Hydrogen-Containing Amorphous Carbon Layers as Optical Materials in the Near-IR Spectral Range
(2007)
Hydrogenated amorphous carbon layers were deposited on various substrates by means of a plasma CVD process with a RF substrate bias as well as an ECR plasma source. The optical properties of the a-C:H layers were obtained via spectroscopic ellipsometry and correlated with their mechanical and chemical properties. The layers from pure RF plasma exhibit a higher absorption constant in the visible spectral range and a higher refractive index. All layers are nearly transparent in the NIR spectral range making them candidates for optical thin layer systems. The laser damage behaviour of the a-C:H layers was investigated with ultrashort pulses. The damage thresholds were consistent with the absorption constants of the layers. Interesting damage morphologies were observed indicating a sensitivity of this experiment to sub-structures in the layer.
The friction and wear behaviour of thin hard coatings, such as TiN and the promising class of C-based coatings (a-C, a-C:H, and diamond for example), are compared under oscillating and reciprocating sliding conditions. The typical effects of test parameters, such as stroke, frequency, normal force, relative humidity and test duration, are described as a basis for the proper selection of test conditions or, conversely, for the selection of suitable coatings for particular practical applications.
Friction and wear data from over 1000 vibrating tests using thin hard coatings against 100Cr6 and against Al2O3 have been compiled in a database. This allows easy manipulation and comparison of test results. Using selection criteria and filter procedures (e. g., lifetime of coatings, friction limits, and critical wear rate), suitable coating systems for different test conditions can be chosen from the database. The effects of test parameters on friction and wear behaviour and changes have anyway to be known for meaningful tribotesting, as well as for the selection of coatings.