The results reported in this research study are part of a larger EU RFCS (Research Fund for Coal and Steel) project where the aim is to study the fatigue behavior of improved welds in high strength steels by utilizing different improvement techniques. In this particular study LTT (Low Transformation Temperature) weld filler material have been investigated and their possibility to improve the fatigue strength. The characteristic of these filler material is that they undergo phase transformation at temperature close to room temperature which will reduce the tensile residual stress in the weld and in some cases result in compressive residual stresses. Two different LTT alloy compositions have been developed, with different Ms (Martensite Start) temperatures in order to study the amount of tensile/compressive residual stresses produced by these wires. Welding residual stress measurements were carried out by X-ray diffraction technique. Plates with welded longitudinal attachments were fabricated in 700 MPa and 960 MPa steel grades using different LTT filler materials. These specimens were fatigue tested in constant and variable amplitude loading and the fatigue test results were compared with results from specimen welded with conventional weld filler material.
The surface of a titanium alloy (Ti6Al4V) implant material was covered with a bioactive calcium alkali phosphate ceramic with the aim to accelerate the healing and to form a stronger bond to living bone tissue. To fix the ceramic powder we used a femtosecond laser, which causes a thin surface melting of the metal. It is a requirement to prove that the laser irradiation would not reduce the lifetime of implants. Here we present the results of mechanical stability tests, determined by the rotating bending fatigue strength of sample rods. After describing the sample surfaces and their modifications caused by the laser treatment we give evidence for an unchanged mechanical stability. This applies not only to the ceramic fixation but also to a comparatively strong laser ablation.