Cracks perpendicular to the surface may be initial indicators for a deterioration process of concrete structures. Moisture penetrates inside the structure and transports adverse chemicals. The paper presents an investigation about the reliability of available commercial non-destructive evaluation techniques to reliably estimate the depth of surface-breaking cracks in reinforced concrete structures. Aim of the study was the investigation of surface-braking cracks under laboratory conditions. Commercial acoustic devices as impact echo equipment, single ultrasonic transducers and arrays were applied even if they have not been developed for this purpose. The commercial software and descriptions for application was followed strictly to compare the function, precision and repeatability of the measurements. Both, perpendicular notches and cracks have been considered. The study was completed with a discussion about reference specimens. The study was the basis for formulation of gaps in research. The Electric Power Research Institute (EPRI) has initiated and funded a Project.
The corner echo is a well-known effect in ultrasonic testing, which allows detection of surface breaking cracks with predominantly perpendicular orientation to the surface as, for example, corrosion cracks in metal pipes or shafts. This echo is formed by two planes, the surface of the crack and the surface which the crack breaks. It can also be classified as a half-skip method, since a reflection of the pulse occurs on the backwall before the reflection at the defect takes place. In combination with the diffraction from the crack tip, the corner echo also allows crack sizing. As shown in this paper, the corner reflection can be used in civil engineering for nondestructive inspection of concrete. Commercially available low frequency ultrasonic arrays with dry point contact sources generate SH transversal waves with sufficient divergence of the sound field in order to detect corner reflections. Ultrasonic line-scans and area-scans were acquired with a linear array on flat concrete specimens, and the data were reconstructed by the Synthetic aperture focusing technique. If the angles and the area of reconstruction are chosen accordingly, the corner echo reflection can be distinguished from other ultrasonic information. The corner echo can thus be used as a method for deciding whether a crack is a partial-depth crack or a full-depth crack and thus for obtaining a statement about crack depth. This paper presents corresponding experimental results obtained on concrete specimens with artificial test defects and cracks induced under controlled conditions.