solidification during cooling in the region of the solidification cracking.
An approach to develop an arc sensor for gap width estimation during automated NG-GMAW with a weaving electrode motion is introduced by combining arc sensor readings with optical measurements of the groove shape to allow precise analyses of the process. The two test specimen welded for this study were designed to feature a variable groove geometry in order to maximize efficiency of the conducted experimental efforts, resulting in 1696 individual weaving cycle records with associated arc sensor measurements, process parameters and groove shape information. Gap width was varied from 18 mm to 25 mm and wire feed rates in the range of 9 m/min to 13 m/min were used in the course of this study. Artificial neural networks were applied as a modelling tool to derive an arc sensor for estimation of gap width suitable for online process control that can adapt to changes in process parameters as well as changes in the weaving motion of the electrode. Wire feed rate, weaving current, sidewall dwell currents and angles were defined as inputs to calculate the gap width. The evaluation of the proposed arc sensor model shows very good estimation capabilities for parameters sufficiently covered during the experiments.
In recent years, laser beam welding has found wide applications in many industrial fields. Solidification cracks are one of the most frequently encountered welding defects that hinder obtaining a safe weld joint. Decades of research have shown that one of the main causes of such cracks are the strain and the strain rate. Obtaining meaningful measurements of these strains has always been a major challenge for scientists, because of the specific environment of the measurement range and the many obstacles, as well as the high temperature and the plasma plume. In this study, a special experimental setup with a high-speed camera was employed to measure the strain during the welding process. The hot cracking susceptibility was investigated for 1.4301 stainless steel, and the critical strain required for solidification crack formation was locally and globally determined.
Laser metal deposition (LMD) has been applied as a coating technology for many years. Today, the technologies capacity to produce 3D depositions leads to a new field of application as additive manufacturing method. In this paper, 3D laser metal deposition of titanium alloy Ti-6Al-4V is studied with special regard to the demands of additive manufacturing. Therefore, only the coaxial LMD powder nozzle is used to create the shielding gas atmosphere, which ensures high geometric flexibility. Furthermore, specimen with high aspect ratio and hundreds of layers are manufactured, which represent typical features in additive manufacturing. The presented study contains the following steps: First, cylindrical specimens are manufactured with a standard shell-core build-up strategy and mechanical properties as well as fracture mechanisms are determined. Based on the results, experiments are conducted to improve the build-up strategy and new tensile test specimens are built with the improved strategy. The improved strategy incorporates variable track overlap ratios to achieve a constant growth in the shell and core area. As blanks, lean cylinders comprising more than 240 layers and a height of more than 120mm are manufactured. The specimens are analyzed by X-ray inspection for material defects. Fractured surfaces are observed via scanning electron microscopy and the composition of the surfaces is determined using energy dispersive X-ray spectroscopy. The tensile test results prove mechanical properties close to ASTM F1108 specification for wrought material.
The phase transformation under various cooling rates and in different HAZ regions for high-strength armour steel was analysed by dilatometry. To develop a continuous cooling transformation (CCT) diagram, the samples were heated up to a peak temperature of 1250 °C to achieve a coarse-grained microstructure and then cooled down with a cooling time t 8/5 varying from 3 to 240 s. Analysis of dilatation curves revealed the austenite decomposition process, during which transformation temperatures were determined. The results showed martensitic transformations for all welding-relevant cooling times. Furthermore, to analyse different heat-affected subzones of the weld, the peak temperature was varied between 550 and 1250 °C at a constant cooling time t 8/5 of 6 s. The simulated coarse-grained heat-affected zone (CGHAZ) and fine-grained-heat affected zone (FGHAZ) showed only martensitic transformations with transformation temperatures below 400 °C. The steel exhibited an inhomogeneous hardness with hardening in the CGHAZ and FGHAZ and softening in the intercritical and subcritical HAZ. The physically simulated microstructure was validated by a real hybrid laser-arc weld microstructure.
Low heat input gas metal arc welding for dissimilar metal weld overlays part II: the transition zone
(2018)
Dissimilar metal weld overlays (DMWOL) of nickel base alloys on low alloy steel components are commonly used in the oil and gas, petrochemical, and power generation industries to provide corrosion and oxidation resistance in a wide range of service environments and temperatures. Traditionally, dissimilar weld overlays are produced using cold or hot wire gas tungsten arc welding. This study aims to identify and evaluate potential advantages of low heat input gas metal arc welding processes over the conventional gas tungsten arc welding in the production of dissimilar weld overlays. In order to evaluate the quality of these overlays regarding resistance against hydrogen-assisted cracking, their transition zone region is investigated in this part of the publication series. Metallurgical characterization, including energy-dispersive x-ray spectroscopy, is performed on Alloy 625/grade 22 steel overlays. The transition zone is characterized by a narrow planar growth zone and steep compositional gradients from the fusion boundary towards the weld metal. Evidence of low carbon contents in the planar growth zone, as well as for carbide precipitation in the cellular growth zone was found. The microstructure in the transition zone region of the fusion zone shows characteristics known to be suitable for good resistance against hydrogen embrittlement.
The analytical potential of a nanosecond laser ablation inductively coupled plasma mass spectrometer (ns-LA-ICP-SFMS) system, equipped with an ultra-fast wash-out ablation chamber, is critically investigated for fast and highly spatially resolved (∼μm) qualitative elemental distribution within single cells. Initially, a low surface roughness (< 10 nm) thin In–SnO2 layer (total coating thickness ∼200 nm) deposited on glass is employed to investigate the size, morphology and overlapping of laser-induced craters obtained at different laser repetition rates, making use of Atomic Force Microscopy (AFM). Conical craters with a surface diameter of about 2 µm and depths of about 100 nm were measured after a single laser shot. Furthermore, the influence of the sampling distance (i.e. distance between the sample surface and the inner sniffer of the ablation chamber) on the LA-ICP-MS ion signal wash-out time is evaluated. A significant decrease of the transient 120Sn+ ion signal is noticed after slight variations (±200 μm) around the optimum sampling position. Ultra-fast wash-outs (< 10 ms) are achieved reducing the aerosol mixing from consecutive laser shots even when operating the laser at high repetition rates (25 – 100 Hz). Fast and highly spatially resolved images of elemental distribution within mouse embryonic fibroblast cells (NIH/3T3 fibroblast cells) and human cervical carcinoma cells (HeLa cells), incubated with gold nanoparticles (Au NPs) and Cd-based quantum dots (QDs), respectively, are determined at the optimized operating conditions. Elemental distribution of Au and Cd in single cells is achieved using a high scanning speed (50 µm/s) and high repetition rate (100 Hz). The results obtained for the distribution of fluorescent Cd-based QDs within the HeLa cells are in good agreement with those obtained by confocal microscopy. The size, morphology and overlapping of laser-induced craters in the fixed cells are also investigated using AFM, observing conical craters with a surface diameter of about 2.5 µm and depths of about 800 nm after a single laser shot.
Laser metal deposition (LMD) is an established technology for two-dimensional surface coatings. It offers high deposition rates, high material flexibility, and the possibility to deposit material on existing components. Due to these features, LMD has been increasingly applied for additive manufacturing of 3D structures in recent years. Compared to previous coating applications, additive manufacturing of 3D structures leads to new challenges regarding LMD process knowledge. In this paper, the process steps for LMD as additive manufacturing technology are described. The experiments are conducted using titanium alloy Ti-6Al-4Vand Inconel 718. Only the LMD nozzle is used to create a shielding gas atmosphere. This ensures the high geometric flexibility needed for additive manufacturing, although issues with the restricted size and quality of the shielding gas atmosphere arise. In the first step, the influence of process parameters on the geometric dimensions of single weld beads is analyzed based on design of experiments. In the second step, a 3D build-up strategy for cylindrical specimen with high dimensional accuracy is described. Process parameters, travel paths, and cooling periods between layers are adjusted. Tensile tests show that mechanical properties in the as-deposited condition are close to wrought material. As practical example, the fir-tree root profile of a turbine blade is manufactured. The feasibility of LMD as additive technology is evaluated based on this component.
Laser texturing is an emerging technology for generating surface functionalities on basis of optical, mechanical, or chemical properties. Taking benefit of laser sources with ultrashort (fs) pulse durations features outstanding precision of machining and negligible rims or burrs surrounding the laser-irradiation zone. Consequently, additional mechanical or chemical post-processing steps are usually not required for fs-laser surface texturing (fs-LST). This work aimed to provide a bridge between research in the field of tribology and laser materials processing. The paper reviews the current state-of-the-art in fs-LST, with a focus on the tribological performance (friction and wear) of specific self-organized surface structures (so-called ripples, grooves, and spikes) on steel and titanium alloys. On the titanium alloy, specific sickle-shaped hybrid micro-nanostructures were also observed and tribologically tested. Care is taken to identify accompanying effects affecting the materials hardness, superficial oxidation, nano- and microscale topographies, and the role of additives contained in lubricants, such as commercial engine oil.
Three high-strength Nb-,.Ti- and Ti+ V-bearing S690QL steels were welded to investigate and compare the effects of microalloy addition on heat-affected zone (HAZ) toughness. Charpy V notch impact tests from three microalloyed welds under different cooling rates have been performed. Fractographic examination shows that several factors, including large-sized grain, upper bainite or hard second phase, interact to determine brittle fracture and impaired toughness in Nb-bearing weld with high heat input. In contrast to this reduced toughness, Ti-bearing welds exhibits satisfied toughness regardless of at fast or slow cooling. This is attributed to its limited austenite grain and refines favorable intragranular acicular ferrite structure. Moreover, in the case of such refined structure as matrix, TiN particles are found to be irrelevant to the facture process. The crystallographic results also confirm that high-angle boundaries between fine ferrites plates provide effective barriers for crack propagation and contribute to improved toughness.
The influence of the support structure on residual stress and distortion in SLM Inconel 718 parts
(2018)
The effect of support structure and of removal from the base plate on the residual stress state in selective laser melted IN718 parts was studied by means of synchrotron X-ray diffraction. The residual stresses in subsurface region of two elongated prisms in as-built condition and after removal from the base plate were determined. One sample was directly built on a base plate and another one on a support structure. Also, the distortion on the top surface due to stress release was measured by contact profilometry. High tensile residual stress values were found, with pronounced stress gradient along the hatching direction. In the sample on support, stress redistribution took place after removal from the base plate, as opposed to simple stress relaxation for the sample without support. The sample on support structure showed larger distortion compared to sample without support. We conclude that the use of a support decreases stress values but stress-relieving heat treatments are still needed.
The effects of weathering exposure on unfilled and filled thermoplastic polyurethanes (TPU) materials are described as performed under different humidity conditions. For this purpose, a weathering device was used with UV-A 340 nm lamps at a constant temperature of 40 °C. The effects of environmental (UV and humidity condition) degradation on the frictional properties of TPU materials are presented along with surface analyses to characterize the chemistry of the degradative process. Photooxidative degradation of unfilled polymer leads to deterioration of physical and mechanical properties, which affects its tribological behavior significantly. Due to crosslinking, the stiffness of the material increases, reducing drastically the friction coefficient of unfilled TPUs. The frictional behavior of glass fiber reinforced TPU is less affected by radiation.
Foreword
(2018)
The subject of this Special Issue is the fracture mechanics-based determination of the fatigue strength of weldments. Except for one, all papers were written in closer or wider relation to a methodology developed within the framework of the German Project cluster IBESS. Some of them provide background or supplementary information needed in that context but which is also relevant in a wider frame of research activities. The acronym IBESS stands for the topic of this Special Issue (in German: „Integrale Methode zu Bruchmechanischen Ermittlung der Schwingfestigkeit von Schweißverbindungen). Eight partners were involved. The cluster was cooperatively founded by the German Research Foundation (Deutsche Forschungsgemeinschaft) and by the German AiF Network (Arbeitsgemeinschaft industrieller Forschungsvereinigungen) for industrial research.
A laser-induced breakdown spectroscopy (LIBS) system was combined with a bead-on-plate Tungsten Inert Gas (TIG) welding process for the in situ measurement of chemical compositions in austenitic stainless steels during welding.Monitoring the weld pool's chemical composition allows governing the weld pool solidification behavior, and thus enables the reduction of susceptibility to weld defects. Conventional inspection methods for weld seams (e.g. ultrasonic inspection) cannot be performed during the welding process. The analysis system also allows in situ study of the correlation between the occurrence ofweld defects and changes in the chemical composition in theweld pool or in the two-phase regionwhere solid and liquid phase coexist. First experiments showed that both the shielding Ar gas and the welding arc plasma have a significant effect on the selected Cr II, Ni II and MnII characteristicemissions, namely an artificial increase of intensity values via unspecific emission in the spectra.
In situ investigations showed that this artificial intensity increase reached a maximum in presence of weld plume. Moreover, an explicit decay has been observedwith the termination of thewelding plumedue to infrared radiation during sample cooling. Furthermore, LIBS can be used after welding to map element distribution. For austenitic stainless steels,Mnaccumulations on both sides of theweld could be detected between the heat affected zone (HAZ) and the base material.
Distortions in Additive Manufacturing (AM) Laser Metal Deposition (LMD) occur in the newly-built component due to rapid heating and solidification and can lead to shape deviations and cracking. This paper presents a novel approach to quantify the distortions experimentally and to use the results in numerical simulation validation. Digital Image Correlation (DIC) is applied together with optical filters to measure in-situ distortions directly on a wall geometry produced with LMD. The wall shows cyclic Expansion and shrinking with the edges bending inward and the top of the sample exhibiting a slight u-shape as residual distortions. Subsequently, a structural Finite Element Analysis (FEA) of the experiment is established, calibrated against experimental temperature profiles and used to predict the in-situ distortions of the sample. A comparison of the experimental and numerical results reveals a good agreement in length direction of the sample and quantitative deviations in height direction, which are attributed to the material model used. The suitability of the novel experimental approach for measurements on an AM sample is shown and the potential for the validated numerical model as a predictive tool to reduce trial-and-error and improve part quality is evaluated.
Build-up strategies for temperature control using laser metal deposition for additive manufacturing
(2018)
The track geometry created with laser metal deposition (LMD) is influenced by various parameters. In this case, the laser power has an influence on the width of the track because of an increasing energy input. A larger melt pool is caused by a rising temperature. In the case of a longer welding process, there is also a rise in temperature, resulting in a change of the track geometry. This paper deals with the temperature profiles of different zigzag strategies and spiral strategies for additive manufacturing. A two-color pyrometer is used for temperature measurement on the component surface near the melt pool. Thermocouples measure the temperatures in deeper regions of a component. The welds are located in the center and in the edge area on a test part to investigate the temperature evolution under different boundary conditions. The experiments are carried out on substrates made from mild steel 1.0038 and with the filler material 316L. The investigations show an influence on the temperature evolution by the travel path strategy as well as the position on the part. This shows the necessity for the development and selection of build-up strategies for different part geometries in additive manufacturing by LMD.
Giant magneto-resistive (GMR) sensor based metal magnetic memory (MMM) technique is proposed for mapping of deformation-induced self-magnetic leakage fields (SMLFs) in carbon steel. The specimens were subjected to different amounts of tensile deformation and the deformation-induced SMLFs were measured using a GMR sensor after unloading the specimens. 3D-nonlinear finite element modeling was performed to predict stress–strain state in a steel specimen under tensile load. The experimentally obtained SMLF images were correlated with the finite element model predicted stress–strain states. Studies reveal that the MMM technique can detect the plastic deformation with signal-to-noise ratio better than 20 dB. The technique enables the mapping of plastic deformation in carbon steels for the evaluation of the severity of deformation. The study also reveals that deformation-induced SMLF is influenced by the presence of initial surface residual stress, introduced by shot peening. The intensity of SMLF signal is found to increase with increase in tensile load and decrease with shot peening.
Residual stresses are crucial when assessing the performance of welded components. The present work deals with the possibilities of transferring the real-life boundary conditions of welding, which influence the residual stress, into the laboratory. The possibilities of a test system specifically developed for this purpose with a maximum capacity of 2 MN are shown. Due to the structural design, global process, geometry and material-dependent stresses are induced, which can be simulated and quantified within the system. Additionally, X-ray diffraction can be applied to determine the resulting local residual stress distribution precisely with high spatial resolution. Two examples are presented how the conditions to be found during production are simulated in the laboratory. It is shown how welding residual stresses in high-strength steels are affected by the heat control. It was possible to clarify why elevated working temperatures significantly increase the bending stresses in the welded joint and therefore the tensile residual stresses in the heat affected zone (HAZ). The effect of a heat treatment applied under mechanical stress resulting from welding is demonstrated by the example of a creep resistant steel. Reheat cracking is significantly increased in this case compared to small scale laboratory based tests.
The development within the offshore wind energy sector towards more powerful turbines combined with increasing water depth for new wind parks is challenging both, the designer as well as the manufacturer of support structures. Besides XL-monopiles the jacket support structure is a reasonable alternative due to the high rigidity combined with low material consumption. However, the effort for manufacturing of the hollow section joints reduces the economic potential of jacket structures significantly. Therefore, a changeover from an individual towards a serial production based on automated manufactured tubular joints combined with standardized pipes must be achieved. Hence, this paper addresses the welding process chain of automated manufactured tubular joints including digitization of the relevant manufacturing parameters such as laser scanning of the weld seam geometry. Additionally, a methodology for the computation of the notch radius as well as the weld seam angle is presented based on the scanned profiles of three analysis points of an automated manufactured tubular X-joint. Subsequently, these parameters are considered within the notch stress approach based fatigue design and their impact is quantified by a comparison with the structural stress approach using equivalent stress concentration factors.
Today, an expanding application of high-strength steels in modern welded constructions can be observed. The economical use of these steel grades largely depends on the strength and reliability of the weldments. Therefore, the special microstructure and mechanical properties of these grades have to be taken into account by keener working ranges regarding the welding parameters.
However, performance and safety of welded components are strongly affected by the stresses occurring during and after welding fabrication locally in the weld seam and globally in the whole component, especially if the shrinkage and distortion due to welding are restrained. Some extensive studies describe the optimization of the welding stresses and the metallurgical effects regarding an adapted welding heat control. Lower working temperatures revealed to be particularly effective to reduce the local and global welding-induced residual stresses of the complete weld significantly. However, decreased interpass temperatures cause concurrently higher stresses during welding fabrication. This work shows strategies to reduce these in-process stresses.
With help of multi-axial welding stress analyses in component-related weld tests, using a special 2-MN-testing facility, differences in stress build-up are described in detail for root welds, filler layers and subsequent cooling to ambient temperature.
The performance and safety of welded high-strength low-alloyed steel (HSLA) components are substantially affected by the stresses occurring during and after welding fabrication, especially if welding shrinkage and distortion are severely restrained. The surrounding structure of the whole component affects loads in the far-field superimposing with welding stresses in the near-field of the weld. In this study a unique testing facility was used to restrain shrinkage and bending while analyse multiaxial far-field loads (max. 2 MN) during assembly of thick-walled component. A novel approach for the assessment of the in-situ-measured far-field data in combination with the actual weld geometry was elaborated. For the first time, analyses of the global bending moments of restrained welds based on the neutral axis of the actual weld load bearing section were achieved. Hence, far-field measurements offered the possibility to determine critical near-field stresses of the weld crosssections for the entire joining process. This work presents the approach for far-to-near field in-situ determination of stresses in detail for the 2-MN-testing system based on an extensive experimental work on HSLA steel welds, which demonstrates sources and consequences of these high local welding stresses. Thus, it was clarified, why the first weld beads are crucial regarding welding stresses and cold cracking, which is well known, but has never been measured so far. Accompanying analyses using X-ray diffraction (XRD) after welding show effects on local residual stress distributions. These analyses indicated viable prospects for stress reduction during assembly of thick-walled HSLA steel components.
Pores in additive manufactured metal parts occur due to different reasons and affect the part Quality negatively. Few investigations on the origins of porosity are available, especially for Ni-based super alloys. This paper presents a new study to examine the influence of common processing Parameters on the Formation of pores in parts built by laser metal Deposition using Inconel 718 powder. Further, a comparison between the computed tomography (CT) and the Archimedes method was made. The Investigation Shows that CT is able to identify different kinds of pores and to give further Information about their distribution. The identification of some pores as well as their shape can be dependent on the Parameter Setting of the Analysis tool. Due to limited measurement Resolution, CT is not able to identify correctly pores with Diameters smaller than 0.1 mm, which leads to a false decrease on Overall porosity. The applied Archimedes method is unable to differentiate between gas porosity and other Kinds of holes like internal cracks or lack of Fusion, but it delivered a proper value for Overall porosity. The method was able to provide suitable data for the statistical Evaluation with design of Experiments, which revealed significant Parameters ont he Formation of pores in LMD.
With the recent rise in the demand for additive manufacturing (AM), the need for reliable simulation tools to support experimental efforts grows steadily. Computational welding mechanics approaches can simulate the AM processes but are generally not validated for AM-specific effects originating from multiple heating and cooling cycles. To increase confidence in the outcomes and to use numerical simulation reliably, the result quality Needs to be validated against experiments for in-situ and post-process cases. In this article, a validation is demonstrated
for a structural thermomechanical simulation model on an arbitrarily curved Directed Energy Deposition (DED)part: at first, the validity of the heat input is ensured and subsequently, the model’s predictive quality for in-situ
deformation and the bulging behaviour is investigated. For the in-situ deformations, 3D-Digital Image Correlation measurements are conducted that quantify periodic expansion and shrinkage as they occur. The results show a strong dependency of the local stiffness of the surrounding geometry. The numerical Simulation model is set up in accordance with the experiment and can reproduce the measured 3-dimensional in-situ displacements. Furthermore, the deformations due to removal from the substrate are quantified via 3D-scanning, exhibiting considerable distortions due to stress relaxation. Finally, the prediction of the deformed shape is discussed in regards to bulging simulation: to improve the accuracy of the calculated final shape, a novel Extension of the model relying on the modified stiffness of inactive upper layers is proposed and the experimentally observed bulging could be reproduced in the finite element model.
The paper describes an experimental investigation of the electromagnetic porosity reduction in partial penetration laser beam welding of 6 mm thick aluminum die casting AlSi9MnMg. The Investigation reveals that the usage of an electromagnetic field leads to a significant reduction of the porosity as well as to a surface smoothing of aluminum die casting. Based on the reference case without an electromagnetic influence, the porosity area was reduced gradually up to 76%.
Metallurgical pores as well as process pores were removed from the weld pool. Also the weld reinforcement was improved up to 78%. Best results were reached with a frequency of 4325 Hz and a magnetic flux density of 348 mT. Although a complete prevention of porosity was not achieved, the best weld seam reached a high quality and can be ranked in valuation group B of DIN EN ISO 13919-2:2001–12.
Additive Manufacturing (AM) through the Selective Laser Melting (SLM) route offers ample scope for producing geometrically complex parts compared to the conventional subtractive manufacturing strategies. Nevertheless, the residual stresses which develop during the fabrication can limit application of the SLM components by reducing the load bearing capacity and by inducing unwanted distortion, depending on the boundary conditions specified during manufacturing. The present study aims at characterizing the residual stress states in the SLM parts using different diffraction methods. The material used is the nickel based superalloy Inconel 718. Microstructure as well as the surface and bulk residual stresses were characterized. For the residual stress analysis, X-ray, synchrotron and neutron diffraction methods were used. The measurements were performed at BAM, at the EDDI beamline of -BESSY II synchrotronand the E3 line -BER II neutron reactor- of the Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. The results reveal significant differences in the residual stress states for the different characterization techniques employed, which indicates the dependence of the residual state on the penetration depth in the sample. For the surface residual stresses, longitudinal and transverse stress components from X-ray and synchrotron agree well and the obtained values were around the yield strength of the material. Furthermore, synchrotron mapping disclosed gradients along the width and length of the sample for the longitudinal and transverse stress components. On the other hand, lower residual stresses were found in the bulk of the material measured using neutron diffraction. The longitudinal component was tensile and decreased towards the boundary of the sample. In contrast, the normal component was nearly constant and compressive in nature. The transversal component was almost negligible. The results indicate that a stress re-distribution takes place during the deposition of the consecutive layers. Further investigations are planned to study the phenomenon in detail.
Submerged arc welded (SAW) components of creep-resistant low-alloyed Cr-Mo-V steels are used for thick-walled heavy petrochemical reactors (wall-thickness up to 475 mm) as well as employed in construction of modern high-efficient fossil fired power plants. These large components are accompanied by significant restraints during welding fabrication, especially at positions of different thicknesses like welding of nozzles. As a result, residual stresses occur, playing a domi-nant role concerning so-called stress relief cracking (SRC) typically during post weld heat treat-ment (PWHT). Besides specific metallurgical factors (like secondary hardening due to re-precipitation), high tensile residual stresses are a considerable influence factor on SRC. For the assessment of SRC susceptibility of certain materials mostly mechanical tests are applied which are isolated from the welding process. Conclusions regarding the influence of mechanical factors are rare so far. The present research follows an approach to reproduce loads, which occur during welding of real thick-walled components scaled to laboratory conditions by using tests designed on different measures. A large-scale slit specimen giving a high restraint in 3 dimensions by high stiffness was compared to a medium-scale multi-pass welding U-profile specimen showing a high degree of restraint in longitudinal direction and a small-scale TIG-re-melted specimen. The small-scale specimens were additionally subjected to mechanical bending to induce loads that are found during fabrication on the real-scale in heavy components. Results show for all three cases compa-rable high tensile residual stresses up to yield strength with high gradients in the weld metal and the heat affected zone. Those high tensile stresses can be significant for cracking during further PWHT.
The sound numerical prediction of welding-induced thermal stresses, residual stresses, and distortions strongly depends on the accurate description of a welded material’s thermomechanical deformation behaviour. In this work, we provide experimental data on the viscoplastic deformation behaviour of a grade-s960ql steel up to a temperature of 1000 ◦C. In addition, a multi-phase viscoplastic material model is proposed, which accounts for the experimentally observed isothermal deformation behaviour of grade-s960ql steel base and austenitised material, as well as for athermal contributions that originate from solid-state phase transformations. The multi-phase viscoplastic and a classic rateindependent isotropic hardening material model were applied in the numerical simulations of both-ends-fixed bar Satoh tests and a single-pass gas metal arc weld. The influence of material modelling choices on the agreement between numerical simulation and experimental results is discussed, and recommendations for further work are given.
Compared to conventional welding consumables using low transformation temperature (LTT) filler materials is an innovative method to mitigate tensile residual stresses due to delayed martensite transformation of the weld. For the effective usage of LTT filler materials, a deeper understanding of the complex processes that lead to the final residual stress state during multipass welding is necessary. Transformation kinetics and the strain evolution of multi-pass welds during welding were investigated in situ at the beamline HEMS@PETRAIII, Germany. Compared to conventional welds, the total strain was reduced and compression strain was achieved when using LTT filler materials. For an optimal use of the LTT effect in the root of multi-pass welds, the alloying concept must be adapted taking care of dilution.
The work presents the procedure developed within the German research project IBESS, which allows for the fracture mechanics-based prediction of the fatigue strength of welded joints under constant amplitude loading. Based on the experimental observations of the crucial failure mechanisms, the approach focuses on the short crack propagation, where elastic-plastic fracture mechanics and the build-up of closure effects must be considered as well as the variability of the local geometry at the weld toe and the modelling of multiple crack interaction. Analytical solutions are provided for the approximation of the through-thickness stress profiles at the weld toe and for the determination of the crack driving force in the form of a plasticity-corrected stress intensity factor range ∆K_p. Proposals for the determination of the initial crack size and the crack closure factor are also included.
The approach is validated against a large number of experimental data, which comprises fatigue tests on individual cracks monitored by heat tinting and beach-marking techniques, as well as stress life curves. Three kinds of welded joints, two steels of significant different strengths and three stress ratios are considered. The results show that the procedure provides good estimations of the statistical distribution of the fatigue strength of welded joints both for the finite and infinite life regime. Furthermore, the predictions are compared with available benchmark data for structural steels.
Any fracture mechanics based determination of the fatigue strength of weldments requires different input information such as the local weld geometry and material data of the areas the crack is passing through during its propagation. The latter is so far not a trivial task as the fatigue crack is usually initiated at the weld toe at the transition from the weld metal to the heat affected zone and it subsequently propagates through the different microstructures of the latter to eventually grow into the base material and to cause final fracture. This paper describes how the material input information has gained particularly for heat affected zone material by thermo-mechanically simulated material specimens for two steels of quite different static strength. The data comprise the cyclic stress-strain curve, the crack closure effect-corrected crack growth characteristics, long crack fatigue crack propagation thresholds, the dependency of the parameter on the crack length and monotonic fracture resistance. The substantial experimental effort was necessary for the validation exercises of the IBESS approach, however, within the scope of practical application more easily applicable estimating methods are required. For that purpose the paper provides a number of appropriate proposals in line with its check against the reference data from the elaborate analyses.
The so-called cyclic R curve, i.e. the crack size dependence of the fatigue crack propagation threshold in the physically short crack regime, is a key parameter for bringing together fatigue strength and fracture mechanics concepts. Its adequate determination is of paramount importance. However, notwithstanding this relevance, no test guideline is available by now and only very few institutions have spent research effort on cyclic R curves so far. The aim of the present paper is to give an overview on the state-of-the-art. Besides an introduction into the basic principles, the discussion will concentrate on the experimental determination on the one hand and questions of its application on the other hand.
The cyclic J-integral (∆J-integral) is a crack tip parameter of elastic-plastic fracture mechanics which can be used as governing parameter for the description of fatigue crack growth (FCG) in metallic structures. In this contribution, it is applied for modelling FCG in weldments. The ∆J-integral is determined by means of analytical approximation formulas as well as numerical methods. An analytical solution, which takes into account effects of the local ligament plasticity, was derived. This solution is based on well established methods such as R6, BS7910 and SINTAP which were modified for cyclic loading. It incorporates methods for the description of short crack closure behaviour as well as the well known analytical (long) crack closure function of Newman. A specific code was written to evaluate the ∆J-integral numerically in the course of finite element based crack growth simulations. The code was first validated for an infinite plate with centre crack by applying elastic and elastic-plastic material behaviour. Next, the ∆J-integral was calculated for cracks in various butt and cruciform welded joints. The results were compared with the results of the derived analytical approximation formula. A good accordance was achieved between the results.
The paper provides an application of the IBESS approach to the investigation of the influence of various parameters of the global and local weld geometry as well as material defects on the fatigue strength of weldments. For this purpose, the global weld parameters, such as the weld toe radius, the flank angle, the excess weld metal, local secondary notches (in the present study as a measure of surface imperfections) and inclusions sizes have been determined as statistical distributions for different joint types and geometries and two steels of different strengths. The results are in line with literature data and reveal the potential of the theoretical approach to predict the correct trends. The combination with an advanced weld quality system has been demonstrated to be possible.
The interaction of hydrogen with various tungsten-inert-gas-welded austenitic stainless steels’ (AUSS) microstructure is studied by means of desorption/absorption analysis and microstructure observations. One of the limitations of welding is created by the presence of hydrogen in the weld, which can shorten the steel’s service life. The local hydrogen concentration, trapping, and its distribution along the welded samples were studied by thermal desorption spectrometry and were supported by X-ray diffraction (XRD) and electronic microstructural observations. Hydrogen content demonstrated a dependence on the welding zone. It was found that hydrogen distribution, and accepted microstructure during welding, played a significant role in the trapping mechanism of 316L AUSS. XRD analysis revealed residual stresses which were caused due to the presence of hydrogen in c-phase. It was shown that the austenite microconstituents inside 316L can have a crucial effect in preventing hydrogen-assisted cracking phenomenon. The effects of AUSS microstructure on hydrogen absorption and desorption behavior are discussed in detail.
Hybrid laser-arc welding of thick-walled ferromagnetic steels with electromagnetic weld pool support
(2018)
The hybrid laser-arc welding (HLAW) process provides many advantages over laser welding and arc welding alone, such as high welding speed, gap bridgeability, and deep penetration. The developments in hybrid laser-arc welding technology using modern high-power lasers allow single-pass welding of thick materials. This technology can be used for the heavy metal industries such as shipbuilding, power plant fabrication, and line-pipe manufacturing. The obvious problem for single-pass welding is the growth of the hydrostatic pressure with increasing thickness of materials leading to drop-out of molten metal. This phenomenon is aggravated at slow welding velocities because of increasing weld seam width followed by a decrease of Laplace pressure compensating the hydrostatic pressure. Therefore, weld pool support is necessary by welding of thick materials with slow welding velocities. The innovative electromagnetic weld pool support system is contactless and has been used successfully for laser beam welding of aluminum alloys and austenitic and ferromagnetic steels. The support system is based on generating Lorentz forces within the weld pool. These are produced by an oscillating magnetic field orientated perpendicular to the welding direction. The electromagnetic weld pool support facilitates a decrease in the welding speed without a sagging and drop-out of the melt thus eliminating the limitations of weldable material thickness.
Welding residual stresses have an impact on the performance of welded structures, on their fracture resistance, their resistance against fatigue crack propagation and, most important, their fatigue strength and fatigue lifetime. The present paper provides an overview on the issue mainly from the point of view of the application of fracture mechanics to the determination of the fatigue strength as the topic of this Special issue. Besides own experimental and theoretical data a comprehensive discussion is provided in that context which includes the definition and interaction of short- and long-range (or reaction) residual stresses, the effect of cyclic mechanical loading and its treatment in fracture and fatigue analyses.
Common fracture mechanics based fatigue considerations are usually limited to the residual lifetime determination of so-called long cracks. The extension of this concept to the total lifetime, as in the S-N curve approach, requires an adequate description of short crack propagation which cannot be based on the Delta K concept, and it must consider the crack closure phenomenon as well as its gradual build-up at the short crack stage. Further, it has to provide a meaningful definition of initial crack dimensions and a solution for the multiple crack problem at stress levels higher than the fatigue limit as it is specific for some configurations such as weldments. This paper aims at a discussion of all these points and offers possible solutions which are illustrated by examples taken from the German IBESS project on fracture mechanics based determination of the fatigue strength of weldments, the results of which will be discussed in more detail in this Special issue.
Laser beam oscillation, applied one- or two-dimensional to the actual welding process, influences the welding process in terms of compensation of tolerances and reduction of process emissions like spatter and melt ejections that occur in industrial applications, such as in body-in-white manufacturing. If the welding process could be adapted to these tolerances by the momentarily demanded melt pool width to generate sufficient melt volume or to influence melt pool dynamics, e.g. for a better degassing, laser welding would become more robust. However, beam oscillation results are highly dependent on the natural frequency of the melt pool, the used spot diameter and the oscillation speed of the laser beam. The conducted investigations with an oscillated 300 μm laser spot show that oscillation strategies which are adjusted to the joining situation can bridge gaps to approximately 0.6 mm at metal sheet thickness of 0.8 mm. However, the complex behaviour of the melt pool has to be considered to generate proper welding results. This work puts emphasis on showing aspects of beam oscillation in fillet welding in lap joints.
Modern advanced high-strength steel sheets for automotive applications are mostly zinc coated for corrosion resistance. However, the presence of zinc can—besides its positive effects—increase the material’s susceptibility to liquid metal embrittlement (LME) during resistance spot welding (RSW). Zinc and its eutectics are, due to their low melting point, present in liquid state during the welding process. This fact can, in combination with other factors like tensile strains or stresses, lead to the formation of brittle, intergranular cracks in the weld, and heat-affected zone. This phenomenon is commonly called liquid metal embrittlement. In order to understand the process from a practical perspective, one must learn what factors facilitate it. In this study, industry-relevant parameters are investigated regarding their influence on the occurrence of LME, embodied by the formation of surface cracks. It was found that electrode wear has less of an influence on the cracking susceptibility than welding current or tensile stresses. Finite element analysis is believed to provide a powerful tool in order to gain insights on the formation process. Modeling of the process shows promising initial results, revealing the underlying local stress and strain fields, unmeasurable with common techniques.
Comparison between GTA and laser beam welding of 9%Ni steel for critical cryogenic applications
(2018)
IncomparisonwithGTAweldedjoints,highertensilestrengthcomparabletothatofthebasemetalwasobtained for laser beam welded joints due to fine martensitic microstructure. Impact fracture toughness values with much lower mismatching were obtained for laser beam welded joints due to similarity in the microstructures of its weld metal and HAZ. In this case, the lower impact fracture toughness obtained (1.37J/mm2) was much higher than that of the GTA welded joints (0.78J/mm2), which was very close to the specified minimum value (≥0.75J/mm2). In contrast to other research works, the overall tensile and impact properties are influenced not only by the fusion zone microstructure but also by the size of its hardened area as well as the degree of its mechanical mismatching, as a function of the welding process. A better combination of tensile strength and impact toughness of the concerned steel welded joints is assured by autogenous laser beam welding process.
In order to generate a material data base for computational welding mechanics, temperature and strain-rate dependent stress-strain experiments were performed by using a Gleeble®3500 testing system. The object of the investigation was HSLA transformable steel S960QL and related solid phases as bainite, martensite and austenite. For the production of these solid phases, the base material was heat treated according to an average weld temperature cycle which was extracted within the heat affected zone of a thermal numerical weld simulation of a GMA weld. The hot tensile tests were carried out via cost-saving flat specimen geometries. Two experimental series with different strain-rates were conducted, where the longitudinal strain-rate was controlled by specification of the transversal strain-rate applying Poisson’s-ratio. Subsequently, the resulting stress-strain curves were approximated in accordance with the Ramberg-Osgood-materials law. Consequently, it is shown that the temperature and strain-rate dependent stress-strain behavior of metals can be successfully characterized by means of a Gleeble®-system.
However, this requires a control of the longitudinal strain-rate by specification of the transversal strain-rate. The related experimental procedure and the method of evaluation are explained in detail. With regard to all tested solid phases, a significant strain-rate dependency can only be observed upwards from temperatures of 400 °C. Based on experimental results, Ramberg-Osgood-parameters will be presented to describe the stress-strain behavior of steel S960QL and related solid phases for temperatures between 25 °C and 1200 °C. Furthermore, the use of costsaving flat specimen-geometry appears reasonable.
Two-dimensional residual stress mapping of multilayer LTT weld joints using the contour method
(2018)
Low transformation temperature (LTT) weld filler materials offer an attractive alternative to cost intensive postweld treatments as they can mitigate detrimental welding residual stresses during the welding process. Compared to conventional weld filler materials, LTT alloys are characterized by a delayed martensite transformation at low temperatures, which can result in compressive residual stresses in the weld. The high strength of these filler materials makes them potentially applicable to high-strength steels as well as for a large amount of requested repair works in steel structures. The focus of the study is on the confirmation of the LTT idea with regard to the residual stress state for multipass weld lines processed by metal active gas welding. It is demonstrated that the contour method is a well-suited technique for measuring the residual stress in the weld joint as it gives an entire two-dimensional map of the residual stress state in the weld line, heat affected zone (HAZ), and base material. The technique was applied at different LTT alloys with varying chemical compositions. Additionally, the results are compared to residual stress maps that were determined by Neutron diffraction using the Strain Analyzer for Large Scale Engineering Applications, an
instrument referred to as SALSA, at the Institut Laue-Langevin in Grenoble. For all investigated specimens, compressive residual stress distributions were determined in the area of the weld joint and the HAZ. They are balanced by tensile residual stresses in the surrounding base material. However, it is shown that the size of theregion exhibiting compressive residual stresses and the absolute values of the compressive residual stresses depend on the chemical composition of the weld filler material.
The residual stress distribution in IN718 elongated prisms produced by Selective Laser Melting was studied by means of neutron (bulk) and laboratory X-ray (surface) diffraction.
Two deposition hatch lengths were considered. A horizontal plane near the top surface (perpendicular to the building direction) and a vertical plane near the lateral surface (parallel to the building direction) were investigated. Samples both in as-built (AB) condition and removed (RE) from the base plate were characterized.
While surface stress fields seem constant for AB condition, X-ray diffraction shows stress gradients along the hatch direction in the RE condition. The stress profiles correlate with the distortion maps obtained by tactile probe measurements.
Neutron diffraction shows bulk stress gradients for all principal components along the main sample directions. We correlate the observed stress patterns with the hatch length, i.e. with its effect on temperature gradients and heat flow. The bulk stress gradients partially disappear after removal from the baseplate.
Influence of support configurations on the characteristics of selective laser-melted Inconel 718
(2018)
Samples fabricated using two different support configurations by following identical scan strategies during selective laser melting of superalloy Inconel 718 were characterized in this study. Characterization methods included optical microscopy, electron back-scattered diffraction and x-ray diffraction residual stress measurement. For the scan strategy considered, microstructure and residual stress development in the samples were influenced by the support structures. However, crystallographic texture intensity and the texture components formed within the core part of the samples were almost independent of the support. The formation of finer grains closer to the support as well as within the columnar grain boundaries resulted in randomization and texture intensity reduction by nearly half for the sample built on a lattice support. Heat transfer rates dictated by the support configurations in addition to the scan strategy influenced the microstructure and residual stress development in selective laser-melted Inconel 718 samples.
Due to the increasing global demand for pure silver, native wire silver aggregates in very high purities are gaining more industrial attention. Up to the present, no substantial metallurgical Investigation of natural wire silver exists in the accessible literature. To convey urgently needed cross-disciplinary fundamental knowledge for geoscientists and metallurgical engineers, twenty natural wire silver specimens from eight different ore deposits have been investigated in detail for the first time by EBSD (Electron Back Scattering Diffraction), supported by light microscopy and micro-probe analyses. The improved understanding of the natural silver wire microstructure provides additional Information regarding the growth of natural silver aggregates in comparison to undesired artificial growth on electronic devices. Clear evidence is provided that natural silver curls and hairs exhibit a polycrystalline face-centered cubic microstructure associated with significant twinning. Although the investigated natural wire silver samples have relatively high purity (Ag > 99.7 wt.-%), they contain a variety of trace elements such as, S, Cu, Mn, Ni, Zn, Co and Bi, As and Sb. Additionally, Vickers micro-hardness measurements are provided for the first time which revealed that natural silver wires and curls are softer than it might be expected from conversion of the general Mohs hardness of 2.7.
This study examines the relationship between the magnetic mesostructure with the microstructure of low carbon steel tungsten inert gas welds. Optical microscopy revealed variation in the microstructure of the parent material, in the heat affected and fusion zones, correlating with distinctive changes in the local magnetic stray fields measured with high spatial resolution giant magneto resistance sensors. In the vicinity of the heat affected zone high residual stresses were found using neutron diffraction.
Notably, the gradients of von Mises stress and triaxial magnetic stray field modulus follow the same tendency transverse to the weld. In contrast, micro-X-ray fluorescence characterization indicated that local changes in element composition had no independent effect on magnetic stray fields.
Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms.
During the energy transformation from fossil fuels to renewable energy sources, the use of hydrogen as fuel and energy storage can play a key role. This presents new challenges to industry and the scientific community alike. The storage and transport of hydrogen, which is nowadays mainly realized by austenitic stainless steels, remains problematic, which is due to the degradation of mechanical properties and the possibility of phase transformation by hydrogen diffusion and accumulation. The development of materials and technologies requires a fundamental understanding of these degradation processes. Therefore, studying the behavior of hydrogen in austenitic steel contributes to an understanding of the damage processes, which is crucial for both life assessment and safe use of components in industry and transportation. As one of the few tools that is capable of depicting the distribution of hydrogen in steels, time-of-flight secondary ion mass spectrometry was conducted after electrochemical charging. To obtain further information about the structural composition and cracking behavior, electron-backscattered diffraction and scanning electron microscopy were performed. Gathered data of chemical composition and topography were treated employing data fusion, thus creating a comprehensive portrait of hydrogen-induced effects in the austenite grade AISI 304L. Specimens were electrochemically charged with deuterium instead of hydrogen. This arises from the difficulties to distinguish between artificially charged hydrogen and traces existing in the material or the rest gas in the analysis chamber. Similar diffusion and permeation behavior, as well as solubility, allow nonetheless to draw conclusions from the experiments.
Automotive engine lubricants
(2019)
In 2003, ASTM Manual 37, Fuels and Lubricants Handbook: Technology, Properties, Performance and Testing, featured a chapter discussing automotive lubricants, including engine oils, automatic transmission fluids, manual transmission fluids, gear lubricants, and greases. This chapter, by Schwartz, Tung, and McMillan, surveyed all of these classes of lubricants, up to its publication in 2003.
More recently, the period between 2003 and 2010 has been addressed as part of a book copublished by ASTM and SAE International (coeditors Simon Tung and George Totten), where Fox surveyed the development of engine oil specifications that emerged during those years.
This chapter surveys the evolution of engine oil design and testing since 2002 and concludes with insights into future directions offered by recent tribological research. Our objective is to provide a reader new to the field with an understanding of the following:
- Engine oil composition and formulation
- North American engine oil specification development, and an outline of emergent European specifications
- How emergent specifications and legislative requirements are linked to the introduction of new engine hardware
- How tribological innovation can contribute to future enhancements in engine efficiency
In parallel, we will provide several tables comparing groups of contemporaneous specifications.
Plasma-Transferred-Arc (PTA) welding is a process that enables high deposition rates, but also causes increased thermal load on the component. Laser metal deposition (LMD) welding, on the other hand, reaches a high level of precision and thus achieves comparatively low deposition rates, which can lead to high processing costs. Combining laser and arc energy aims to exploit the respective advantages of both technologies. In this study, a novel approach of this process combination is presented using a PTA system and a 2 kW disk laser. The energy sources are combined in a common process zone as a high-speed plasma laser cladding technology (HPLC), which achieves process speeds of 10 m/min at deposition rates of 6.6 kg/h and an energy per unit length of 39 J/mm.
Resistance spot welding (RSW) is widely used in the automotive industry
as the main joining method. Generally, an automotive body contains
around 2000 to 5000 spot welds. Therefore, it is of decisive importance to characterize the mechanical properties of these areas for the further optimization and improvement of an automotive body structure. The present paper aims to introduce a novel method to investigate the mechanical properties and microstructure of the resistance spot weldment of DP1000 sheet steel. In this method, the microstructure of RSW of two sheets was reproduced on one sheet and on a bigger area by changing of the welding parameters, e. g. welding current, welding time, electrode force and type. Then, tensile tests in combination with digital Image correlation (DIC) measurement were performed on the notched tensile specimens to determine the mechanical properties of the weld metal.
The notch must be made on the welded tensile specimen to force the fracture and elongation on the weld metal, enabling the characterization of its properties. Additionally, the parameters of a nonlinear isotropic material model can be obtained and verified by the simulation of the tensile specimens. The parameters obtained show that the strength of DP1000 steel and the velocity of dislocations for reaching the Maximum value of strain hardening, are significantly increased after RSW. The effect of sample geometry and microstructural inhomogeneity of the welded joint on the constitutive property of the weld metal are presented and discussed.
The paper provides an overview on material defects which may serve as fatigue crack initiation sites and can cause final fatigue failure of a component. These comprise nonmetallic inclusions in Steel and aluminum alloys, cavities such as pores, micro-shrinkages and un-welded regions in cast, sinter and additively manufactured alloys, graphite nodules, shrinkages and other items in modular cast iron, regions of defective microstructure, microcracks and secondary notches such as undercuts and surface roughness. Besides their origin, the effect and mechanisms on fatigue crack initiation and propagation are discussed.
The considerations are proceeded and accompanied by a Brief discussion of some Basic aspects such as the stages of crack propagation along their length scale, the overcoming of crack arrest and the question when a secondary notch can be treated as a crack.
In this paper shortwave infrared (SWIR) thermographic measurements of the manufacturing of thin single-line walls via laser metal deposition (LMD) are presented. As the thermographic camera is mounted fixed to the welding arm, an acceleration sensor was used to assist in reconstructing the spatial position from the predefined welding path. Hereby we could obtain data sets containing the size of the molten pool and the oxide covered areas as functions of the position in the workpiece. Furthermore, the influence of the acquisition wavelength onto the thermograms was investigated in a spectral range from 1250 nm to 1550 nm. All wavelengths turned out to be usable for the in-situ process monitoring of the LMD process. The longer wavelengths are shown to be beneficial for the lower temperature range, while shorter wavelengths show more details within the molten pool.
Among the various welding technologies, resistance spot welding (RSW) and laser beam welding (LBW) play a significant role as joining methods for the automobile industry. The application of RSW and LBW for the automotive body alters the microstructure in the welded areas. It is necessary to identify the mechanical properties of the welded material to be able to make a reliable statement about the material behavior and the strength of welded components. This study develops a method by which to determine the mechanical properties for the weldment of RSW and LBW for two dual phase (DP) steels, DP600 and DP1000, which are commonly used for the automotive bodies. The mechanical properties of the resistance spot weldment were obtained by performing tensile tests on the notched tensile specimen to cause an elongation of the notched and welded area in order to investigate its properties. In order to determine the mechanical properties of the laser beam weldment, indentation tests were performed on the welded material to calculate its force-penetration depth-curve. Inverse numerical simulation was used to simulate the indentation tests to determine and verify the parameters of a nonlinear isotropic material model for the weldment of LBW. Furthermore, using this method, the parameters for the material model of RSW were verified. The material parameters and microstructure of the weldment of RSW and LBW are compared and discussed. The results show that the novel method introduced in this work is a valid approach to determine the mechanical properties of welded high-strength steel structures. In addition, it can be seen that LBW and RSW lead to a reduction in ductility and an increase in the amount of yield and tensile strength of both DP600 and DP1000.
The introduction of electromagnetic stirring to laser beam welding can bring several beneficial effects e.g. element homogenization and grain refinement. However, the underlying physics has not been fully explored due to the absence of quantitative data of heat and mass transfer in the molten pool. In this paper, the influence of electromagnetic stirring on the thermo-fluid flow and element transport in the wire feed laser beam welding is studied numerically and experimentally. A three-dimensional transient heat transfer and fluid flow model coupled with dynamic keyhole, magnetic induction and element Transport is developed for the first time. The results suggest that the Lorentz force produced by an oscillating magnetic field and its induced eddy current shows an important influence on the thermo-fluid flow and the keyhole stability. The melt flow velocity is increased by the electromagnetic stirring at the rear and lower regions of molten pool. The keyhole collapses more frequently at the upper part. The additional Elements from the filler wire are significantly homogenized because of the enhanced forward and downward flow. The model is well verified by fusion line shape, high-speed images of molten pool and measured element distribution. This work provides a deeper understanding of the transport phenomena in the laser beam welding with magnetic field.
The two-part paper provides an overview on the state-of-the-art in the application of engineering fracture mechanics to weldments. This, of course, cannot be exhaustive but is limited to butt and fillet welds with crack initiation at weld toes. In the present first pari, the authors briefly focus on the susceptibility of welds to cracks and other defects. Following this, they discuss in more detail the consequences of material inhomogeneity across the weld for fracture mechanics. Inhomogeneity causes scatter in fracture toughness and strength mis-match effects which both have to be considered in fracture toughness testing, crack driving force determination and fracture assessment of welded components. Part 2 of the paper series will add a discussion of welding residual stresses and questions of applying fracture mechanics to residual as well as total lifetime estimation of welds under cyclic loading.
Neutron cameras allow visualizing hydrogen distributions with radiographic or tomographic imaging methods in iron (and steel) and many other metals. The necessary contrast between hydrogen and these metals stems from the high difference in the total neutron cross section of both elements. This allows, e.g., the in situ measurement of hydrogen mass flow inside cm thick metal samples with a temporal resolution of at best 10 s using neutron radiography as well as the quantitative measurement of hydrogen accumulations, e.g., at the crack’s inner surfaces in hydrogen embrittled iron samples with neutron tomography. This new quality of the information on a micrometer scale allows new insights for the analysis of hydrogen-assisted damage mechanisms. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20 μm - 30 μm. In this contribution, we give a short historical overview of neutron imaging and show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography methods in order to visualize and quantify hydrogen accumulations, absorption processes, and diffusion. The examples are taken from the works of researchers dealing with titanium, palladium, zirconium, and iron or steel. More detailed descriptions of the experimental and analytic procedures are given for hydrogen detection using radiography and tomography on iron and steel samples.
Hybrid laser-arc welding offers many advantages, such as deep penetration, good gap bridge-ability, and low distortion due to reduced heat input. The filler wire which is supplied to the process is used to influence the microstructure and mechanical properties of the weld seam.
A typical problem in deep penetration high-power laser beam welding with filler wire and hybrid laser-arc welding is an insufficient mixing of filler material in the weld pool, leading to a non-uniform element distribution in the seam. In this study, oscillating magnetic fields were used to form a non-conservative component of the Lorentz force in the weld pool to improve the element Distribution over the entire thickness of the material. Full penetration hybrid laser-arc welds were performed on 20-mm-thick S355J2 steel plates with a nickel-based wire for different arrangements of the oscillating magnetic field. The Energy-dispersive X-ray spectroscopy (EDS) data for the distribution of two tracing elements (Ni and Cr) were used to analyze the homogeneity of dilution of the filler wire.
With a 30° turn of the magnetic field to the welding direction, a radical improvement in the filler material distribution was demonstrated. This would lead to an improvement of the mechanical properties with the use of a suitable filler wire.
The advantage of selective laser melting (SLM) is its high accuracy and geometrical flexibility.
Because the maximum size of the components is limited by the process chamber, possibilities must be found to combine several parts manufactured by SLM. An application where this is necessary, is, for example, the components of gas turbines, such as burners or oil return pipes, and inserts, which can be joined by circumferential welds. However, only a few investigations to date have been carried out for the welding of components produced by SLM. The object of this paper is, therefore, to investigate the feasibility of laser beam welding for joining SLM tube connections made of nickel-based alloys.
For this purpose, SLM-manufactured Inconel 625 and Inconel 718 tubes were welded with a Yb:YAG disk laser and subsequently examined for residual stresses and defects. The results showed that the welds had no significant influence on the residual stresses. A good weld quality could be achieved in the seam circumference. However, pores and pore nests were found in the final overlap area, which meant that no continuous good welding quality could be accomplished. Pore formation was presumably caused by capillary instabilities when the laser power was ramped out.
The Modified Varestraint Transvarestraint (MVT) test was used to investigate the solidification cracking susceptibility of an unstabilised, a Nb-stabilised and two (Ti + Nb) dual-stabilised ferritic stainless steels. Two different welding speeds of 6 and 3 mm/s using autogenous gas tungsten arc welding were employed. At the welding speed of 6 mm/s, the high-content (Ti + Nb) steel was resistant and the Nb-stabilised steel was marginally susceptible to solidification cracking. At the welding speed of 3 mm/s, the Nb and the high (Ti + Nb) steels were found to be marginally susceptible to solidification cracking while the unstabilised and low-content (Ti + Nb) grades were resistant to solidification cracking. The weld metal microstructures transverse to the welding direction revealed columnar grains in all the samples for both welding speeds. The ferritic stainless steels were generally resistant to solidification cracking, except the Nb-stabilised steel, which was marginally susceptible to solidification cracking.
A numerical framework for simulation of the steady-state thermal behaviour in keyhole mode welding has been developed. It is based on the equivalent heat source concept and consists of two parts: computational thermo-fluid dynamics and heat conduction. The solution of the thermo-fluid dynamics problem by the finite element method for a bounded domain results in a weld pool interface geometry being the input data for a subsequent heat conduction problem solved for a workpiece by a proposed boundary element method. The main physical phenomena, such as keyhole shape, thermo-capillary and natural convection and temperature-dependent material properties are taken into consideration. The developed technique is applied to complete-penetration keyhole laser beam welding of a 15 mm thick low-alloyed steel plate at a welding speed of 33 mm/s and a laser power of 18 kW. The fluid flow of the molten metal has a strong influence on the weld pool geometry. The thermo-capillary convection is responsible for an increase of the weld pool size near the plate surfaces and a bulge formation near the plate middle plane. The numerical and experimental molten pools, cross-sectional weld dimensions and thermal cycles of the heat affected zone are in close agreement.
Advantages such as element homogenization and grain refinement can be realized by introducing electromagnetic stirring into laser beam welding. However, the involved weld pool behavior and its direct role on determining the final microstructure have not been revealed quantitatively. In this paper, a 3D transient heat transfer and fluid flow model coupled with element transport and magnetic induction is developed for wire feed laser beam welding with electromagnetic stirring. The magnetohydrodynamics, temperature profile, velocity field, keyhole evolution and element distribution are calculated and analyzed. The model is well tested against the experimental results. It is suggested that a significant electromagnetic stirring can be produced in the weld pool by the induced Lorentz force under suitable electromagnetic parameters, and it shows important influences on the thermal fluid flow and the solidification parameter. The forward and downward flow along the longitudinal plane of the weld pool is enhanced, which can bring the additional filler wire material to the root of the weld pool. The integrated thermal and mechanical impacts of electromagnetic stirring on grain refinement which is confirmed experimentally by electron backscatter diffraction analysis are decoupled using the calculated solidification parameters and a criterion of dendrite fragmentation.
A discussion is provided on demands that must be met in order to apply fracture mechanics to the determination of overall fatigue lifetime and strength, i.e., S-N curves and fatigue limits. These comprise the determination of the cyclic crack driving force for all stages of fatigue crack propagation, in particular for the short crack stage where the crack driving force has to be determined for elastic-plastic deformation and the gradual build-up of the crack closure phenomenon. Special emphasis is put on a fatigue damage relevant specification of the initial crack size. Different approaches in the literature are discussed. Another important aspect is the adequate treatment of multiple crack propagation. Finally, the discussion is illustrated by an example of a butt weld made of a medium strength steel.
Dissimilar metal weld overlays of nickel-base alloys on low-alloy steel components are commonly used in the oil and gas, petrochemical, and power generation industries to provide corrosion and oxidation resistance in a wide range of service Environments and temperatures. Traditionally, dissimilar weld overlays are produced using cold or hot wire gas tungsten arc welding.
This study aims to identify and evaluate potential advantages of low heat input gas metal arc welding processes over the conventional gas tungsten arc welding in the production of such overlays. Parts I and II of this publication series described characteristics of the heat-affected zone and the transition zone region of alloy 625 on grade 22 steel overlays. These results indicate a good resistance against hydrogen-assisted cracking, which is being verified within this third part of the publication series. To determine the hydrogen-assisted cracking susceptibility, welded samples are tested using the delayed hydrogen-assisted cracking test. Fractography is performed using scanning electron microscopy along with energy dispersive spectroscopy. The results confirm the suitability and efficiency of low heat input gas metal arc welding for dissimilar weld overlays. Variation of the postweld heat treatment procedure bears potential for improvement in this respect.
Class II hydrophobins are amphiphilic proteins produced by filamentous fungi with the tendency to accumulate at the air-water interface. They show unusual adsorption kinetics with a coverage-independent adsorption rate, which was monitored with ellipsometry and atomic force microscopy. A theoretical model was introduced to identify the underlying mechanism.
To increase the competitiveness of jacket substructures compared to monopiles a changeover from an individual towards a serial jacket production based on automated manufactured tubular joints com-bined with standardized pipes has to be achieved. Therefore, this paper addresses fatigue tests of automatical-ly welded tubular X-joints focusing on the location of the technical fatigue crack. For this X-joint, the detect-ed location of the technical crack is then compared to numerical investigations predicting the most fatigue prone notch considering the structural stress approach as well as the notch stress approach. Additionally, the fatigue prone hot spot according to both approaches is compared for a typical offshore jacket double-K-joint to emphasize the significance of the presented outcomes for the existing offshore structures. Besides, the welding process of the automated manufactured tubular X-joints is presented.
Ferritic spheroidal graphite cast iron (SGI) materials have a remarkable technical poten-tial and economic impact in modern industry. These features are closely related to the question of how the cast materials can be produced without structural defects and graphite degenerations such as for example chunky graphite. Although the chunky graphite degeneration superficially seems to be well known, its metallurgical background is still controversially discussed, appropriate field-tested non-destructive tools for its quantification in castings are lacking and the knowledge on its impact on material properties is fairly limited. Addressing this status, the article is providing a current overview on the subject. Existing theories on formation and growth mechanisms of chunky graphite are briefly reviewed. Furthermore, from a metallurgical point of view, causes for the appearance of chunky graphite as well as preventive measures are concisely summarized. Particular attention is paid to the morphology of chunky graphite and how it can be characterized by destructive and non-destructive techniques. Special emphasis was laid on providing a comprehensive overview on the impact of chunky graphite on strength, ductility, fatigue limit, fatigue crack growth rate as well as fracture tough-ness of ferritic SGI materials based on experimental data. Moreover, conclusions for the assessment of castings affected by chunky graphite are drawn.
In the present work it was shown that the tribologcal profiles of special model oxides under dry unidirectional sliding have shown, that sub-oxides have a contribution to the tribological behavior of carbides and cermets, when they are tribo-oxidatively formed, because their tribological profiles as monolithic materials are homologous in part or totally, or compete with hardmetals or cermets, depending from the operating conditions regarded.
The laser implantation–named technique aims to address the tribological problems frequently seen on tool surfaces during hot stamping. It is based on the creation of elevated dome- or ring-shaped hard structures on the surface of tool steels by a localized dispersing of hard particles. Therefore, a combination of the two distinct approaches that are normally used in surface Technology for optimizing friction and wear, i.e., surface texturing and surface material optimization, are realized in one processing step. In experimental studies, a localized dispersing of TiB2 particles in the surface layer of the hot work tool steel X38CrMoV5-3 was considered and compared with punctual laser–remelted textures. The structures (micro-) hardness was measured at top- and cross-sections. With the aid of a scanning electron microscope, energy dispersive X-ray spectroscopy and X-ray diffraction the interaction between the hard particles and the substrate material were studied. From the results, an optimal parameter range was identified for laser implantation. To the investigation’s end, the implant geometry was measured by optical microscopy and White light microscopy. Furthermore, a mathematic model was introduced, which allows a prediction of the implant geometry as a response to the laser parameters. It was shown that the implantation of TiB2 particles leads to a significant hardness increase up to 1600 HV1 due to the dispersion of initial particles and an in situ precipitation of new titanium-rich phases. It was possible to create defect-free dome- and ring-shaped microstructures on the surfaces. It was also shown that the implants geometry highly depends on the applied laser parameters. The applied central composite design shows a good agreement with the experimental results.
Advanced high strength steels are usually coated by a zinc layer for an increased resistance against corrosion. During the resistance spot welding of zinc coated steel grades, liquid metal embrittlement (LME)mayoccur. As a result, cracking inside and around the spot weld indentation is observable. The extent of LME cracks is influenced by a variety of different factors. In this study, the impact of the used electrode geometry is investigated over a stepwise varied weld time.
A spot welding finite element simulation is used to analyse and explain the observed effects. Results show significant differences especially for highly increased weld times. Based on identical overall dimensions, electrode geometries with a larger working plane allow for longer weld times, while still preventing LME within the investigated material and maintaining accessibility.
Aircraft main landing gear (MLG) components are commonly manufactured from low-alloyed, martensitic, ultra-high strength steels (UHSS) that have to be coated for corrosion protection, representing an expensive and environmentally harmful production step. To avoid already partly banned corrosion protection plating, the new high-alloyed UHSS, Ferrium S53 (UNS S10500), has been designed to replace lowalloyed legacy materials and has been subjected to a limited field test over five years. As with the legacy alloys, UNS S10500 has a fully hardened martensitic microstructure known to be susceptible to hydrogen assisted cracking, per se. Containing about 10 wt% Cr, steels such as S10500 are at the lower limit for corrosion resistant alloys. Similar to super-martensitic stainless steels used in the oil and gas industry, a common failure sequence in marine environments represents pitting and subsequent hydrogen assisted stress corrosion cracking (HASCC). For addressing such phenomena quantitively, as required for respective lifetime assessments of MLG components and systems, the tolerance of such materials dependent on the absorbed hydrogen concentration must be evaluated quantitatively. However, there is a lack of such valuable materials data, as well as of the fractographic behavior dependent on the hydrogen concentration that might be absorbed during HASCC. To provide an improved understanding of the hydrogen dependent mechanical and fractographic behavior, samples of the legacy AISI 4340 and the new S10500 MLG steels have electrochemically been hydrogen-saturated and subjected to tensile testing. In contrast to a previous study, this contribution for the first time focuses on materials that have been salvaged from real service used landing gear components. In this study, it has been demonstrated that the service-applied S10500 steel has not only a higher strength, but also an improved ductility in comparison to the legacy AISI 4340 steel after similar service durations that provides a higher tolerance against hydrogen concentrations that might be absorbed during potential pitting and HASCC in marine environments. In addition, it has been found that the absorbed hydrogen concentration significantly affects the fracture behavior. Interestingly, hardening of the hydrogen charged low-alloyed AISI 4340 steel changes the fracture topography from trans- toward intergranular, while hardening of the S10500 steel turned the fracture topography from inter- to transgranular at respectively high hydrogen concentrations.
A seamless pipe made of AISI 321 stainless steel represented a part of a transportation Pipeline system for hydrogen-containing hot gas in a hydrocarbon cracking unit. After a service period of approximately 21 months, a segment of such pipe demonstrated the cracks, causing leakage and respective fire. For clarification of a failure root cause, various metallurgical investigations combined with numerical simulations have been applied. The results revealed that the rupture of seamless pipe was evidently influenced by hydrogen assisted cracking (HAC). An increased susceptibility of the alloy to HAC had to be attributed to its sensitive microstructure which was related to the occurrence of slip bands with a high quantity in austenite grains, particularly in the specific region underneath the outer wall surface. In addition, the intensity of restraint resulting from the T-joint weld configuration caused respectively higher triaxial stresses in the confined area on the outer wall surface where the crack started. The numerical simulations of hydrogen diffusion revealed that a uniform hydrogen concentration profile over the pipe wall thickness was reached when the service period was more than 20 months. This duration agreed well to the timeto-failure of the actual component. Considering additionally that the final stage of rupture by overload was preceded by severe HAC, as confirmed by the respective intergranular fracture topography.
The present work deals with the development of a strategy for the prevention of end crater defects in high-power laser welding of thick-walled circumferential welds. A series of experiments were performed to understand the influence of the welding Parameters on the formation of end crater defects such as pores, cracks, root excess weld metal and shrinkage cavities in the overlap area. An abrupt switch-off of the laser power while closing the circumferential weld leads to a formation of a hole which passes through the whole welded material thickness. A laser power ramp-down causes solidification cracks which are initiated on the transition from full-penetration mode to partial penetration. Defocusing the laser beam led to promising results in terms of avoiding end crater defects. Cracks and pores in the overlap area could be effectively avoided by using defocusing techniques.
A strategy for avoiding of end crater imperfections was tested on flat specimens of steel grade S355J2 with a wall thickness of between 8 mm and 10 mm and then transferred on the 10 mm thick pipe sections made of high-strength pipeline steel API5L-X100Q.
The tribological behavior of neat and filled PEEK and PEKK composites were compared in air and vacuum conditions. Very low friction and wear coefficient were obtained at low sliding speed while severe wear occurred at high speed. Experimental results are discussed by analysing the transfer film and wear debris.
AISI D2 is one of the most applied cold-working tool steel for deep drawing operations, due to the materials good toughness and high wear resistance. However, since the lubricant-free deep drawing as well as the processing of high strength and ultra-high strength steel sheets remaining ongoing trends in the automotive industry, the tool surfaces need to be improved regarding their friction and wear behavior. For this purpose elevated micro textures can be applied. Since protruded micro features are predominantly affected by wear, a structuring process enabling the formation of suitable textures with high wear resistance is needed.
In this paper surface texturing at microscale was conducted by laser implantation. This technique allows the fabrication of highly wear resistant, separated and elevated features (implants) on steel surfaces via a discontinuous dispersing of ceramic particles by pulsed laser radiation. The aim of this study was to investigate the techniques potential for the creation of wear resistant elevated micro features on AISI D2 tool steel surfaces by the application of TiB2 particles. The laser parameters (pulse power and length) were varied and a comparative material analysis on AISI D2 laser remelted spots and TiB2 localized dispersed zones was examined. High-speed camera recordings allowed the description of the particle insertion mechanism from pre-coatings during laser processing. Mechanical properties were analyzed by (micro-) hardness measurements at top and cross sections. The microstructure was investigated by optical microscopy, scanning electron microscopy (SEM), energy dispersive Xray
spectroscopy (EDX) and X-ray diffraction (XRD). The implants geometrical properties (diameter, height, depth) were investigated by white light interferometry and optical microscopy. The experiments reveal that a pulsed laser remelting of AISI D2 leads to a significant hardness drop due to high retained austenite (γR) contents. Contrary, a localized dispersing of TiB2 particles leads to defect free dome- or ring-shaped elevated features with hardness values up to 1800 HV1. The high hardness values result from the dispersed TiB2 particles and an in-situ precipitation of new hard particle phases, which lead to a reduction of the γR content within the matrix.
Carrier gas hot extraction (CGHE) is a commonly applied technique for determination of hydrogen in weld joints using a thermal conductivity detector (TCD) for hydrogen measurement. The CGHE is based on the accelerated hydrogen effusion due to thermal activation at elevated temperatures. The ISO 3690 standard suggests different specimen geometries as well as necessary minimum extraction time vs. temperature. They have the biggest influence on precise hydrogen determination. The present study summarizes the results and experience of numerous test runs with different specimen temperatures, geometries (ISO 3690 type B and small cylindrical samples), and factors that additionally influence hydrogen determination. They are namely specimen surface (polished/as-welded), limited TCD sensitivity vs. specimen volume, temperature measurement vs. effects of PI-furnace controller, as well as errors due to insufficient data assessment. Summarized, the temperature is the driving force of the CGHE. Two different methods are suggested to increase the heating rate up to the desired extraction temperature without changing the experimental equipment. Suggestions are made to improve the reliability of hydrogen determination depended on the hydrogen signal stability during extraction accompanied by Evaluation of the recorded data. Generally, independent temperature measurement with dummy specimens is useful for further data analysis, especially if this data is used for calculation of trapping kinetics by thermal desorption analysis (TDA).
A 3D electro-thermomechanical model is established in order to investigate liquid metal embrittlement.
After calibration to a dual phase steel of the 1000 MPa tensile strength class, it is used to analyse the thermo-mechanical system of an experimental procedure to enforce liquid metal embrittlement during resistance spot welding. In this procedure, a tensile stress level is applied to zinc coated advanced high strength steel samples during welding. Thereby, liquid metal embrittlement formation is enforced, depending on the applied stress level and the selected material.
The model is suitable to determine and visualise the corresponding underlying stresses and strains responsible for the occurrence of liquid metal embrittlement. Simulated local stresses and strains show good conformity with experimentally observed surface crack locations.
Using a novel optical measurement technique together with the optical flow algorithm, a two-dimensional deformation analysis during welding was conducted. The presented technique is the first to provide a measurement of the full strain field locally in the immediate vicinity of the solidification front.
Additionally, the described procedure of the optical measurement allows the real material-dependent values of critical strain and strain rate characterizing the transition to hot cracking during laser welding processes to be determined. Furthermore, the above-mentioned technique is independet on the welding process, which means, it can be also used for arc welding processes. Dependency between the external strain rate and the critical local strain and strain rate has been observed. That is to say, the critical local strain and strain rate is increased with an increase of the strain rate.Moreover, this technique allows automatic identification of the cases that can be critical for the solidification crack formation by monitoring the state of strain on the crack-sensitive region within the mushy zone.
Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates.
High-strength low-alloyed (HSLA) steels with yield strength ≥ 690 MPa are gaining popularity in civil engineering and construction of heavy vehicles. With increasing yield strength, the susceptibility for degradation of the mechanical properties in the presence of diffusible hydrogen, i.e., hydrogen-assisted cracking (HAC), generally increases. HAC is a result of the critical interaction between local microstructure, mechanical load, and hydrogen concentration. In existing standards for welding of HSLA-steels, recommendations including working temperatures and dehydrogenation heat treatment (DHT) are given to Limit the amount of introduced hydrogen during welding. These recommendations are based on investigations into conventional arc welding processes. In the past decade, modern weld technologies were developed to enable welding of narrower weld seams with V-grooves of 30°, e.g., the modified spray arc process. In that connection, a reduced number of weld runs and weld volume are important technical and, economic benefits. In the present study, the hydrogen distribution in S960QL multi-layer welds with thickness of 20 mm was analyzed. The influence of different weld seam opening angles, heat input, working temperature and DHT were investigated. The results show that weldments with narrow grooves contained an increased amount of diffusible hydrogen. Hydrogen concentration has been reduced by decreasing both the heat input and working temperature. Hydrogen-free weldments were only achieved via subsequent DHT after welding. Furthermore, hydrogen distribution was experimentally determined across the weld seam thickness in HSLA gas metal arc welded multi-layer welds for the first time.
The shape of the weld pool in laser beam welding plays a major role to understand the dynamics of the melt and its solidification behavior. The aim of the present work was its experimental and numerical investigation. To visualize the geometry of the melt pool in the longitudinal section a butt joint configuration of 15 mm thick structural steel and transparent quartz glass was used. The weld pool shape was recorded by means of a high-speed video camera and two thermal imaging MWIR and VIS cameras. The observations show that the dimensions of the weld pool vary depending on the depth. The regions close to the surface form a teardrop shaped weld pool. A bulge-region and its temporal evolution were observed approximately in the middle of the depth of the weld pool. Additionally, a transient numerical simulation was performed until reaching a steady state to obtain the weld pool shape and to understand the formation mechanism of the observed bulging phenomena. A fixed keyhole with an experimentally obtained shape was used to represent the full-penetration laser beam welding process. The model considers the local temperature field, the effects of phase transition, thermo-capillary convection, natural convection and temperature-dependent material properties up to evaporation temperature. It was found that the Marangoni convection and the movement of the laser heat source are the dominant factors for the formation of the bulging-region. Good correlation between the numerically calculated and the experimentally observed weld bead shapes and the time-temperature curves on the upper and bottom surface were found.