Carbon fiber reinforced polymer (CFRP) specimens with artificial delaminations and with impact damage have been characterized using active thermography with flash excitation. Systematic investigations have been performed in four different experimental configurations of flash lamps and infrared (IR) camera in transmission as well as in reflection alignment. It is shown here that the diffusivities determined for the sound and for the damaged areas give a good measure for damage characterization. Although reflection measurements also give information about defect depth, reflection measurements from only one side are not sufficient for assessing the whole cross section of the specimens. Thus, depending on sample thickness the lateral size of damage could only be determined from reflections measurements from both sides or from transmission measurements. In this paper, measurement accuracy and limits of flash thermography for the investigation of CFRP specimens are presented in detail together with quantitative data concerning the defects.
Carbon nanofibers (CNFs) were functionalized with 3-glycidoxypropyltrimethoxysilane and dispersed into epoxy resin. The chemical modification of CNFs was confirmed by FTIR, SEM, EDX and TGA measurements. After silanization, FTIR showed the existance of epoxy ring; EDX detected Si element; while TGA indicated 1.1 wt.% Si on CNFs. Mechanical properties were analyzed by DMA. Silanized CNFs/epoxy composites demonstrated improved dispersion of CNFs in the matrix, and an enhancement of storage modulus for about 20% compared to the neat matrix, which indicated that the modification of CNFs improved the adhesion between fillers and matrices. DC electrical conductivity of CNFs was reduced about 7-fold compared to the original CNFs due to the silane coating. Accordingly, the composites containing silanized CNFs also had lower electrical conductivity than those containing original CNFs. In spite of decreased electrical conductivity, thermal conductivity of silanized CNFs/epoxy composites was increased due to the surface modification of CNFs.