For a deep process understanding of the laser powder bed fusion process (PBF-LB/M), recording of the occurring surface temperatures is of utmost interest and would help to pave the way for reliable process monitoring and quality assurance. A notable number of approaches for in-process monitoring of the PBF-LB/M process focus on the monitoring of thermal process signatures. However, due to the elaborate calibration effort and the lack of knowledge about the occurring spectral directional emissivity, only a few approaches attempt to measure real temperatures. In this study, to gain initial insights into occurring in the PBF-LB/M process, measurements on PBF-LB/M specimens and metal powder specimens were performed for higher temperatures up to T = 1290 °C by means of the emissivity measurement apparatus (EMMA) of the Center for Applied Energy Research (CAE, Wuerzburg, Germany). Also, measurements at ambient temperatures were performed with a suitable measurement setup. Two different materials—stainless steel 316L and aluminum AlSi10Mg—were examined. The investigated wavelength λ ranges from the visible range (λ-VIS= 0.40–0.75 µm) up to the infrared, λ = 20 µm. The influence of the following factors were investigated: azimuth angle φ, specimen temperature TS, surface texture as for PBF-LB/M surfaces with different scan angles α, and powder surfaces with different layer thicknesses t.
Infrared thermography using a focused (spot or line) beam has proved to be effective for detection of surface breaking cracks on planar samples. In this work, we use the same principle, but applied to complex shaped components, like a rail section, a gear, and a gas turbine blade. We use a six-axis robot arm to move the sample in front of our thermographic setup. Several scanning paths and thermographic parameters are explored: scanning speed, density of points in each scanning slice, laser power and camera frame-rate. Additionally, we explore semi-automatic evaluation algorithms for crack detection, as well as 2D-to-3D registration of the found indications.