The paper provides an overview on material defects which may serve as fatigue crack initiation sites and can cause final fatigue failure of a component. These comprise nonmetallic inclusions in Steel and aluminum alloys, cavities such as pores, micro-shrinkages and un-welded regions in cast, sinter and additively manufactured alloys, graphite nodules, shrinkages and other items in modular cast iron, regions of defective microstructure, microcracks and secondary notches such as undercuts and surface roughness. Besides their origin, the effect and mechanisms on fatigue crack initiation and propagation are discussed.
The considerations are proceeded and accompanied by a Brief discussion of some Basic aspects such as the stages of crack propagation along their length scale, the overcoming of crack arrest and the question when a secondary notch can be treated as a crack.
Die Charakterisierung von Oberflächen mittels optischer Technologien wird dank des ständigen Fortschritts bei der Entwicklung von Sensoren und Lichtquellen immer attraktiver. Die kommerziell erhältlichen Systeme werden dabei immer leistungsstarker, empfindlicher und genauer. Mit diesen Systemen ist es möglich, viele hundert Messpunkte innerhalb weniger Sekunden zu erfassen und auszuwerten. Dieser Fortschritt führt auch im Baubereich zu einer ständigen Weiterentwicklung und Verbesserung von Messmethoden und Systemen. So werden bereits standardisierte und angewandte Messprinzipien weiterentwickelt, den neuen Möglichkeiten angepasst und deren Anwendung auf neue Bereiche ausgeweitet. An der BAM ist es gelungen ein Messsystem zu entwickeln, mit dem Rautiefen von Bauteiloberflächen in Anlehnung an bereits standardisierte Verfahren bestimmt werden können. Mit dem Mer vorgestellten System können sowohl horizontale als auch vertikale, gewölbte und geneigte Oberflächen untersucht werden. Dank der Implementierung geeigneter Algorithmen entsprechen die vom System ausgegebenen Ergebnisse denen der seit Jahrzehnten mit den volumetrischen Messverfahren erzielten Ergebnisse. Vor allem bei der Instandsetzung von Bauwerken bringt das an der BAM entwickelte System erhebliche Vorteile, da es zukünftig auch möglich sein wird Wände und Decken genauer zu untersuchen.
During laser beam welding of aluminum alloys an electromagnetic field may favour pore outgassing through the top oxide layer. High frequencies cause a small penetration depth and thus exert a stabilizing effect on the weld surface. The point at which the laser beam between the two magnetic poles hits the workpiece surface is crucial to the influence of the magnetic field on the weld surface roughness. Using analyzed parameters for different laser points of application cause a change in weld surface roughness could be observed. The weld surface roughness could be reduced by 50%. The outgassing effect in terms of a reduction of pores could be observed for all parameter sets investigated.
The influence of the surface roughness of pearlitic grey cast iron discs on the formation of tribofilms and the evolution of the friction coefficient during a ring on disc tribotest with the addition of magnetite and magnetite–graphite nanopowders as interfacial media was investigated. The roughness parameters of the cast iron discs were varied by electro discharge machining (EDM) and grinding processes, producing four distinct surface roughness conditions. The evolution of the friction coefficient, however, did not reach the steady state for most of the samples and the role of the surface roughness on the friction coefficient could not be identified. Focused ion beam (FIB) microscopy on the cast iron discs was carried out to investigate the microstructure of the discs near the tribosurface. These results showed that the EDM process not only varied the surface roughness, but also changed the microstructure of the cast iron discs, promoting the incipient fusion of the cast iron surface, with the formation of ridges and casting defects (pores). As a result, a layer of rapidly solidified metal with a dendritic microstructure was formed near to the surface of the EDMed discs.
Processing and cytocompatibility of Cu-doped and undoped fluoride-containing bioactive glasses
(2024)
Sintered or additive-manufactured bioactive glass (BG) scaffolds are highly interesting for bone replacement applications. However, crystallization often limits the high-temperature processability of bioactive glasses (BGs). Thus, the BG composition must combine high bioactivity and processability. In this study, three BGs with nominal molar (%) compositions 54.6SiO2-1.7P2O3-22.1CaO-6.0Na2O-7.9K2O-7.7MgO (13–93), 44.8SiO2-2.5P2O3-36.5CaO-6.6Na2O-6.6K2O-3.0CaF2 (F3) and 44.8SiO2-2.5P2O3-35.5CaO-6.6Na2O-6.6K2O-3.0CaF2-1.0CuO (F3–Cu) were investigated. The dissolution and ion release kinetics were investigated on milled glass powder and crystallized particles (500–600 μm). All glasses showed the precipitation of hydroxyapatite (HAp) crystals after 7 days of immersion in simulated body fluid. No significant differences in ion release from glass and crystalline samples were detected. The influence of surface roughness on cytocompatibility and growth of preosteoblast cells (MC3T3-E1) was investigated on sintered and polished BG pellets. Results showed that sintered BG pellets were cytocompatible, and cells were seen to be well attached and spread on the surface after 5 days of incubation. The results showed an inverse relation of cell viability with the surface roughness of pellets, and cells were seen to attach and spread along the direction of scratches.
Tribological properties of ultrahigh-molecular weight polyethylene (UHMWPE) and cross-linked polyethylene (XLPE) were studied in two different wear modes. Firstly, reciprocating sliding wear studies under non-conformal contact investigated the effects of counterface surface roughness (polished, lapped and ground) of Ti6Al4V on the friction and wear of the polyethylenes. Secondly, two-body abrasive wear studies in conformal contact against different abrasive grit size papers were also carried out to ascertain the wear sensitivity of the polyethylenes under these adverse conditions. Wear mechanisms were studied using optical and scanning electron micrographs. The results of the reciprocating sliding wear studies showed that surface roughness of the counterface influenced friction and wear characteristics although no correlation was found between the coefficient of friction and specific wear rate. XLPE demonstrated wear sensitivity, particularly under severe abrasive wear condition. The results indicated that the performance of the polyethylenes greatly depends upon the tribological system under which it is operating.
Additively manufactured (AM) triply periodic metallic minimum surface structures (TPMSS, from the English Triply Periodic Minimum Surface Structures) fulfill several requirements in both biomedical and engineering fields: tunable mechanical properties, low sensitivity to manufacturing defects, mechanical stability, and high energy absorption. However, they also present some quality control challenges that may prevent their successful application. In fact, optimization of the AM process is impossible without considering structural features such as manufacturing accuracy, internal defects, and surface topography and roughness. In this study, quantitative nondestructive analysis of Ti-6Al-4V alloy TPMSS was performed using X-ray computed tomography (XCT). Several new image analysis workflows are presented to evaluate the effects of buildup direction on wall thickness distribution, wall degradation, and surface roughness reduction due to chemical etching of TPMSS. It is shown that the fabrication accuracy is different for the structural elements printed parallel and orthogonal to the fabricated layers. Different strategies for chemical etching showed different powder removal capabilities and thus a gradient in wall thickness. This affected the mechanical performance under compression by reducing the yield stress. A positive effect of chemical etching is the reduction of surface roughness, which can potentially improve the fatigue properties of the components. Finally, XCT was used to correlate the amount of powder retained with the pore size of the TPMSS, which can further improve the manufacturing process.
Additively manufactured (and in particular laser powder bed fused) materials represent a manyfold challenge for the materials scientist and engineer because of their distinctive microstructure. If laser powder bed fusion is used to produce components, the complexity level increases because meso-structures (e.g., overhanging features, surface and internal defects) gain importance. Furthermore, if the main advantage of additive manufacturing, i.e., the freedom of design, is to be fully exploited, and geometrically complex structures, such as lattices, are manufactured, then such structures become meta-materials. This means that the geometry and the materials properties become equally important.
This matryoshka-like (more literary than the dry “multi-scale”) complexity makes the characterization of the residual stress fields by means of diffraction methods so difficult with the current means, that new paradigms are necessary to tackle the challenge.
Indeed, classic open problems acquire an extra layer of difficulty, such that new solutions need to be found and the sometimes-dormant debate needs to be re-opened. Examples include the determination of: a- the unstrained reference: this reference can become location-dependent and needs to be carefully determined; b- the so-called diffraction elastic constants, which becomes immensely challenging since even the single-crystal elastic constants are not known for additively manufactured materials.
On top of this, other problems arise. The determination of the principal axes of stress becomes non-trivial because the hatching strategy sometimes dominates over the sample geometry. Even further, in complex structures, such as lattices, the textbook statement that the strain measurement in six independent directions uniquely identifies the strain tensor becomes simply invalid. The peculiar surface features of additively manufactured materials transform trivial tasks into formidable challenges: the precise alignment of a specimen in a beam or the determination of surface stresses with laboratory X-rays need to be thoroughly re-discussed and lay far from being routine tasks.
In this paper, we will show a few examples of the cases mentioned above. We will demonstrate that sometimes the classic approach works very well, but other times surprising conclusions can be drawn from in-depth studies of the residual stress in additively manufactured materials. In short, we predicate that classic methods cannot be used on additively manufactured materials and structures without a critical evaluation of their validity and application range.
This paper shows how Angle-Resolved Scattering can reveal wear on engineered surfaces. The samples studied, three discs made of steel 100Cr6H used in gear wheels in the automotive industry, were assessed after they had undergone ball-on-disc tests. Scattering maps recorded for spatial frequencies from 0.1 µm-1 to 2.7 µm-1 show a contrast inversion around 0.36 µm-1 revealing the wear trace. Besides measurements of rms roughness, where mean values are 20 nm and 24 nm depending on the locations considered, stationarity and isotropy, we demonstrate the ability of the technique to reveal localized wear on this type of surface in a rapid, robust and convenient way. We show that the tool trace is influenced by the load magnitude rather than by the number of oscillation cycles and highlight the key role played by surface roughness in how the sample responds to wear tests.
The contour scan strategies in laser powder bed fusion (LPBF) of Ti-6Al-4V were studied at the coupon level. These scan strategies determined the surface qualities and subsurface residual stresses. The correlations to these properties were identified for an optimization of the LPBF processing. The surface roughness and the residual stresses in build direction were linked: combining high laser power and high scan velocities with at least two contour lines substantially reduced the surface roughness, expressed by the arithmetic mean height, from values as high as 30 μm to 13 μm, while the residual stresses rose from ~340 to about 800 MPa. At this stress level, manufactured rocket fuel injector components evidenced macroscopic cracking. A scan strategy completing the contour region at 100 W and 1050 mm/s is recommended as a compromise between residual stresses (625 MPa) and surface quality (14.2 μm). The LPBF builds were monitored with an in-line twin-photodiode-based melt pool monitoring (MPM) system, which revealed a correlation between the intensity quotient I2/I1, the surface roughness, and the residual stresses. Thus, this MPM system can provide a predictive estimate of the surface quality of the samples and resulting residual stresses in the material generated during LPBF.