Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (28) (entfernen)
Schlagworte
- Composites (28) (entfernen)
Organisationseinheit der BAM
- 6 Materialchemie (2)
- 6.6 Physik und chemische Analytik der Polymere (2)
- 8 Zerstörungsfreie Prüfung (2)
- 9 Komponentensicherheit (2)
- 9.5 Tribologie und Verschleißschutz (2)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
- 7 Bauwerkssicherheit (1)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (1)
- 8.4 Akustische und elektromagnetische Verfahren (1)
- 8.5 Röntgenbildgebung (1)
A key application of atomic force microscopy (AFM) is the measurement of physical properties at sub-micrometer resolution. Methods such as force–distance curves (FDCs) or dynamic variants (such as intermodulation AFM (ImAFM)) are able to measure mechanical properties (such as the local stiffness, kr) of nanoscopic heterogeneous materials. For a complete structure–property correlation, these mechanical measurements are considered to lack the ability to identify the chemical structure of the materials. In this study, the measured attractive force, Fattr, acting between the AFM tip and the sample is shown to be an independent measurement for the local chemical composition and hence a complete structure–property correlation can be obtained. A proof of concept is provided by two model samples comprised of (1) epoxy/polycarbonate and (2) epoxy/boehmite. The preparation of the model samples allowed for the assignment of material phases based on AFM topography. Additional chemical characterization on the nanoscale is performed by an AFM/infrared-spectroscopy hybrid method. Mechanical properties (kr) and attractive forces (Fattr) are calculated and a structure–property correlation is obtained by a manual principle component analysis (mPCA) from a kr/Fattr diagram. A third sample comprised of (3) epoxy/polycarbonate/boehmite is measured by ImAFM. The measurement of a 2 × 2 µm cross section yields 128 × 128 force curves which are successfully evaluated by a kr/Fattr diagram and the nanoscopic heterogeneity of the sample is determined.
Epoxy carbon-fibre prepreg, Hexcel Type 6376 HTS, was investigated using Dynamic Mechanical Analysis (DMA). The DMA characteristic parameters are storage modulus E', loss modulus E' and loss factor tanδ. These parameters are ideally suited to observe the vitrification, referred to as glass transition, resulting from the cross-linking reaction. Detection of the cure state may also be achieved by determining the momentary glass transition temperature of partially cured samples. The consequent use of a multi-frequency measuring regime was used to derive the apparent activation energy for the glass transition process. Different temperature programs were also applied to monitor the curing process directly, as well as to investigate the different states of incomplete cure reached in preceding curing steps. The intention was to provide better understanding of the consequences of an interrupted autoclave curing process and to use DMA to detect the cure state achieved. With DMA, the continuation of an incomplete curing process also can be monitored. DMA measurements up to 300 °C showed, furthermore, that the final glass transition temperature was reduced by thermal degradation at high temperatures.
After a delamination process in a C-fiber reinforced polymer composite, the identification of the polymer residue of poly-(phenylene sulphide) on carbon fiber surfaces gives important information on the composite failure mechanism. Using scanning force microscopy (SFM) in its lateral force imaging mode or with the stiffness imaging mode, it is almost impossible to distinguish the two composite components owing to a very low material-based contrast of the local friction and compliance. The new technique using contrast based on a local AC current measurement allows a clear identification of the conducting carbon fiber and the non-conducting polymer coverage.
Basic paths towards fully green flame retarded kenaf fiber reinforced polylactic acid (K-PLA) biocomposites are compared. Multicomponent flame retardant Systems are investigated using an amount of 20 wt% such as Mg(OH)2 (MH), ammonium polyphosphate (APP) and expandable graphite (EG), and combinations with Silicon dioxide or layered silicate (LS) nanofillers. Adding Kenaf fibers and flame retardants increases the E modulus up to a factor 2, although no compatibilizer was used at all. Thus, in particular adding EG and MH decreases the strength at maximum elongation, and kenaf fibers, MH, and EG are crucial for reducing the elongation to break. The Oxygen index is improved by up to 33 vol% compared to 17 vol% for K-PLA. The HB classification of K-PLA in the UL 94 test is outperformed. All flame retarded biocomposites show somewhat lower thermal stability and increased amounts of residue. MH decreases the fire load significantly, and the greatest reduction in peak heat release rate is obtained for K-PLA/15MH/5LS. Synergistic effects are observed between EG and APP (ratio 2:1) in flammability and fire properties. Synergistic multicomponent systems containing EG and APP, or MH with adjuvants offer a promising route to green flame retarded natural fiber reinforced PLA biocomposites.
Die tribologischen Eigenschaften von graphitgefüllten Polyimiden gegen Stahl 100Cr6 wurden an Luft, im Hochvakuum (l0⁻ ³ Pa) und in Wasserstoffumgebung bei verschiedenen Drücken (10³ Pa, 10⁴ Pa und 10⁵ Pa) untersucht. Zwei unterschiedliche Polyimid-Typen wurden eingesetzt, wobei Typ und Menge des Graphits variiert wurden.
Die Experimente wurden bei 3,1 MPa Kontaktdruck und einer Gleitgeschwindigkeit von 0,2 m/s bzw. 1 m/s durchgeführt. Die verschlissenen Oberflächen und die Morphologie des Materialübertrags auf die Stahl-Gegenfläche wurden mittels Lichtmikroskopie, REM, TEM und FTIR untersucht. Die Untersuchung zeigt, dass sowohl die Matrix als auch der Graphitanteil einen deutlichen Einfluss auf das Reibverhalten von Verbundwerkstoffen in Wasserstoffumgehungen haben können.
The development of hydrogen technologies entails high safety requirements in distribution and dispensing infrastructure. Therefore, it is necessary to pursue research on material compatibility in hydrogen, especially for critical parts with tribological issues.
The focus of this study is to evaluate the influence of hydrogen on a wider range of commercially available polymer materials. Thereby, the friction and wear behavior of different grades of TPE, POM, PA66, PA12, PPA, PEEK, PPS, PTFE, PAI, PI and PBI were investigated against a rotating steel disk (AISI 304). Filled and unfilled polymers from different suppliers were evaluated at room temperature in air, vacuum and hydrogen gas (H2) as well as in liquid hydrogen at - 253°C (LH2).
The sliding behavior of the polymer materials is discussed by means of surface analyses, whereby special attention is paid to the formation of a transfer film.
According to the results at ambient temperature, the effect of hydrogen environment on the tribological behavior of neat polymers may be related to lack of moisture, but also to saturated hydrocarbons in gaseous hydrogen. In liquid hydrogen, the best tribological performances were achieved with neat PA polymers as well as PPS and PI composites.
The tribological behavior of neat and filled PEEK and PEKK composites were compared in air and vacuum conditions. Very low friction and wear coefficient were obtained at low sliding speed while severe wear occurred at high speed. Experimental results are discussed by analysing the transfer film and wear debris.
The search for durable and sustainable construction materials inspires the developments in the world of cement concrete, as well as in the world of concretepolymer composites. Both worlds recognize, strive for and accept each others contribution to the synergetic effects that are realized by the combination of classical building materials and polymers. A better knowledge of materials behaviour, especially in the field of admixtures, and a better understanding of curing processes allowed the development of highly performing mineral or modified mineral concretes, mortars and grouts. CPC-science becomes an invaluable element in the development of sustainable construction materials. ICPIC brings together practitioners and scientists, dealing with concretepolymer composites in all industrial fields, but with emphasis on construction industry. The 11th International ICPIC Congress took place in Berlin, 24th June 2004. New trends and evolutions have been presented and discussed. The highlights of the Congress, and the synergies for the construction world that emerge from this congress on polymers in concrete in combination with cement concrete, are presented.