The status of standardization related to x-ray photoelectron spectroscopy (XPS, ESCA) at ASTM International (Subcommittee E42.03) and ISO (TC 201) is presented and commented upon in a structured manner. The survey also identifies other active bodies, here VAMAS Technical Working Area 2 and the Surface Analysis Working Group at the International Meter Convention, contributing to prestandardization Research and metrology of XPS and reports their specific activities. It is concluded that existing standardization is delivering good practices in the use of XPS and has a high potential to avoid the recently observed erroneous use, misapplications, and misinterpretation by new and inexperienced users of the method—which seems to be the main reason for the “reproducibility crisis” in the field of XPS applications. A need for a more proactive publicizing of international documentary standards by experienced XPS users, specifically those who are involved in standardization, is identified. Because the existing portfolio of standards addressing the use of XPS is not complete, future standardization projects planned or already ongoing are mentioned. The way the standardization bodies are identifying future needs is shortly explained.
The surface chemistry of nanomaterials controls their interaction with the environment and biological species and their fate and is hence also relevant for their potential toxicity. This has meanwhile led to an increasing interest in validated and preferably standardized methods for the determination and quantification of surface functionalities on nanomaterials and initiated different standardization projects within ISO/TC 229 and IEC/TC 113 as well as interlaboratory comparisons (ILCs) of different analytical methods for the quantification of surface coatings by OECD. Here we present the results of a first ILC on the quantification of the amount of amino functionalities on differently sized inorganic nanoparticles done by division Biophotonics and the National Research Council of Canada (NRC) and the PWI 19257 on the Characterization and Quantification of Surface Functional Groups and Coatings on Nanoobjects approved by ISO/TC 229 (WG2) in fall 2022 that will result in a VAMAS study on this topic organized by division Biophotonics. Key words: nanoparticles, surface analysis, surface functional groups, quantification, optical assay, qNMR, VAMAS, standardization, ICL, quality assurance, reference material.
International standards describing reliable protocols will facilitate the commercialization of graphene and related 2D materials. One physico-chemical key property next to flake size and thickness is the chemical composition of the material. Therefore, an ISO standard is under development with X-ray photoelectron spectroscopy having a prominent role. With its information depth of around 10 nm which is the similar length scale as the thickness as of particles of 2D materials consisting of a few monolayer XPS seems to be highly suitable for this purpose. Different sample preparation methods like pressing the powders onto adhesive tapes, into recesses, or into solid pellets result in inconsistencies in the quantification. For the validation of the quantification with XPS an interlaboratory comparison was initiated under the auspice of the “Versailles Project on Advanced Materials and Standards” (VAMAS). First results confirm that the sample preparation method (pellet vs. powder) influences the quantification results clearly. Considering this effect, a good agreement of the results from the different participants were observed. Similar results were observed for raw, N- and F-functionalized graphene.
Since its isolation, graphene has received growing attention from academia and industry due to its unique properties. Promising opportunities for applications are discussed in different field like electronics and optoelectronics, detection, and sensing devices, biosystems or chemical and environmental corrosion inhibition. Here, functionalization with elements like oxygen, nitrogen or fluorine can broaden the application, for example in composite materials. However, lack of generally accepted operation procedures hinders the commercialization, the so-called “what is my material” barrier. Therefore, first efforts were done to develop common, reliable, and reproducible ways to characterize the morphological and chemical properties of the industrially produced material.
In this contribution, our efforts in the development of reliable chemical characterizations protocols for functionalized graphene are presented. An ISO standard for the chemical characterization of graphene-related (GRM) is under development with X-ray photoelectron spectroscopy (XPS) having a prominent role. With its information depth of around 10 nm, which is the similar length scale as the thickness of particles of 2D materials consisting of a few monolayers, XPS seems to be highly suitable for the quantitative analysis of (functionalized) GRM. Thereby, different sample preparation methods like pressing the powders onto adhesive tapes, into recesses, or into solid pellets result in inconsistencies in the quantification. Furthermore, different morphologies like stacks of graphene layers (left figure) or irregular particles (right figure) lead to different analysis results for the chemical composition.
For the validation of the quantification with XPS and the further development of standards an international interlaboratory comparison was initiated under the head of the “Versailles Project on Advanced Materials and Standards” (VAMAS). First results are reported showing the suitability of the protocols. Finally, the XPS results are compared with the elemental composition results obtained after quantification with energy-dispersive X-ray spectroscopy (EDS) as a fast analytical method which is usually combined with electron microscopy.
This paper reports the results of an international interlaboratory study sponsored by the Versailles Project on Advanced Materials and Standards (VAMAS) and led by the National Institute of Standards and Technology (NIST) on the measurement of water vapor sorption isotherms at 25 °C on a pelletized nanoporous carbon (BAM-P109, a certified reference material). Thirteen laboratories participated in the study and contributed nine pure water vapor isotherms and four relative humidity isotherms, using nitrogen as the carrier gas. From these data, reference isotherms, along with the 95% uncertainty interval (Uk=2), were determined and are reported in a tabular format.
A case study on the TEM analysis of the size and shape distribution of TiO2 bipyramidal nanoparticles prepared on TEM grids was included in the recently published ISO standard ISO 21363. It was agreed to organize at a later stage a second inter-lab comparison with the nanoparticles distributed to the participants as a liquid suspension. Protocols for uniform nanoparticle deposition on suited supports developed and optimized within the EMPIR nPSize project are also prepared to be distributed. For this, we have chosen the VAMAS platform (www.vamas.org) which offers an excellent international infrastructure of laboratories with high competence in nanoparticle measurement. The VAMAS technical working area dedicated to nanoparticle measurement is TWA 34 ‘Nanoparticle populations’. For this type of nanoparticles, the size and shape distributions are the primary parameters to be reported. Due to the good deposition protocols developed, an automated image analysis is enabled (in contrast to the manual analysis of irregular TiO2 nanoparticles.
In parallel with the TiO2 nanoparticle exercise, two spherical SiO2 nanoparticle samples with bi-modal size distributions (nominal relative number concentrations of 1:1 and 10:1) are prepared for a second VAMAS inter-lab comparison. Here, the nanoparticle concentration is the primary parameter to be measured. For the imaging methods it is targeted to measure the relative nanoparticle concentrations of the two modes. For the absolute nanoparticle concentration to be measured by imaging methods it is necessary to control the volume of the liquid suspension deposited on the substrate and to obtain such a homogeneous nanoparticle deposition on the substrate which allows to count (or extrapolate) all the deposited particles.
International standardisation network VAMAS is calling for participants in two studies on the measurement of (relative) number concentration of bimodal silica nanoparticles including deposition from liquid suspension and the measurement of particle size and shape distribution of bipyramidal titania including deposition from liquid suspension.