Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (23) (entfernen)
Sprache
- Englisch (23)
Schlagworte
- Catalysis (23) (entfernen)
Organisationseinheit der BAM
- 6 Materialchemie (11)
- 6.3 Strukturanalytik (6)
- 6.0 Abteilungsleitung und andere (3)
- 6.1 Oberflächen- und Dünnschichtanalyse (3)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (3)
- 3 Gefahrgutumschließungen; Energiespeicher (2)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (2)
- 9 Komponentensicherheit (1)
- 9.2 Versuchsanlagen und Prüftechnik (1)
Spectroscopy in Catalysis
(2020)
Knowledge-based catalyst development is always an interaction between preparation, analysis and catalytic testing. Only if these three factors fit together can success be expected. For the analytic side of this triangle, spectroscopic methods play a crucial role. Whereas with diffraction, scattering and microscopy, decisive insights into the structure and morphology of the catalysts can be obtained, spectroscopy produces new knowledge about the chemical nature of the catalyst, e.g., its bonding and valence states.
Using solid catalysts in disulfide-based dynamic combinatorial solution- and mechano-chemistry
(2022)
We here show for the first time that solid amines can act as catalysts for disulfide-based dynamic combinatorial chemistry by ball mill grinding. The mechanochemical Equilibrium for the two disulfide reactions studied is reached within one to three hours using ten different amine catalysts. This contrasts with the weeks to months to achieve solution equilibrium for most solid amine catalysts at 2%M at 2mM concentration in a suitable solvent. The final mechanochemical equilibrium is independent of the catalyst used, but varies with other ball mill grinding factors such as the presence of traces of solvent. The different efficiencies of the amines tested are discussed.
Efficient water electrolysis requires electrode coatings with high catalytic activity. Platinum efficiently catalyzes the hydrogen evolution reaction in acidic environments, but is a rare and expensive metal. The activity achieved per metal atom can be increased if small Pt particles are dispersed onto electrically conductive, highly accessible and stable support materials.
However, the addition of Nafion, a typical binder material used in the manufacture of electrode coatings, can decrease catalytic activity by the blocking of pores and active surface sites. A new approach is reported for the direct synthesis of highly active Nafion-free Pt/C catalyst films consisting of small Pt nanoparticles supported in size-controlled mesopores of a conductive carbon film. The synthesis relies on the co-deposition of suitable Pt and C precursors in the presence of polymer micelles, which act as pore templates. Subsequent carbonization in an inert atmosphere produces porous catalyst films with controlled film thickness, pore size and particle size. The catalysts clearly outperform all Nafion-based Pt/C catalysts reported in the literature, particularly at high current densities.
The influence of zeolite support materials and their impact on CH4 oxidation activity was studied utilizing Pd supported on H-beta and H-SSZ-13. A correlation between CH4 oxidation activity, Si/Al ratio (SAR), the type of zeolite framework, reduction-oxidation behaviour, and Pd species present was found by combining catalytic activity measurements with a variety of characterization methods (operando XAS, NH3-TPD, SAXS, STEM and NaCl titration). Operando XAS analysis indicated that catalysts with high CH4 oxidation activity experienced rapid transitions between metallic- and oxidized-Pd states when switching between rich and lean conditions. This behaviour was exhibited by catalysts with dispersed Pd particles. By contrast, the formation of ion-exchanged Pd2+ and large Pd particles appeared to have a detrimental effect on the oxidation-reduction behaviour and the conversion of CH4. The formation of ion-exchanged Pd2+ and large Pd particles was limited by using a highly siliceous beta zeolite support with a low capacity for cation exchange. The same effect was also found using a small-pore SSZ-13 zeolite due to the lower mobility of Pd species. It was found that the zeolite support material should be carefully selected so that the well-dispersed Pd particles remain, and the formation of ion-exchanged Pd2+ is minimized.
Influence of Sb on the structure and performance of Pd-based catalysts: An X-ray spectroscopic study
(2017)
Combined X-ray photoelectron and absorption fine spectroscopy (XAFS) investigations on 10 wt % Pd–16 wt % Sb/TiO2 catalyst allow new insight into the impact of the co-component Sb on the active Pd species, which catalyzes the gas-phase acetoxylation of toluene to benzyl acetate. Ex situ Pd 3d XPS and Pd L-edge XANES studies indicate the presence of an excess electron charge on metallic Pd species (more 4d electrons than in Pd metal) formed after several hours of stream. This observation was explained by the electron transfer from metallic Sb incorporated into the Pd bulk to the neighboring Pd atoms. TEM-EDX analysis confirms the presence of intermixed Pd–Sb particles with an atomic ratio of between 5 and 6 in the most active catalysts and of 3 in deactivated samples. In situ Sb-K-edge XAFS investigations provide evidence that the Pd–Sb interaction is more pronounced under reaction feed than in the ex situ samples.
Solgel prepared ternary FeF3–MgF2 materials have become promising heterogeneous catalysts due to their porosity and surface Lewis/Brønsted acidity (bi-acidity). Despite the good catalytic performance, nanoscopic characterisations of this type of material are still missing and the key factors controlling the surface properties have not yet been identified, impeding both a better understanding and further development of ternary fluoride catalysts. In this study, we characterised the interaction between the bi-acidic component (FeF3) and the matrix (MgF2) on the nano-scale. For the first time, the formation pathway of FeF3–MgF2 was profiled and the template effect of MgF2 during the synthesis process was discovered. Based on these new insights two novel materials, FeF3–CaF2 and FeF3–SrF2, were established, revealing that with decreasing the atomic numbers (from Sr to Mg), the ternary fluorides exhibited increasing surface acidity and surface area but decreasing pore size. These systematic changes gave rise to a panel of catalysts with tuneable surface and bulk properties either by changing the matrix alkaline earth metal fluoride or by adjusting their ratios to Fe or both. The template effect of the alkaline earth metal fluoride matrix was identified as the most probable key factor determining the surface properties and further influencing the catalytic performance in ternary fluoride based catalysts, and paves the way to targeted design of next-generation catalysts with tunable properties.
A facile and efficient methodology is described for the solvothermal synthesis of size-tunable, stable, and uniform NiCu core–shell nanoparticles (NPs) for application in catalysis. The diameter of the NPs is tuned in a range from 6 nm to 30 nm and to adjust the Ni:Cu ratio from 30:1 to 1:1. Furthermore, the influence of different reaction parameters on the final NPs is studied. The NPs are structurally characterized by a method combination of transmission electron microscopy, anomalous small-angle X-ray scattering, X-ray absorption fine structure, and X-ray photoelectron spectroscopy. Using these analytical methods, it is possible to elucidate a core–shell–shell structure of all particles and their chemical composition. In all cases, a depletion from the core to the shell is observed, with the core consisting of NiCu alloy, surrounded by an inner Ni-rich shell and an outer NiO shell. The SiO2-supported NiCu core–shell NPs show pronounced selectivity of >99% for CO in the catalytic reduction of CO2 to CO using hydrogen as reactant (reverse water–gas shift reaction) independent of size and Ni:Cu ratio.
A route to a ZrF4 catalyst active in room temperature Friedel–Crafts and dehydrofluorination reactions was developed via a fluorolytic sol–gel route, which was followed by a postfluorination step using a stream of CHClF2. The behaviour of different Zr(IV) precursors in a sol–gel reaction with anhydrous isopropanol/HF solution was investigated. The subsequent post-fluorination step was optimised in its temperature ramp and confirmed the necessity of a fluorination of the generated xerogels to obtain catalytic activity. The process is discussed in the context of the analysis of the materials using Brunauer–Emmett–Teller analysis (BET), powder X-ray diffraction (XRD), infrared spectroscopy (IR), thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The local structure of the amorphous catalyst was elucidated by extended X-ray absorption fine structure spectroscopy (EXAFS).
Time-optimized 15N quantitative NMR (qNMR) is described for the precise determination of Lewis and Brønsted site concentrations per gram catalyst, enabling a measurement time reduction of more than a factor of 10. The proof-of-principle is demonstrated for amorphous aluminum hydroxide fluorides with their tunable Lewis to Brønsted functionalities and relevance to highly active and selective heterogeneous catalysis using pyridine as a widely accepted probe molecule for Lewis and Brønsted sites. Two different Lewis centers were found, and reliable site concentrations down to the micromole per gram region can be determined. Furthermore, 1H{15N} REDOR NMR for the acid proton at the Brønsted site yields a distance of the 15N atom of bonded pyridine to this acid proton of (0.112 ± 0.002) nm, such that fast motion/diffusion of the Brønsted site-bonded pyridine at the surface can be excluded.
15N NMR of pyridine has been used to study Lewis and Brønsted sites at the acid surface of magnesium hydroxide fluoride at two different pyridine loadings with ratios of excess pyridine compared to pyridine molecules bound to Lewis and Brønsted sites of about 1:1 (highly loaded) and 0.15:1 (low loaded), respectively. The Lewis and Brønsted sites can be distinguished by the 15N chemical shift of pyridine at about –100 ppm (LPy) and –175 ppm (BPy). In both samples a very broad 15N resonance is found around –88 ppm assigned to weakly adsorbed (excess) pyridine molecules via hydrogen bridges (HPy). Additionally, another signal at about –49 ppm is observed in the highly loaded sample only representing physisorbed pyridine (PPy). A slow chemical exchange process of strongly bound LPy and BPy molecules with excess HPy and PPy molecules can be monitored using 15N exchange NMR. It takes place on a time scale of about 50–100 ms at room temperature. All pyridine molecules have the same 15N T1 and its value increases from 800 ms (highly loaded sample) to 5.3 s (low loading) hinting on changed pyridine mobility depending on the loading level.