Stiffness variation in the interphase of amine-cured epoxy adjacent to copper microstructures
(2007)
In an effort to expand the understanding of the mechanical properties of the polymeric interphase on a metal surface, a composite consisting of epoxy and copper was prepared and analyzed. Scanning force microscopy-based force modulation microscopy (SFM-FMM) was employed along with dynamic mechanical analysis (DMA) and energy dispersive X-ray analysis (EDX). Diglycidyl ether of bisphenol A (DGEBA)-based epoxy resins were applied with amine curing agents. The samples were made taking advantage of electron beam lithography (EBL) in order to produce sharp edges of copper structures and a flat surface suitable for the SFM-FMM analysis, which was able to depict the stiffness within the interphase. It is considered significant information because the mechanical characteristic within the narrow interphase was revealed. Comparing with DMA and EDX, the stiffness information of SFM-FMM demonstrated a matching correlation and agreement in terms of preferential adsorption of the curing agent in the vicinity of the interface. The stiffness profiles of the two epoxy systems turned out to be different, and it shows the material dependence of the interphase characteristics.
Scanning force microscopy (SFM) has been used to assess the local mechanical properties of fibre-reinforced polymers. Using a sinusoidal displacement modulation (DM) and lock-in technique the method allows to characterize local viscoelastic properties with a high lateral resolution. The simultaneous measurement of the local electrical conductivity is proposed which facilitates the interpretation of the mechanical data. The investigation of cross-sections perpendicular to the axis of carbon fibres embedded in PPS delivers some information about the change in local stiffness within the interfacial region. As a first approach, assuming a single-exponential decrease in local stiffness along a radial line from fibre to polymer we find characteristic decay lengths which are distributed in a range between 20 and 80nm. Further, a modified DM-mode is proposed which is expected to provide a contrast enhancement of the signal which is related to local stiffness. This can be achieved by installing an additional feedback loop which keeps constant the amplitude of dynamic indentation (CDI-mode).