- Sol-gel process (4) (entfernen)
Organisationseinheit der BAM
Transparent dispersions of hydrophobic SrF2 :Eu3+ nanoparticles in cyclohexane with up to 20% europium were obtained by fluorolytic sol-gel synthesis followed by Phase transfer into cyclohexane through capping with sodium dodecylbenzenesulfonate (SDBS). The particles were characterized by TEM, XRD and DLS as spherical objects with a diameter between 6 and 11 nm in dry state. 1H-13CP MAS NMR experiments revealed the binding of the anionic sulfonate head group to the particle surface. The particles show bright red luminescence upon excitation of the aromatic capping agents, acting as antennas for an Energy transfer from the benzenesulfonate unit to the Eu3+ centers in the particles. This synthesis method overcomes the current obstacle of the fluorolytic sol-gel synthesis that transparent dispersions can be obtained directly only in hydrophilic solvents. To demonstrate the potential of such hydrophobized alkaline-earth fluoride particles, transparent luminescent organic-inorganic composites with 10% SrF2 :Eu3+ embedded into polyTEGDMA, polyBMA, poly-BDDMA and polyD3MA, respectively, were prepared, endowing the polymers with the luminescence features of the nanoparticles.
Decay resistance of pine sapwood treated with titanium alkoxide solutions was tested against the brown-rot fungi Coniophora puteana and Poria placenta for exposure times of 10 and 16 wk. In practice, wood-specimens were vacuum-impregnated by alcoholic solutions of titanium alkoxide with concentrations in the range of 5–16 mass % (solid content in solution) and subsequently cured under different humidity conditions. Results reveal that treated wood degraded up to 5% in comparison to untreated one that deteriorated 38% and 50%, respectively against both wood-decay fungi. Even full protection (mass loss below 3%) was achieved against brown rot with titanium alkoxide solution containing solid content of around 5 mass% with a weight percentage gain (WPG) of 9 mass%. With increased concentration, fungal resistance decreased slightly which was associated with more cracks and imperfections formed in the deposited layers of titanium dioxide in the adjacent wood matrix. Thermal analysis verified that a considerable amount of precursor remained in the wood structure as un-hydrolyzed organic residues. These organics, being bioactive, had the tendency to induce similar fungicidal effects as those of conventional fungicides. The amount of organic residues is correlated with the decay resistance of the tested samples. In a prolonged decay test, mass losses of 16-wk incubated samples do not show behavior different from that of the wood samples incubated for 10 wk. This result implies that the decay protection is permanent and confirms further the fungicidal activity of titanium-alkoxide-treated wood.
The role of Fe3+ ions in the transformations from boehmites and pseudoboehmite xerogels via transition aluminas to corundum was studied here. Especially, the active iron species responsible for the decrease of the temperature of transformation to corundum were looked for. To enable the formation of various Fe3+
and Fe2+ species, samples were subjected to thermal treatments in different atmospheres as well as mechanically activated. Thermal analysis and ESR spectroscopy served to follow the processes and to characterise the resulting products. It was found that (i) isolated Fe3+ ions can indicate local structural changes but have (almost) no influence on the temperature of corundum formation, (ii) the temperature of corundum formation decreases in the result of action of small
α-Fe2O3 particles and (iii) during thermal treatments Fe3+ ions are distributed between different phases or precursors thereof: transition aluminas, corundum, Fe2O3, and a Fe3+ pool.