The permeation of hydrogen gas was studied in meta-aluminous (tectosilicate) glass powders of Li2O×Al2O3×SiO2 (LAS), Na2O×Al2O3×SiO2 (NAS) and MgO×Al2O3×SiO2 (MAS) systems by pressure loading and vacuum extraction in the temperatures range 210–310 °C. With this method, both the solubility S and the diffusivity D were determined, while the permeability was given by the product SD. For all glasses, S was found to decrease with temperature, while D increased. Since the activation energy of diffusion of H2 molecules exceeded that of dissolution, permeation increased slightly with temperature. When extrapolated to standard conditions (25 °C), the permeability of tectosilicate glasses was found to be only 10-22–10-24 mol H2 (m s Pa)-1, which is 8–10 magnitudes lower than most polymers. Thin glass liners of these compositions are expected to be the most effective barrier for tanks of pressurised hydrogen.
The influence of interfacial pH between AISI 4135 steel and seawater under different polarization potentials on the formation of calcareous deposits has been studied. An interfacial pH of 9.61 at −0.9 V vs. SCE using state of the art iridium oxide microelectrode was found to be the critical pH for the precipitation of magnesium hydroxide. Calcareous deposits with a double-layer structure comprising an inner-brucite layer and an outer-aragonite layer were found to form at potentials between −1.0 V and −1.2 V vs. SCE. Furthermore, the facilitation of hydrogen permeation into steel induced by the formation of calcareous deposits was verified using the Devanathan-Stachurski electrochemical test. The mechanism of calcareous deposits facilitates hydrogen permeation into steel is related to its inhibition on hydrogen recombination and escape processes.