Geogenic gases from natural sources, carbon dioxide (CO2) from a geological repository (carbon capture and storage - CCS) or a leaking gas pipeline can present serious risks in industrial and urban areas. To extend the lead time for risk treatment in such critical regions, reliable detection of gases within the shallow subsurface is required to observe critical gas accumulations before degassing into the atmosphere.
A near real-time monitoring approach is introduced to determine the volumetric expansion of a leakinggas in the subsurface. Considering the pressure relaxation with the ambient air pressure, the approach enables the forecasting of the final size of a pressurized gas body in terms of characteristic lengths. According to theoretical basics, such a characteristic length, which enables us to perform a gas (safety) measurement based on a purely geometrical measure, behaves independently of subsurface properties,i.e., it enables a reliable quantification of the escaping gas irrespective of its heterogeneous or changingflow path distribution. A field test for a 10 l/min pinhole leakage injected into a 10 m long, 0.4 m wide, 0.95 m deep soil-filled trench that was equipped with linear sensors shows the lateral-vertical volumetric gas expansion along these sensors, and demonstrates the applicability of the characteristic length approach.
Static immersion tests of potential injection pipe steels 42CrMo4, X20Cr13, X46Cr13, X35CrMo4, and X5CrNiCuNb16-4 at T = 60°C and ambient pressure, as well as p = 100 bar were performed for 700–8000 h in a CO2-saturated synthetic aquifer environment similar to CCS sites in the Northern German Basin (NGB). Corrosion rates at 100 bar are generally lower than at ambient pressure. The main corrosion products are FeCO3 and FeOOH with surface and local corrosion phenomena directly related to the alloy composition and microstructure. The appropriate heat treatment enhances corrosion resistance. The lifetime reduction of X46Cr13, X5CrNiCuNb16-4, and duplex stainless steel X2CrNiMoN22-5-3 in a CCS environment is demonstrated in the in situ corrosion fatigue CF experiments (axial push-pull and rotation bending load, 60°C , brine: Stuttgart Aquifer and NGB, flowing CO2: 30 L/h, +/- applied potential). Insulating the test setup is necessary to gain reliable data. S-N plots, micrographic-, phase-, fractographic-, and surface analysis prove that the life expectancy of X2CrNiMoN22-5-3 in the axial cyclic load to failure is clearly related to the surface finish, applied stress amplitude, and stress mode. The horizontal grain attack within corrosion pit cavities, multiple fatigue cracks, and preferable deterioration of austenitic phase mainly cause fatigue failure. The CF life range increases significantly when a protective potential is applied.
Static immersion tests of potential injection pipe steels 42CrMo4, X20Cr13, X46Cr13, X35CrMo4, and X5CrNiCuNb16-4 at T = 60 °C and ambient pressure, as well as p = 100 bar were performed for 700–8000 h in a CO₂-saturated synthetic aquifer environment similar to CCS sites in the Northern German Basin (NGB). Corrosion rates at 100 bar are generally lower than at ambient pressure. The main corrosion products are FeCO₃ and FeOOH with surface and local corrosion phenomena directly related to the alloy composition and microstructure. The appropriate heat treatment enhances corrosion resistance. The lifetime reduction of X46Cr13, X5CrNiCuNb16-4, and duplex stainless steel X2CrNiMoN22-5-3 in a CCS environment is demonstrated in the in situ corrosion fatigue CF experiments (axial push-pull and rotation bending load, 60 °C, brine: Stuttgart Aquifer and NGB, flowing CO₂: 30 L/h, +/- applied potential). Insulating the test setup is necessary to gain reliable data. S-N plots, micrographic-, phase-, fractographic-, and surface analysis prove that the life expectancy of X2CrNiMoN22-5-3 in the axial cyclic load to failure is clearly related to the surface finish, applied stress amplitude, and stress mode. The horizontal grain attack within corrosion pit cavities, multiple fatigue cracks, and preferable deterioration of austenitic phase mainly cause fatigue failure. The CF life range increases significantly when a protective potential is applied.
Carbon capture and storage (CCS) includes processing of supercritical carbon dioxide (scCO2). The carbon dioxide (CO2) stemming from flue gases contains acid forming impurities, especially in the case of coal fired power plants. In the present work, the mobility and reactivity of acids in supercritical scCO2 was investigated. The corrosive attack of low alloyed carbon steel (material 1.0484) by water (H2O) alone in scCO2 was negligible. Nitric acid (HNO3) was very mobile and corrosive towards the carbon steel while sulfuric acid did not migrate through the scCO2 to react with the steel surface. Hydrochloric acid in scCO2 was very mobile and reactive towards both carbon steel and high alloyed test equipment. Gravimetric analyses revealed a severe material loss after corrosion in the presence of HNO3. Thickness measurements showed localized material losses.