Relation between crack opening and extent of the damage induced at the steel/mortar interface
(2018)
Cracks are inevitable in reinforced concrete structures and promote the diffusion of aggressive agents towards the reinforcement. In Eurocodes, for some exposure conditions, a threshold not to be exceeded for crack width near the rebar is recommended in order to limit risks of corrosion development and ensure structure durability. On the other hand, several studies show that the steel/mortar interface quality at the intersection with a crack strongly influences corrosion development. The aim of this study was therefore to test whether a relation exists between the extent of mechanical damage at the interface and the corresponding residual crack opening. To this end, specimens were cracked using three point bending test apparatus and the evolution of crack opening was determined on the outer surface and deep within the specimen. It was observed that the crack opening measured on the outer surface of the specimen was very close to that measured at various depths within the specimen at the same height level. In addition, the length of the mechanically damaged interface was determined for each residual crack opening.
It was deduced that cracks induced significant steel/mortar Interface damage independently of the size of their openings. The length of the mechanically damaged interface increased proportionally to the residual crack opening without showing marked variation after a certain crack opening value.
Based on the observed results, it is deduced that defining thresholds on crack openings is logical for esthetic reasons but is not articularly relevant for corrosion risk assessment.
Performance of calcium phosphate cements in the augmentation of sheep vertebrae - An ex vivo study
(2021)
Oil-based calcium phosphate cement (Paste-CPC) shows not only prolonged shelf life and injection times, but also improved cohesion and reproducibility during application, while retaining the advantages of fast setting, mechanical strength, and biocompatibility. In addition, poly(L-lactideco-glycolide) (PLGA) fiber reinforcement may decrease the risk for local extrusion. Bone defects (diameter 5 mm; depth 15 mm) generated ex vivo in lumbar (L) spines of female Merino sheep (2–4 years) were augmented using: (i) water-based CPC with 10% PLGA fiber reinforcement (L3); (ii) Paste-CPC (L4); or (iii) clinically established polymethylmethacrylate (PMMA) bone cement (L5). Untouched (L1) and empty vertebrae (L2) served as controls. Cement performance was analyzed using micro-computed tomography, histology, and biomechanical testing. Extrusion was comparable for Paste-CPC(-PLGA) and PMMA, but significantly lower for CPC + PLGA. Compressive strength and Young’s modulus were similar for Paste-CPC and PMMA, but significantly higher compared to those for empty defects and/or CPC + PLGA. Expectedly, all experimental groups showed significantly or numerically lower compressive strength and Young’s modulus than those of untouched controls. Ready-to-use Paste-CPC demonstrates a performance similar to that of PMMA, but improved biomechanics compared to those of water-based CPC + PLGA, expanding the therapeutic arsenal for bone defects. O, significantly lower extrusion of CPC + PLGA fibers into adjacent lumbar spongiosa may help to reduce the risk of local extrusion in spinal surgery.
X-ray computed microtomography for the study of the soil-root relationship in grassland soils
(2013)
We present results from the analysis of three-dimensional X-ray computed tomography images of undisturbed soil samples in grassland sites. A strong positive correlation between root parameters and the solid surface/solid volume ratio was found. Preliminary analyses suggest that the relationship between soil structure and root patterns is related to the intensity of land management at the grassland sites, with reduced root volumes at sites with increased land use intensity.
The exploration of soil structure and its consequences for ecological functions is of prime importance for understanding of the 'critical zone.' In soils, the relationship between soil structure and plant roots—which influences water dynamics in soil—deserves special interest. With X-ray computed microtomography (micro-CT), soil structure and roots may be visualized and quantified simultaneously. We analyzed undisturbed soil samples from three grassland sites. After scanning the soil cores with an X-ray micro-CT scanner (resolution 40 µm), roots were delineated from the soil material and soil pore space by means of their X-ray grey value characteristics followed by the use of space transformation during image analyses. To determine efficacy of the X-ray micro-CT to identify roots, root volumes and surfaces were quantified with a standard root washing method showing good correspondence. A strong positive correlation between root volume and surfaces and the solid surface/solid volume ratio was found, with greater root growth in a more aggregated and porous soil. Preliminary analyses suggest that the relationship between soil structure and root patterns is related to the intensity of land management at the grassland sites, with reduced root volumes and surfaces at sites with increased land use intensity. This methodology has substantial potential for further research on management influences on soil structure and root growth across landscapes.
Corrosion is the major degradation pathway affecting reinforced concrete structures. In the long-term, the rust layer might become thick and slow down the diffusion of oxygen from the atmosphere to the steel. With this in mind, the mineralogy, microstructure and diffusion properties of an old and thick corrosion product layer were investigated. Despite the presence of macropores, the gas diffusion coefficient was found to be low. The impact of the layer on the oxygen diffusion was evaluated using Fick’s law. The results showed that the layer could reduce the flux of oxygen only in a specific configuration.
Material extrusion of thermoplastic polymers enables the realization of complex specific designs with high performance composites. The present study aims at evaluating the mechanical properties of carbon fiberreinforced semi-crystalline thermoplastic polymer polyether ether ketone (CFR-PEEK) manufactured by material extrusion and correlating them with results obtained by micro-CT. Samples in the shape of small bars were provided by Kumovis (Munich, Germany). The determination of surface roughness and density was followed by three-point bending tests. To reveal the pore distribution as well as the fusion quality of CFR PEEK when applied with external forces, micro-CT scans were performed with an X-ray microscope before and after the mechanical test to localize the sites where the fracture is generated. The density of CFR-PEEK bars indicated that they had superior mechanical properties compared with our previous study on unfilled 3D printed PEEK (bending modulus: (5.4 ± 0.5) GPa vs. (1.05 ± 0.05) GPa to (1.48 ± 0.10) GPa; bending strength: (167 ± 11) MPa vs. (51 ± 15) to (193 ± 7) MPa). Micro-CT analyses revealed the local 3D-distribution of voids. Voids of 30 μm diameter are nearly spherical and make up the main part of the total porosity. The larger the voids, the more they deviate from a spherical shape. Significant lack-of-fusion voids are located between the deposited filaments. By growing and merging, they act as seeds for the forming fracture line in the region of the flexural specimens where the maximum local tensile stresses occurred under bending load. Our work provides a detailed analysis of printed PEEK with fiber additive and relates this with mechanical properties.