Silicate glass fracture surface energy calculated from crystal structure and bond-energy data
(2023)
We present a novel method to predict the fracture surface energy, γ, of isochemically crystallizing silicate glasses using readily available crystallographic structure data of their crystalline counterpart and tabled diatomic chemical bond energies, D0. The method assumes that γ equals the fracture surface energy of the most likely cleavage plane of the crystal. Calculated values were in excellent agreement with those calculated from glass density, network connectivity and D0 data in earlier work. This finding demonstrates a remarkable equivalence between crystal cleavage planes and glass fracture surfaces.
In 1976, a pressure vessel of a tank wagon burst during gravity shunting. The pressure vessel was filled with cold fluid carbon dioxide and failed by cleavage fracture explosively. Big parts of the vessel were flung up to 300 m, a building was destroyed, and rails as well as the superstructure of the gravity shunting yard were damaged.
The initiation sites of the fracture and the orientations of crack propagation were determined by means of the patterns on the fracture surfaces of the broken parts. The initiation sites were located in the heat-affected zone (HAZ) of welds, close to transitions of cross-sections and the starting and end points, respectively, of the welds. The primary initiation of crack propagation was almost certainly on the left side, close to the weld of the fixed bearing connecting the vessel with the carriage.
The results of metallographic investigations indicated the development of cold weld cracks during welding. Mechanical behavior assessments on specimens extracted from the failed vessel indicated sufficient strength and ductility in tensile loading. The values of the notched-bar impact energy or toughness were within the limits according to industry rules and standards, except for one metal sheet of the vessel that was welded to the left fixed bearing.
During shunting, two tank wagons were inappropriately braked, and began to roll too quickly. One rail brake used for deceleration of the wagons caused impulsive noises and vibrations, resulting in high impulsive loading of the first wagon. The cold weld cracks in the heat-affected zones near the fixed bearing of the pressure vessel were initiation points for unstable crack growth. As the result of very low notched-bar impact toughness, crack propagation was not arrested and unstable cleavage fracture occurred.
Due to a second similar accident, happened one year before, a program was started to assess characteristic values of pressure vessel materials and the influence of weld parameters by the manufacturer, the inspecting authority, and BAM. The scientific findings led to modifications of industry rules and standards with regard to using ISO-V specimens and to higher required values for notched-bar impact energy for fine grain structural steels.
Three high-strength Nb-,.Ti- and Ti+ V-bearing S690QL steels were welded to investigate and compare the effects of microalloy addition on heat-affected zone (HAZ) toughness. Charpy V notch impact tests from three microalloyed welds under different cooling rates have been performed. Fractographic examination shows that several factors, including large-sized grain, upper bainite or hard second phase, interact to determine brittle fracture and impaired toughness in Nb-bearing weld with high heat input. In contrast to this reduced toughness, Ti-bearing welds exhibits satisfied toughness regardless of at fast or slow cooling. This is attributed to its limited austenite grain and refines favorable intragranular acicular ferrite structure. Moreover, in the case of such refined structure as matrix, TiN particles are found to be irrelevant to the facture process. The crystallographic results also confirm that high-angle boundaries between fine ferrites plates provide effective barriers for crack propagation and contribute to improved toughness.
The influence of heat input and welding speed on the microstructure and mechanical properties of single-pass hybrid laser arc welded 20mm thick plates of high-strength pipeline steel X120 were presented. The heat Input was varied in the range of 1.4 kJ mm−1 to 2.9 kJ mm−1, while the welding speed was changed between 0.5m min−1 and 1.5m min−1. A novel technique of bath support based on external oscillating electromagnetic field was used to compensate the hydrostatic pressure at low welding velocities. A major advantage of this technology is, that the welding speed and thus the cooling time t8/5 can be variated in a wide parameter window without issues regarding the weld root quality. The recommended welding thermal cycles for the pipeline steel X120 can be met by that way. All tested Charpy-V specimens meet the requirements of API 5 L regarding the impact energy. For higher heat inputs the average impact energy was 144 ± 37 J at a testing temperature of −40 °C. High heat Input above 1.6 kJ mm−1 leads to softening in the weld metal and heat-affected-zone resulting in loss of strength. The minimum tensile strength of 915 MPa could be achieved at heat inputs between 1.4 kJ mm−1 and 1.6 kJ mm−1.