The influence of weathering on the fire retardancy of polymers is investigated by means of a cone calorimeter test, before and after artificial weathering. The surface degradation was monitored using different techniques (ATR–FTIR, microscopy, colour measurement). Different kinds of polymeric materials were chosen, all as they are used in practice: polycarbonate (PC) blends, polyamide (PA) and polypropylene (PP) flame-retarded with arylphosphate, melamine cyanurate (MC) and intumescent formulation based on ammonium polyphosphate (APP), respectively.
All samples show material degradation at the surface due to weathering. No significant weathering influence occurs on the flame retardancy when it is a bulk property, as was observed for aryl phosphates in PC blends and MC in PA. When the fire retardancy is dominated by a surface mechanism, dependence on the duration of weathering is detected: for intumescent formulations based on ammonium APP in PP, a worsening in the formation of the intumescent network was observed.
Thermal insulation and mechanical resistance play a crucial role for the performance of an intumescent coating. Both properties depend strongly on the morphology and morphological development of the foamed residue. Small amounts (4 wt%) of fiberglass, clay and a copper salt, respectively, are incorporated into an intumescent coating to study their influence on the morphology and Performance of the residues. The bench scale fire tests were performed on 75 x 75 x 2 mm³ coated steel plates according to the standard time–temperature curve in the Standard Time Temperature Muffle Furnace+ (STT Mufu+). It provided information about foaming dynamics (expansion rates) and thermal insulation. Adding the copper salt halved the expansion height, whereas the clay and fiberglass Change the height of the residue only moderately. The time to reach 500 °C was improved by 31% for clay and 15% for the other two fillers. Nondestructive micro computed tomography is used to assess the inner structure of the residues. A transition of the residue from a black, carbonaceous foam with closed cells into an inorganic, residual open cell sponge occurs at high temperatures. This transition is due to a loss of carbon; the change in microstructure is analyzed by scanning electron microscopy. Additional mechanical tests are performed and interpreted with respect to the results of the morphology analysis. Adding clay or copper salt improved the mechanical resistance tested by a factor 4. The additives significantly influence the thickness and foaming Dynamics as well as the inner structure of the residues, whereas their influence on insulation Performance is moderate. In conclusion, different modes of action are observed to achieve similar insulation performance during the fire test.
The cone calorimeter has become one of the most important and widely used instruments for the research and development of fire retarded polymeric materials. The paper addresses three important ways in which the principal setup influences the results factors which sometimes do not receive due consideration when drawing conclusions. The paper discusses in detail the impact on cone calorimeter results of the choice of external heat flux, the influence on the peak of heat release rate of sample thickness and thermal feedback from the back of the sample, and the influence on irradiance of the horizontal and vertical distances from the cone heater.
In addition to the acid source, charring agent, and blowing agent, the binder is a crucial part of an intumescent coating. Its primary task is to bind all compounds, but it also acts as a carbon source and influences the foaming process. A series of intumescent coatings based on five different binders was investigated in terms of insulation, foaming, mechanical impact resistance, and residue morphology. The Standard Time-Temperature modified Muffle Furnace (STT MuFu+ ) was used for the bench-scale fire resistance tests and provided data on temperature and residue thickness as well as well-defined residues. The residue morphology was analyzed by nondestructive m-computed tomography and scanning electron microscopy. A moderate influence of the binder on insulation performance was detected in the set of coatings investigated, whereas the foaming dynamics and thickness achieved were affected strongly. In addition, the inner structure of the residues showed a rich variety. High expansion alone did not guarantee good insulation. Furthermore, attention was paid to the relation between the microstructure transition induced by carbon loss due to thermo-oxidation of the char and the development of the thermal conductivity and thickness of the coatings during the fire test.
Intumescent coatings are used for decades to increase the fire resistance of steel or wood constructions. Intermediate and full scale tests are used to assess their protection performance. For the product development and screening, cheaper and faster bench-scale tests are demanded that provide information about thermal protection, foaming dynamics and mechanical resistance. In the recent years, we have developed several bench-scale fire resistance tests and used them in different research and developing projects. The influence of distinct binders and fillers, respectively, was studied in intumescent coatings using the Standard Time Temperature modified muffle furnace (STT Mufu+). This bench-scale test evaluates the fire resistance (by means of temperature measurements) and the foaming behaviour (by means of a high-temperature endoscope) during a standard time-temperature exposure. The fire residues were suitable for advance residue analysing techniques like nondestructive μ-computed tomography (μ-CT). Also, scanning electron microscopy was used to investigate the microscopic structure of the surface and inside of the residues. The mechanical resistance of the residues was tested by an impact resistance experiment.
The binder influence on the insulation of the coating was small for the investigated systems. Nevertheless, it was interestingly noted, that coatings with high expansion did not provide the best protection. The great influence of the binder material on the inner structure of the foamed residues was revealed by the μ-CT images. Clear differing morphologies were observed. These led to distinct mechanical resistance properties of the tested coatings. Also the change of a low amount of fillers, such as fibres and clay was investigated with similar effects. What is more, a transition of the residue from black, carbonaceous foam with closed cells into an inorganic, residual open cell sponge occurs at high temperatures during the test. This transition is due to the loss of carbon; the change in microstructure is analysed by scanning electron microscopy.
The bench-scale tool presented outreaches screening; the investigation based on the STT Mufu+ delivers a deeper understanding of the phenomena controlling the performance of intumescent coatings.
Intumescent coatings have been used for fire protection of steel for decades, but there is still a need for improvement and adaptation. The key parameters of such coatings in a fire Scenario are thermal insulation, foaming dynamics, and cohesion. The fire resistance tests, large furnaces applying the standard time temperature (STT) curve, demand coated full‐scale components or intermediate‐scale specimen. The STT Mufu+ (standard time temperature muffle furnace+) approach is presented. It is a recently developed bench‐scale testing method to analyze the performance of intumescent coatings. The STT Mufu+ provides vertical testing of specimens with reduced specimen size according to the STT curve. During the experiment, the foaming process is observed with a high‐temperature endoscope. Characteristics of this technique like reproducibility and resolution are presented and discussed. The STT Mufu+ test is highly efficient in comparison to common tests because of the reduced sample size. Its potential is extended to a superior research tool by combining it with advanced residue analysis (μ‐computed tomography and scanning electron microscopy) and mechanical testing. The benefits of this combination are demonstrated by a case study on 4 intumescent coatings. The evaluation of all collected data is used to create performance‐based rankings of the tested coatings.
The exploration of condensed phase mechanisms such as charring and intumescence has been pushed forward in the last decades, since it is believed that focusing on these concepts will bring materials closer to an efficient and ecologically friendly fire retardancy. They promise to concentrate efficient fire retardancy at the key position between pyrolysis zone and gas phase. Examples of residue/char forming and intumescent materials are used to illustrate the influence of mass and heat barrier effects on the fire behavior of materials and general results are presented. A comprehensive understanding of the mechanisms and structure-property relationships in fire retardancy is presented.
Phosphorus-based flame retardancy mechanisms - Old hat or a starting point for future development?
(2010)
Different kinds of additive and reactive flame retardants containing phosphorus are increasingly successful as halogen-free alternatives for various polymeric materials and applications. Phosphorus can act in the condensed phase by enhancing charring, yielding intumescence, or through inorganic glass formation; and in the gas phase through flame inhibition. Occurrence and efficiency depend, not only on the flame retardant itself, but also on its interaction with pyrolysing polymeric material and additives. Flame retardancy is sensitive to modification of the flame retardant, the use of synergists/adjuvants, and changes to the polymeric material. A detailed understanding facilitates the launch of tailored and targeted development.
Products and by-products of the invertebrate and vertebrate farming, respectively, are shown to be promising bio-based flame retardant adjuvants in epoxy thermosets. While the addition of bone meal results in the formation of an inorganic shield, protein-based powders from insects provide an intumescent behavior under forced flaming conditions. Combining the latter with a common flame retardant such as ethylene diamine phosphate, the charring efficiency and self-extinguishing properties can be further enhanced.