Mobile Tomographic Computer Aided Radiometry (TomoCAR) is based on the mechanical position control of an X-ray tube in front of an object and the application of a Digital Detector Array (DDA) behind it. Several hundred radiometric projections in small angle steps are acquired during the controlled movement of the X-ray tube along a preselected way. The tomographic or laminographic reconstruction allows the three-dimensional (3D) representation of flaws. A specially designed radiometric detector array with small internal unsharpness and high image contrast was used for visualization and sizing of planar and volumetric defects in austenitic welds in nuclear power plants. A German pilot study was successfully performed on the basis of the European network of inspection and qualification (ENIQ) guidelines. This was the precondition for several applications of TomoCAR in nuclear power stations in Germany and Switzerland.
A versatile computed tomography (CT) system was developed on basis of the TomoCAR design for in situ inspection of large aircraft components under production conditions. A gate based planar computed tomograph was constructed and tested for inspection of the integrity of CFRP stringers, embedded in aircraft fibre composite shells. A probability of crack visibility >90% could be determined.
Novel martensitic filler materials with specially adjusted martensite start temperatures (Ms) can counteract the cooling specific shrinkage due to expansion effects of the weld metal associated with phase transformations. That can be exploited to create compressive residual stresses in the weld and adjacent areas, i.e. beneficial for increasing fatigue strength. The Ms temperature is shifted via the chemical composition, mainly by the alloying elements nickel and chromium, resulting as well in different retained austenite contents. Investigations were made using different Low Transformation Temperature (LTT) alloys with varying nickel content. The resulting phase transformation temperatures were – for the first time – detected using high energy synchrotron diffraction and Single Sensor Differential Thermal Analysis (SS-DTA). Compared to angle dispersive diffraction, energy dispersive diffraction offers the possibility to measure residual stresses of the martensite and austenite phase parallel fast in one experiment up to depths of 100 µm. The residual stresses show significant distributions dependent on Ms temperature. The effect on the cold cracking behaviour of these alloys was investigated using the Tekken test. Results show that cold cracking can be avoided when appropriate contents of retained austenite are existent.
Controlling the level of mostly detrimental residual stresses already during the welding process would be highly attractive as time and cost consuming post processing may be prevented. Therefore, in this study, the approach using suitable alloy concepts with reduced phase transformation temperatures has been evaluated concerning the interactions between transformation temperature, transformation kinetics and resulting residual stresses. Ideal tools for observing these phenomena in-situ are diffraction techniques. For that purpose, a special setup was developed allowing for localized observation of phase transformation kinetics during a real welding process by energy dispersive synchrotron diffraction (EDXRD). In the present work, this setup was successfully applied for the first time in order to characterize a selection of alloys especially designed for residual stress control. The results demonstrate that in-process observation is highly suitable for characterizing and discussing phase transformation sensitive phenomena like residual stress formation. Furthermore, it was proven that residual stresses can be effectively controlled by means of an adjusted alloy design.
Novel martensitic filler materials with specially adjusted martensite start temperatures (Ms) can counteract the cooling specific shrinkage due to expansion effects of the weld metal associated with phase transformations. That can be exploited to create compressive residual stresses in the weld and adjacent areas, i.e. beneficial for increasing fatigue strength. The Ms-temperature is shifted via the chemical composition, mainly by the alloying elements nickel and chromium, resulting as well in different retained austenite contents. Investigations were made using different Low Transformation Temperature (LTT) alloys with varying nickel content. The resulting phase transformation temperatures were — for the first time — detected using high energy synchrotron diffraction and Single Sensor Differential Thermal Analysis (SS-DTA). Compared to angle dispersive diffraction, energy dispersive diffraction offers the possibility to measure residual stresses of the martensite and austenite phase parallel fast in one experiment up to depths of 100 μm. The residual stresses show significant distributions dependent on the Ms-temperature. The effect on the cold cracking behaviour of these alloys was investigated using the Tekken test. Results show that cold cracking can be avoided when appropriate contents of retained austenite are existent.
Single-pass solid-state laser welding of plates in the thickness range of 10 to 20 mm became possible with the invention of the fibre laser. This new technique provides excellent beam quality at powers as high as 20 kW or more, and has proved applicable in several industrial applications. By replacing conventional methods with the fibre laser, it is possible to avoid multiple-pass welding that requires time-consuming bevelling. The high energy density of the fibre laser beam also reduces the heat input and consequently the distortion. However, the rapid solidification and cooling associated with laser welding can cause imbalance of the microstructure of duplex stainless steel weldments, where excessively high ferrite contents may reduce the corrosion resistance and the ductility of the material. The solution is normally to add nickel-based filler wire and to increase the heat input. By using a hybrid welding process where the laser beam and the gas metal arc (GMA) process act in a common process zone, filler metal can be added to the molten pool at higher heat input and at the same time, higher welding speed and deeper penetration can be achieved. In this work, 13.5 mm thick 2205 (EN 1.4462, UNS S31803) was fibre laser-GMA hybrid welded in a single-pass using 14 kW of laser power and ISO 22 9 3 N L as filler wire for the GMA process. The resulting welds were free from defects, with smooth surfaces and full penetration. The investigation examines the weld metal microstructure and the effect on corrosion resistance and mechanical properties. The option to add nickel foil, when hybrid welding, was also investigated, as comparison, and the effect on austenite formation was evaluated.