1:1 Copolymerizations of glycolide (GL) and L-lactide (LA) is performed in bulk at 100°C and at 160°C with four cyclic tin catalysts. The resulting copolyesters are characterized by SEC measurements, 1H and 13C NMR spectroscopy and by MALDI TOF mass spectrometry. At 160°C and longer reaction time (22 h) nearly complete conversion of both monomers is achieved, and cyclic copolymers with nearly random sequences are formed. At shorter times (0.5-3.0 h, depending on catalyst) the conversion of LA is incomplete, and only cyclics having even numbers of lactyl units are obtained. At 100°C at 22 h again cycles mainly consisting of even numbered lactyl units are formed, but with even and odd numbers of glycolyl units. Copolymerization of lactide at 160°C with small amounts of GL show that formation of high Tm crystallites (Tm > 190°C) is hindered even when only > 2% of GL is added. For polyglycolide containing a smaller amount of lactide complete solubility in hexafluoroisopropanol is only observed around and above 20 mol% of lactide.
Covalent bridges play a crucial role in the folding process of sequence-defined biopolymers. This feature, however, has not been recreated in synthetic polymers because, apart from some simple regular arrangements (such as block co-polymers), these macromolecules generally do not exhibit a controlled primary structure—that is, it is difficult to predetermine precisely the sequence of their monomers. Herein, we introduce a versatile strategy for preparing foldable linear polymer chains. Well-defined polymers were synthesized by the atom transfer radical polymerization of styrene. The controlled addition of discrete amounts of protected maleimide at precise times during the synthesis enabled the formation of polystyrene chains that contained positionable reactive alkyne functions. Intramolecular reactions between these functions subsequently led to the formation of different types of covalently folded polymer chains. For example, tadpole (P-shaped), pseudocyclic (Q-shaped), bicyclic (8-shaped) and knotted (α-shaped) macromolecular origamis were prepared in a relatively straightforward manner.
Two different radical polymerization techniques have been applied to covalently graft vinylformamide (VFA) onto silica particles. Grafting by the polymerization of VFA using an immobilized azo initiator on silica has been found less effective, because monomer conversion is limited in non-aqueous solvents and grafting yields are low in water. Radical copolymerization of VFA with vinyltriethoxysilane (VTS)-functionalized silica particles is suitable to produce poly(vinylformamide) (PVFA) silica hybrid particles in respectable yield. The VFA/VTS-silica ratio determines the degree of grafting. The PVFA-VTS-co-grafted silica particles can be acidically hydrolyzed into poly(vinylamine)-grafted silica particles. Molecular structures of the surface groups and grafted polymer chains have been confirmed by means of solid state 13C{1H} cross-polarization magic-angle spinning (CP MAS) NMR spectroscopy. Zeta potential measurements show the altering of the former silica particles surface charges arising from the introduction of basic groups on the surface.