In addition to constructional requirements in civil engineering stainless steels often have to fulfil high visual demands. Unexpected impairments of the visual appearance of stainless steels under low corrosive conditions are a widespread problem today. Frequently it is supposed that this is caused by changes in the alloy composition, worse environmental conditions or improper handling. Within a research project the systematic investigation of several cases of damaged stainless steel bars has shown that the reasons are based on well-known material defects like chemical inhomogeneities (e.g. precipitations or local carburization) or geometrical defects (e.g. undercuts, rolling defects or shell formation). Thus, the failures could be clearly identified as production failures of the respective semi-finished products.
Die Erzeugung geschliffener Oberflächen bei hochlegierten Chrom-Nickel-Stählen aus dekorativen Gründen z. B. beim Einsatz im Bereich Innenarchitektur kann sich u. U. problematisch hinsichtlich der Korrosionsbeständigkeit auswirken. Bei den Untersuchungen zum Einfluss der Verfahrensparameter beim industriellen Schleifen zur Erzeugung eines bestimmten optischen Erscheinungsbildes stellte sich heraus, dass die Rauheit allein kein Maß für die zu erwartende Korrosionsbeständigkeit darstellt. Die Variation verschiedener Schleifparameter, aber auch die Art des Schleifmittels können einen erheblichen Einfluss auf die Korrosionsbeständigkeit ausüben. Neben den Ergebnissen verschiedener Auslagerungsversuche werden elektrochemische Untersuchungen an den geschliffenen Oberflächen vorgestellt. Dabei konnte mittels elektrochemischer Rauschmessungen die unterschiedliche Korrosionsneigung der Oberflächen nachgewiesen werden.
Translated Abstract
The influence of grinding treatment of stainless steels on the corrosion behaviour
Mechanical grinding of stainless steels is often used for decoration purposes, for instance in the interior decoration. However, this treatment can cause problems regarding the corrosion resistance. During investigations of the influences of processing parameters of industrial grinding it was shown, that roughness only is not the expected crucial parameter for the corrosion resistance. The variation of different grinding parameters and also the type of abrasives have a substantial influence. Beside the long term tests electrochemical investigation at the ground surfaces are presented. The different corrosion susceptibility of the surfaces could be proven by means of electrochemical noise measurements.
Thick-walled components made of duplex stainless steels are used in the semi-finished products as well as in machinery, apparatus and plant construction. Electron beam welding (EBW) of these components may be recommended for economic and quality reasons. To guarantee the necessary mechanical and technological properties and the corrosion resistance, the duplex stainless steels are welded with filler material and afterwards undergo a post-weld heat treatment. The present work shows interim results of investigations concerning the development of an electron beam multi-process technology for welding these steels without filler material and post-weld heat treatment. The studies were performed on standard duplex stainless steel of type 1.4462 (X2CrNiMoN22-5-3). When welding duplex stainless steels, the cooling rate and the chemical composition have a crucial influence on the final result. Based on fundamental investigations relating to the influence of the process parameters on the effusion of nitrogen and the cooling rates, the resulting austenite formation, mechanical properties and the corrosion resistance were taken into account to develop appropriate electron beam multi-process techniques. The ferrite content was measured metallographically and by magnetic induction, the impact toughness was measured at –40 °C and the determination of critical pitting temperatures was performed using electrochemical noise measurements.
Neue bauaufsichtliche Zulassung für Bauteile und Verbindungsmittel aus nichtrostenden Stählen
(1999)
Im Rahmen der Erarbeitung einer neuen bauaufsichtlichen Zulassung für nichtrostende Stähle ergab sich die Fragestellung, ob durch eine Kaltverfestigung die Beständigkeit gegenüber Spannungsrißkorrosion negativ beeinflußt wird. Durch experimentelle Versuche an verschiedenen nichtrostenden Stählen sollte geklärt werden, ob kaltverformtes Material bei hoher Chloridbelastung, wie sie z. B. in Schwimmhallenatmosphäre vorkommen kann, eine höhere Empfindlichkeit gegenüber Spannungsrißkorrosion aufweist. Die Untersuchungen wurden mit den hochlegierten Stählen 1.4462 sowie 1.4529 durchgeführt. Als Vergleichswerkstoff mit bekannter Empfindlichkeit gegenüber Spannungsrißkorrosion bei hoher Chloridbelastung wurde der Stahl 1.4301 eingesetzt. Die Versuche erfolgten mittels Bügel- und Zugproben, auf die Tropfen aus gesättigter Magnesiumchloridlösung aufgebracht waren. Hinweise auf eine höhere Spannungsrißkorrosionsempfindlichkeit des kaltverformten Materials wurden aber sowohl bei den Versuchen mit Bügelproben als auch bei den Versuchen mit Zugproben nicht festgestellt.
Translated Abstract
Investigations on stress corrosion cracking resistivity of stainless steels with different degree of cold straining
Within the context of the elaboration of a new approval for stainless steels for civil engineering applications the question arised whether cold straining could adversely affect the resistance against stress corrosion cracking. By means of experimental tests with different stainless steels it should be clarified whether cold straining increase the stress corrosion cracking susceptibility under high chloride loads like e.g. in swimming hall atmospheres.
The investigations were carried out using the high-alloyed steels 1.4462 and 1.4529. As reference material with known susceptibility against stress corrosion cracking the steel 1.4301 was used. The tests were performed using U-bent and tension specimens with saturated MgCl2 salt spots. Indications for an increase in stress corrosion cracking susceptibility of the cold drawn steel were not found.