Filtern
Erscheinungsjahr
Dokumenttyp
- Vortrag (19931) (entfernen)
Sprache
- Deutsch (13122)
- Englisch (6758)
- Mehrsprachig (24)
- Spanisch (13)
- Französisch (9)
- Russisch (3)
- Tschechisch (1)
- Ungarisch (1)
Referierte Publikation
- nein (19931)
Schlagworte
- Korrosion (249)
- Corrosion (138)
- Additive manufacturing (122)
- Additive Manufacturing (121)
- Additive Fertigung (114)
- Concrete (107)
- Hydrogen (102)
- Nanoparticles (93)
- LIBS (92)
- Wasserstoff (82)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (921)
- 6 Materialchemie (832)
- 7 Bauwerkssicherheit (815)
- 9 Komponentensicherheit (739)
- 1 Analytische Chemie; Referenzmaterialien (578)
- 4 Material und Umwelt (440)
- 5 Werkstofftechnik (433)
- 3 Gefahrgutumschließungen; Energiespeicher (419)
- 7.6 Korrosion und Korrosionsschutz (351)
- 9.4 Integrität von Schweißverbindungen (350)
Diese Präsentation stellt die gegenwärtige Situation zur Einstufung von primer caps (Anzündhütchen) gemäß Richtlinie 2014/28/EU und UN Model Regulations Rev.23 (Volume I) dar. Spezifische Eigenschaften und Gefährdungen werden dargestellt und eine Abgrenzung zur Richtlinie 2013/29/EU aufgezeigt.
Gips gehört zu den nachgefragtesten Baustoffen und entsprechend steigt der Gipsverbrauch weltweit schon seit Jahrzehnten an. In Deutschland wird der Gipsbedarf seit vielen Jahren zu einem guten Teil durch REA-Gips, einem Nebenprodukt aus der Abgasreinigung von Kohlekraftwerken, gedeckt. Die weitere Gipsversorgung erfolgt größtenteils durch die Nutzung natürlicher Gipsvorkommen. Ein geringer, aber steigender Anteil an RC-Gips aus dem Baustoffrecycling und die Nutzung synthetischer Gipse aus Nebenprodukten anderer Industriezweige sind ebenfalls zu verzeichnen. Aufgrund der nationalen Klimaschutzziele und der damit verbundenen Abschaltung von Kohlekraftwerken wird das REA-Gipsangebot in den nächsten Jahren jedoch weiter deutlich zurückgehen, so dass andere Gipsquellen erschlossen werden müssen.
Abhängig von der Lebensdauer der verwendeten Gipsprodukte im Bausektor ist infolge des in den vergangenen Jahren erfolgten Anstiegs des Gipsverbrauchs auch mit einer Zunahme von Gipsresten in Bau- und Abbruchabfällen zu rechnen. Im Hinblick auf eine bevorstehende Verknappung von Gips wird die Rückgewinnung dieser Gipse aus Bau- und Abbruchabfällen immer wichtiger. Das Recycling von Gipskartonplatten ist mittlerweile eine etablierte Technik und wird bereits seit einigen Jahren in industriellem Maßstab durchgeführt. Außerdem werden neue Verfahren zur Wiederverwertung weiterer Gipsprodukte aus Rück- und Umbaumaßnahmen untersucht. Von besonderem Interesse sind verschiedene Arten von Gipsplatten, da sie gut für selektiven Rückbau geeignet sind. Daher können sie vergleichsweise frei von Verunreinigungen oder Störstoffen zurückgewonnen werden, was für das Gipsrecycling besonders wichtig ist.
In dem vom Bundesministerium für Bildung und Forschung geförderten Forschungsprojekt "GipsRec 2.0" werden technische, wirtschaftliche und ökologische Aspekte des Recyclings von Gipsfaserplatten sowie von verschiedenen Synthesegipsen untersucht und bewertet. Die Aufbereitung von Gipsfaserplatten erfolgte im halbtechnischen Maßstab, an verschiedenen potentiellen Ausgangsstoffen für synthetische Gipse wurden Laborversuche durchgeführt. Erfolgversprechende Verfahrenswege werden ökobilanziell bewertet. Ziel dieser Arbeiten ist die Erschließung der Sekundärrohstoffpotenziale von weiteren Quellen für die RC-Gipsproduktion um mit einer Steigerung des Gipsrecyclings die in naher Zukunft durch die Reduktion der REA-Gips-Bereitstellung entstehende Lücke in der Rohstoffversorgung zu verringern.
Distributed fiber optic strain sensing for structural health monitoring of 70 MPa hydrogen vessels
(2024)
We report on the development and testing of 70 MPa hydrogen pressure
vessels with integrated fiber optic sensing fibers for automotive use. The paper deals with the condition monitoring of such composite pressure vessels (CPVs) using the optical backscatter reflectometry (OBR) applied for a distributed fiber optic strain sensing along fully integrated polyimide-coated single-mode glass optical fiber (SM-GOF). The sensing fibers were embedded into the vessel structure by wrapping them over the polymer liner during the manufacturing process of the carbon fiber reinforced polymer (CFRP). Detecting local strain events by the integrated fiber optic sensors can be an opportunity for monitoring the material degradation of CPVs under static and cyclic loading.
Low Transformation Temperature (LTT)-Schweißzusätze sind ein innovativer Ansatz, um Eigenspannungen in Schweißnähten zu reduzieren. Dieser Vortrag behandelt neben den Einfluss der LTT-Schweißzusätze auch deren Naht-Ausführungen. Die unterschiedlichen LTT-Nahtgeometrien haben einen signifikanten Einfluss auf den Eigenspannungsabbau in der Schweißnaht und der Wärmeeinflusszone (WEZ).
Surface-modification platforms that are universally applicable are vital for the development of new materials, surfaces, and nanoparticles. Mussel-inspired materials (MIMs) are widely used in various fields because of their strong adhesive properties and post-functionalization reactivity. However, conventional MIM coating techniques have limited deposition selectivity and lack structural control, which has limited their use in microdevices that require full control over deposition. To overcome these limitations, we developed a micropatterning technique for MIMs using multiphoton lithography, which does not require photomasks, stamps, or multistep procedures. This method enables the creation of MIM patterns with micrometer resolution and full design freedom and paves the way for innovative applications of MIMs in various multifunctional systems and microdevices, such as microsensors, MEMS, and microfluidics.
Low transformation temperature (LTT) welding consumables offer an innovative approach to increase the fatigue strength of welded high-strength steel structures. LTT welding consumables are characterized by a martensitic phase transformation near ambient temperature, which generates compressive residual stresses in the weld and heat affected zone (HAZ). The aim is to achieve a weld geometry, which generate high compressive residual stresses at the fatigue crack critical weld toe.
Longitudinal stiffeners were gas metal arc welded using a conventional welding consumable; the base material was a high strength steel S700M. A chromium-nickel alloyed LTT consumable was deposit subsequently just on front sides of the stiffeners. Different welding parameters led to varying cross sections of the weld. The residual stresses were determined using X-ray diffraction (XRD) in the crack critical HAZ.
When using only the conventional, the HAZ is characterized by high tensile residual stresses. The additional application of the LTT alloy leads to a significant reduction of the tensile residual stresses. Depending on the weld geometry, even compressive residual stresses can be observed at the weld toe
The thermal history during additive manufacturing of complex components differs significantly from the thermal history of geometrically primitive test specimens. This can result in differences in properties that can lead to different material behavior. In this talk, the concept of representative test specimens is introduced, which enables the transfer of thermal histories from complex geometries to simple geometries, which can lead to better comparability of material properties.
Laser Powder Bed Fusion (PBF-LB/M) of AISI 316L stainless steel has gained popularity due to its exceptional capacity to produce complex geometries and hierarchical microstructures, which can increase the yield strength while maintaining good ductility. Nevertheless, owing to high thermal gradients encountered during the process, the as printed 316L stainless steel often exhibit microstructural heterogeneities and residual stresses, which can limit its performance in demanding environments. Hence, employing heat treatments which balance the reduction of residual stresses while retaining improved static strength may be beneficial in various scenarios and applications. This study investigates the impact of post-processing heat treatments on the microstructure of 316L stainless steel manufactured via PBF-LB/M, along with its correlation with micro-hardness properties. To this end, 6 different heat treatments, i.e., 450 °C for 4h, 700 °C for 1h, 700 °C for 3h, 800 °C for 1h, 800 °C for 3h, and 900 °C for 1h, were applied to different specimens and Vickers hardness measurements (HV1) were performed in all states. At 800 °C, although the cellular structure appears to be retained, there is an observable increase in cellular size. However, while treatments exceeding 900 °C indicate no significant grain growth compared to other conditions, the cellular structure is entirely dissolved, which leads to a reduced Vickers hardness. The effect of the heat treatments on other microstructural features such as grain size and morphology, melt pool boundaries (MPB), crystallographic texture, chemical segregation, dispersoids and phase stability are also discussed in the present work
The general term additive manufacturing (AM) encompasses processes that enable the production of parts in a single manufacturing step. Among these, laser powder bed fusion (PBF-LB) is one of the most commonly used to produce metal components. In essence, a laser locally melts powder particles in a powder bed layer-by-layer to incrementally build a part. As a result, this process offers immense manufacturing flexibility and superior geometric design capabilities compared to conventional processes. However, these advantages come at a cost: the localized processing inevitably induces large thermal gradients, resulting in the formation of large thermal stress during manufacturing. In the best case, residual stress remains in the final parts produced as a footprint of this thermal stress. Since residual stress is well known to exacerbate the structural integrity of components, their assessment is important in two respects. First, to optimize process parameter to minimize residual stress magnitudes. Second, to study their effect on the structural integrity of components (e.g., validation of numerical models). Therefore, a reliable experimental assessment of residual stress is an important factor for the successful application of PBF-LB. In this context, diffraction-based techniques allow the non-destructive characterization of the residual stress. In essence, lattice strain is calculated from interplanar distances by application of Braggs law. From the known lattice strain, macroscopic stress can be determined using Hooke’s law. To allow the accurate assessment of the residual stress distribution by such methods, a couple of challenges in regard of the characteristic PBF-LB microstructures need to be overcome.
This presentation highlights some of the challenges regarding the accurate assessment of residual stress in PBF-LB on the example of the Nickel-based alloy Inconel 718. The most significant influencing factors are the use of the correct diffraction elastic constants, the choice of the stress-free reference, and the consideration of the crystallographic texture. Further, it is shown that laboratory X-ray diffraction methods characterizing residual stress at the surface are biased by the inherent surface roughness. Overall, the impact of the characteristic microstructure is most significant for the selection of the correct diffraction elastic constants. In view of the localized melting and solidification, no significant gradients of the stress-free reference are observed, even though the cell-like solidification sub-structure is known to be heterogeneous on the micro-scale.
Unter Passivität versteht man den Korrosionsschutz durch dünne, festhaftende Schichten aus Korrosionsprodukten. Für den schadensfreien Einsatz nichtrostender Stähle ergeben sich daraus zwei grundsätzliche Anforderungen.
Erstens muss sich die Passivschicht vollständig ausbilden können. Dabei sind die Oberflächenausführung, die mechanische Bearbeitung, die Elementverteilung, Ausscheidungen, die Wärmeeinbringung z.B. bei der schweißtechnischen Verarbeitung, Anlauffarben, sowie die chemische Nachbehandlung bzw. Konditionierung der Oberflächen von großer Bedeutung. Zweitens muss die Repassivierung von Defektstellen unter den Einsatzbedingungen möglich sein. Für das Repassivierungsvermögen sind die Legierungszusammensetzung, mögliche kritische Betriebszustände, prozessbedingte Besonderheiten, wie etwa Stagnationsbedingungen und Reinigungsprozesse von Bedeutung.