Knowledge of the compressional and thermal behaviour of metals and alloys is of a high fundamental and applied value. In this work, we studied the behaviour of Ir, Rh, and their fcc-structured alloys, Ir0.42Rh0.58 and Ir0.26Os0.05Pt0.31Rh0.23Ru0.15, up to 70 GPa using the diamond anvil cell technique with synchrotron X-ray diffraction. We found that all these materials are structurally stable upon room-temperature hydrostatic compression in the whole pressure interval, as well as upon heating to 2273 K both at ambient and high pressure. Rh, Ir0.42Rh0.58 and Ir0.26Os0.05Pt0.31Rh0.23Ru0.15 were investigated under static compression for the first time. According to our data, the compressibility of Ir, Rh, fcc–Ir0.42Rh0.58, and fcc Ir0.26Os0.05Pt0.31Rh0.23Ru0.15, can be described with the 3rd order Birch-Murnaghan equation of state with the following parameters: V0 = 14.14(6) Å3·atom−1, B0 = 341(10) GPa, and B0' = 4.7(3); V0 = 13.73(7) Å3·atom−1, B0 = 301(9) GPa, and B0' = 3.1(2); V0 = 13.90(8) Å3·atom−1, B0 = 317(17) GPa, and B0' = 6.0(5); V0 = 14.16(9) Å3·atom−1, B0 = 300(22) GPa, B0' = 6(1), where V0 is the unit cell volume, B0 and B0' – are the bulk modulus and its pressure derivative.
The study presented here focusses on a systematic analysis of oxidation mechanisms of the well-known Cr20Mn20Fe20Co20Ni20 alloy and one of its ternary sub-system Cr33.3Co33.3Ni33.3 which were reported in the literature to exhibit attractive mechanical properties. Both alloys are single phase fcc prior to oxidation and were simultaneously exposed to different oxygen containing atmospheres at 700° C and 800° C for durations up to 288 h. Cr20Mn20Fe20Co20Ni20 showed poor oxidation resistance at high temperatures due to its high amount of manganese leading to the formation of non-protective Mn-oxide scales. In contrast, a relatively homogeneous and protective chromia layer was found to form on CrCoNi at 700° C and 800° C after each exposure time. Mass change-, SEM- and XRD analysis of the oxide layers were performed in the present study and provide a better understanding of the oxidation mechanisms as well as the impact of the alloy composition on oxidation behavior.