We report on a new series of isoreticular frameworks based on zinc and 2-substituted imidazolate-4-amide-5-imidate (IFP-1–4, IFP=imidazolate framework Potsdam) that form one-dimensional, microporous hexagonal channels. Varying R in the 2-substitued linker (R=Me (IFP-1), Cl (IFP-2), Br (IFP-3), Et (IFP-4)) allowed the channel diameter (4.0–1.7 Å), the polarisability and functionality of the channel walls to be tuned. Frameworks IFP-2, IFP-3 and IFP-4 are isostructural to previously reported IFP-1. The structures of IFP-2 and IFP-3 were solved by X-ray crystallographic analyses. The structure of IFP-4 was determined by a combination of PXRD and structure modelling and was confirmed by IR spectroscopy and 1H MAS and 13C CP-MAS NMR spectroscopy. All IFPs showed high thermal stability (345–400°C); IFP-1 and IFP-4 were stable in boiling water for 7 d. A detailed porosity analysis was performed on the basis of adsorption measurements by using various gases. The potential of the materials to undergo specific interactions with CO2 was investigated by measuring the isosteric heats of adsorption. The capacity to adsorb CH4 (at 298 K), CO2 (at 298 K) and H2 (at 77 K) at high pressure were also investigated. In situ IR spectroscopy showed that CO2 is physisorbed on IFP-1–4 under dry conditions and that both CO2 and H2O are physisorbed on IFP-1 under moist conditions.
Multifunctional efficiency: Extending the concept of atom economy to functional nanomaterials
(2018)
Green chemistry, in particular, the principle of atom economy, has defined new criteria for the efficient and sustainable production of synthetic compounds. In complex nanomaterials, the number of embedded functional entities and the energy expenditure of the assembly process represent additional compound-associated parameters that can be evaluated from an economic viewpoint. In this Perspective, we extend the principle of atom economy to the study and characterization of multifunctionality in nanocarriers, which we define as “multifunctional efficiency”. This concept focuses on the design of highly active nanomaterials by maximizing integrated functional building units while minimizing inactive components. Furthermore, synthetic strategies aim to minimize the number of steps and unique reagents required to make multifunctional nanocarriers. The ultimate goal is to synthesize a nanocarrier that is highly specialized but practical and simple to make. Owing to straightforward crystal engineering, metal−organic framework (MOF) nanoparticles are an excellent example to illustrate the idea behind this concept and have the potential to emerge as next-generation drug delivery systems. Here, we highlight examples showing how the combination of the properties of MOFs (e.g., their organic−inorganic hybrid nature, high surface area, and biodegradability) and induced systematic modifications and functionalizations of the MOF’s scaffold itself lead to a nanocarrier with high multifunctional efficiency.
Surface-supported metal-organic frameworks HKUST-1 (Hong Kong University of Science and Technology) were used as a model system for a development of a near ambient pressure (NAP) XPS based approach to investigate interaction with atmospheres of water, methanol or pyridine at pressures ranging from 1 to 4 mbar. The films were grown on a gold substrate functionalized with a COOH-terminated self-assembled monolayer using liquidphase epitaxy in a step-by-step fashion. Measurement protocols were developed and optimised for different gases in order to obtain spectra of similar quality in terms of signal intensity, noise and shape. Peak shapes were found to depend on the efficiency of charge compensation. Reference measurements in argon proved to be a useful strategy not only for the evaluation of the Cu(II)-fraction in pristine samples, but also to identify the contributions by the respective gas atmosphere to the C 1s and O 1s photoelectron spectra. Reduced copper was found during the exposition of HKUST-1 to water vapour and pyridine, but this effect was not observed in case of methanol. Additionally, it was established that there are no changes in relative Cu(II) percentage with increasing exposure time. This indicates that saturation was reached already at the lowest time of gas exposure. A detailed elucidation of the mechanism of Cu(II) reduction to Cu(I) in HKUST-1 mediated by water and pyridine is part of ongoing work and not in the scope of the present paper.
The compound MOF-14 (Cu3(BTB)2, BTB = 4,4',4''-benzenetribenzoate) was synthesized by ball milling and characterized by powder X-ray diffraction (XRD). The raw material was activated using an efficient single washing step to ensure a free pore access. Nitrogen adsorption measurements were carried out to determine the specific areas of the samples before and after activation. To interpret the activation process in terms of blocking effects in the micropore channels, NLDFT evaluations (Nonlocal Density Functional Theory) of the MOF-14 nitrogen isotherms were carried out. In connection with the appearance of additional hysteresis loops in the nitrogen isotherms, calculations of the mesopore size distribution were performed using the method of Barret, Joyner, and Halenda (BJH). The results are compared to those of a structurally analogue MOF, namely HKUST-1 (Cu3(BTC)2, BTC = 1,3,5-benzenetricarboxylate). This comparison showed notable differences regarding the impact of the activation step on the formation of mesopores and their size distribution.
The strategy of utilizing mechanochemical synthesis to obtain metal–organic frameworks (MOFs) with high surface areas is demonstrated for two model systems. The compounds HKUST-1 (Cu3(BTC)2, BTC = 1,3,5-benzenetricarboxylate) and MOF-14 (Cu3(BTB)2, BTB = 4,4',4''-benzenetribenzoate) were synthesized by ball milling and characterized by powder X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy (SEM) and thermal analysis (DTA/DTG/MS). The specific surface area (SSA) of both compounds was characterized by nitrogen adsorption. To verify these results and to understand how the synthetic conditions influence the pore structure and the surface area, additional small-angle X-ray scattering (SAXS) experiments were carried out. Our investigations confirm that this synthesis approach is a promising alternative method for distinct MOFs. This facile method leads to materials with surface areas of 1713 m²/g, which is comparable to the highest given values in the literature for the respective compounds.
In order to identify the best porous materials for the cryogenic physisorption of hydrogen, high-throughput calculations are performed starting, i.e., from the collected information in crystallographic databases. However, these calculations, like molecular simulations, require specific training and significant computational cost. Herein, a relatively simple procedure is proposed to estimate and compare hydrogen uptakes at 77 K and pressure values from 40 bar starting from the porous properties of MOF materials, without involving simulation tools. This procedure uses definitions for adsorption and considers the adsorbed phase as an incompressible fluid whose pressure-density change is that for the liquid phase at 19 K. For the 7000 structures from the CoRE MOF database, the average error of the predictions is only of 1% from reference values at 100 bar, with an SD of ±8%. This accuracy is lower than that from simulation tools, but involving lower computational cost and training.