Filtern
Dokumenttyp
- Vortrag (721)
- Beitrag zu einem Tagungsband (210)
- Zeitschriftenartikel (110)
- Posterpräsentation (63)
- Forschungsbericht (11)
- Buchkapitel (7)
- Dissertation (7)
- Sonstiges (6)
- Forschungsdatensatz (4)
- Monografie (3)
Sprache
- Englisch (698)
- Deutsch (440)
- Russisch (5)
- Spanisch (2)
- Mehrsprachig (1)
Referierte Publikation
- nein (1146) (entfernen)
Schlagworte
- Additive Fertigung (94)
- Additive Manufacturing (77)
- Additive manufacturing (69)
- Eigenspannungen (64)
- Hydrogen (64)
- Laser beam welding (64)
- Welding (62)
- Wasserstoff (52)
- Schweißen (43)
- Hochfester Stahl (42)
Organisationseinheit der BAM
- 9 Komponentensicherheit (1146) (entfernen)
Paper des Monats
- ja (1)
Low Transformation Temperature (LTT)-Schweißzusätze stellen einen innovativen Ansatz zur Erhöhung der Ermüdungsfestigkeit geschweißter Konstruktionen dar. LTT-Schweißzusätze zeichnen sich durch eine martensitische Phasenumwandlung nahe der Raumtemperatur aus, welche Druckeigenspannungen in der Schweißnaht und der Wärmeeinflusszone (WEZ) generieren.
Dieser Vortrag fokussiert sich auf die gezielte Einbringung zusätzlicher LTT-Lagen an ermüdungskritischen Stellen von konventionell geschweißten Verbindungen. Dies ermöglicht eine ökonomische Anwendung, ohne dass die Schweißnahtintegrität zu stark beeinflusst wird. Die Auswirkungen zusätzlicher LTT-Lagen wurden anhand geschweißter Längssteifen aus hochfestem Stahl hinsichtlich der chemischen Zusammensetzung und der Eigenspannungen untersucht. Unter Variation der Schweißgeschwindigkeit und Abstand zur konventionellen Naht konnten 3 unterschiedliche Nahtausführungen des Chrom-Nickellegierten LTT-Zusatzes bewertet werden.
Die chemische Zusammensetzung wurde mittels OES-Analysen untersucht. Dabei stellte heraus, dass die Aufmischung in allen Varianten sehr ähnlich war trotz teils unterschiedlicher LTT-Volumina. Härtebestimmungen ergaben in allen 3 Varianten eine ähnliche Härte. Daraus lässt sich annehmen, dass die Martensitstarttemperatur bei allen Nahtvarianten ähnlich ist.
Röntgenografische Eigenspannungsmessungen belegen, dass die Eigenspannungen am versa-genskritischen Nahtübergang bei Einsatz von LTT-Schweißzusätzen deutlich abgesenkt werden. Während die konventionelle Schweißnaht Zugeigenspannungen von ca. 350 MPa aufweist, können an den LTT-Nähten teilweise Druckeigenspannungen von bis zu -150 MPa nachgewiesen werden. Je höher der Abstand zur konventionellen Naht und je größer das eingebrachte LTT-Volumen ist, umso stärker sind die Eigenspannungsreduzierungen am Nahtübergang. Da in allen 3 Varianten eine ähnliche Martensitstarttemperatur angenommen werden kann, ist somit die Geometrische Komponente der LTT-Zusatzlage ein entscheidender Faktor für die Eigenspannungsreduzierung.
AbstractPowder Bed Fusion with Laser Beam of Metals (PBF-LB/M) has gained more industrial relevance and already demonstrated applications at a small series scale. However, its widespread adoption in various use cases faces challenges due to the absence of interfaces to established Manufacturing Execution Systems (MES) that support customers in the predominantly data-driven quality assurance. Current state-of-the-art PBF-LB/M machines utilize communication architectures, such as OPC Unified Architecture (OPC UA), Message Queuing Telemetry Transport (MQTT) and Representational State Transfer Application Programming Interface (REST API). In the context of the Reference Architecture Model Industry 4.0 (RAMI 4.0) and the Internet of Things (IoT), the assets, particularly the physical PBF-LB/M machines, already have an integration layer implemented to communicate data such as process states or sensor values. Missing is an MES component acting as a communication and information layer. To address this gap, the proposed Extract Transform Load (ETL) pipeline aims to extract relevant data from the fabrication of each build cycle down to the level of scan vectors and additionally to register process signals. The suggested data schema for archiving each build cycle adheres to all terms defined by ISO/TC 261—Additive Manufacturing (AM). In relation to the measurement frequency, all data are reorganized into entities, such as the AM machine, build cycle, part, layer, and scan vector. These scan vectors are stored in a runtime-independent format, including all metadata, to be valid and traceable. The resulting machine log represents a comprehensive documentation of each build cycle, enabling data-driven quality assurance at process level.
Der Bau von Gründungs- und Turmstrukturen für Windkraftanlagen erfordert den Einsatz moderner, nachhaltiger und ressourcenschonender hochfester Feinkornbaustähle. Durch den Schweißprozess verursachte Schweißnahtfehler sind nicht akzeptabel. Um diese zu beheben, ist das lokale thermische Fugenhobeln mit anschließendem Reparaturschweißen ein gängiges und wirtschaftliches Verfahren. Die hohe Schrumpfbehinderung um die ausgefugte Nut durch das umgebende Gefüge kann zu Rissbildung führen, wenn sich konstruktiv bedingte Spannungen und Eigenspannungen aus der Reparaturschweißung überlagern. Diese Gefahr wird durch die Verschlechterung der Mikrostruktur und der mechanischen Eigenschaften hochfester Stähle während des Schweißreparaturprozesses noch verstärkt.
For the hydrogen-based energy economy of tomorrow, the construction of the necessary infrastructure will play a central role. Most materials used to date, such as welded steels, can be prone to hydrogen embrittlement under certain conditions. This includes the classic delayed cold cracking during welding as well as degradation phenomena during service of components in hydrogen-containing environment. For the evaluation of any hydrogen effect, for example, on the mechanical properties of a welded metallic material, the hydrogen content must be precisely determined. In the case of weld seams, the carrier gas hot extraction (CGHE) according to ISO 3690 is meanwhile state-of-the-art. CGHE is based on accelerated hydrogen degassing due to the thermal activation of hydrogen at elevated temperatures. In addition to the quantification of hydrogen, thermal desorption analysis (TDA) with varying heating rates can be used to determine and evaluate the hydrogen trapping at microstructural defects in the material. For both techniques, experimental and metrological influences must be considered, which have a major effect on the result. For example, ISO 3690 suggests different sample geometries and minimum extraction times for CGHE. This study summarizes the results and experiences of numerous investigations at the Federal Institute for Materials Research and Testing (BAM) with different sample temperatures and geometries (ISO 3690 type B and cylindrical TDA samples) regarding the influence of the sample surface (polished/welded), measurement accuracy depending on the sample volume and the insufficient monitoring of the effect of PI control on the extraction temperature. A deviating extraction temperature from the target temperature can significantly falsify the measurement results. Based on the results, methods are shown which allow the desired extraction temperature to be reached quickly without physically interfering with the measuring equipment. This serves to significantly improve the reliability of the hydrogen measurement through increased signal stability and accelerated hydrogen desorption. In general, an independent temperature measurement with dummy samples is recommended for the heating procedure of choice to exclude possible undesired temperature influences before the measurement. The methods described can be transferred directly to industrial applications
Based on the state-of-the-art research and regulations, the application of the fracture mechanics master curve (MC) concept to ferritic ductile cast iron (DCI) is being investigated in a joint research project between MPA Stuttgart and BAM Berlin. This paper outlines the research approach, the planned investigations and first results of the experimental program.
Dieser Beitrag befasst sich mit der Entwicklung eines wirtschaftlichen und robusten Verfahrens zum Schweißen dicker Stahlbleche. Es werden Ergebnisse für das Fügen von Blechen im Dickenbereich von 25 mm bis 80 mm vorgestellt. Die 30 mm dicken Schweißnähte konnten im Stumpfstoß in zwei Durchgängen unter Verwendung des Laserhybridschweißens und des Unterpulverschweißens (UP) geschweißt werden. Das Laserhybridschweißen wird als Einschweißung mit einer Tiefe von ca. 25 mm ausgeführt. Die UP-Lagen werden auf der gegenüberliegenden Seite des Blechs aufgebracht. Bei richtiger Wahl der Schweißparameter wird der
Nahtquerschnitt durch eine sichere Überlappung beider Lagen geschlossen. Bei Blechdicken über 30 mm ist eine Kantenvorbereitung erforderlich, die eine Ausführung der UP-Fülllagen in Engspalttechnik ermöglicht. Die Vorteile der vorgeschlagenen Prozesskombination liegen darin, dass die Nahtwurzel der Laserhybridnaht nicht geformt werden muss. Defekte in der Wurzel der Laserhybrideinschweißung können durch die UP-Lagen effektiv beseitigt werden. Das Verfahren bietet eine hohe Stabilität des Schweißprozesses in Bezug auf die
Qualität der Blechkanten. Plasmageschnittene Kanten konnten ohne Bindefehler geschweißt werden. Die erreichte Nahtqualität wurde durch zerstörende und zerstörungsfreie Prüfungen bestätigt.
The presentation gives an overview of BAM's activities on processing influences and application properties of MPEAs in the form of joined and machined high and medium entropy alloys (CoCrFeMnNi and CoCrNi). In the case of welding, the focus is on defect-free welded joints with sufficient mechanical properties. In the case of machining, the focus is on the possible influence on the surface quality of the materials through adequate milling parameters. In addition, the hydrogen absorption and diffusion properties as well as the electrochemical corrosion behavior are fundamentally examined.
Die additive Fertigung mittels Schweißverfahren bietet große ökonomische Vorteile für eine ressourceneffiziente Bauteilherstellung. Offene Fragen bezüglich Homogenität, Anisotropie der Schweißgefüge und den damit verbundenen Bauteileigenschaften stehen einer wirtschaftlichen Verarbeitung oftmals im Wege. Finale Bauteilgeometrie und Oberflächengüte erfordern meist komplementäre subtraktive Fertigungsschritte. Werkstoffe für hochbelastbare Komponenten sind oftmals schwer spanbar. In einem Vorhaben der BAM und des ISAF wurde untersucht, wie die Modifikation der AM-Schweißzusätze und das ultraschallunterstützte Fräsen (US) die Zerspanungssituation verbessern. Der vorliegende Artikel stellt wesentliche Zusammenhänge zwischen Legierung, Gefüge und Zerspanung zweier schwer spanbarer Hochleistungslegierungen (FeNi und CoCr) dar. Großes Potenzial zeigte neben dem US die Modifikation mit Zr und Hf bei Zulegierung in das Schweißgut mittels Beschichtung von Massivdrähten bzw. Herstellung von Fülldrähten.