Results from a study conducted between National Metrology Institutes (NMIs) for the measurements of the absolute thicknesses of ultra-thin layers of SiO2 on Si are reported. These results are from a key comparison and associated pilot study under the auspices of the Consultative Committee for Amount of Substance. ´Amount of substance´ may be expressed in many ways, and here the measurand is the thickness of the silicon oxide layers with nominal thicknesses in the range 1.5-8 nm on Si substrates, expressed as the thickness of SiO2. Separate samples were provided to each institute in containers that limited the carbonaceous contamination to approximately < 0.3 nm. The SiO2 samples were of ultra-thin on (100) and (111) orientated wafers of Si. The measurements from the laboratories which participated in the study were conducted using ellipsometry, neutron reflectivity, X-ray photoelectron spectroscopy or X-ray reflectivity, guided by the protocol developed in an earlier pilot study. A very minor correction was made in the different samples that each laboratory received. Where appropriate, method offset values attributed to the effects of contaminations, from the earlier pilot study, were subtracted. Values for the key comparison reference values (agreed best values from a Consultative Committee study) and their associated uncertainties for these samples are then made from the weighted means and the expanded weighted standard deviations of the means of these data. These results show a dramatic improvement on previous comparisons, leading to 95% uncertainties in the range 0.09-0.27 nm, equivalent to 0.4-1.0 monolayers over the 1.5-8.0 nm nominal thickness range studied. If the sample-to-sample uncertainty is reduced from its maximum estimate to the most likely value, these uncertainties reduce to 0.05-0.25 nm or ~1.4% relative standard uncertainties. The best results achieve ~1% relative standard uncertainty. It is concluded that XPS has now been made fully traceable to the SI, for ultra-thin thermal SiO2 on Si layers, by calibration using wavelength methods in an approach that may be extended to other material systems.
Results are reported from a pilot study under the Consultative Committee for Amount of Substance (CCQM) to compare measurements of and resolve any relevant measurement issues in, the amount of thermal SiO2 oxide on (100) and (111) orientation Si wafer substrates in the thickness range 1.5 - 8 nm. As a result of the invitation to participate in this activity, 45 sets of measurements have been made in different laboratories using 10 analytical methods: medium-energy ion scattering spectrometry (MEIS), nuclear reaction analysis (NRA), RBS, elastic backscattering spectrometry (EBS), XPS, SIMS, ellipsometry, grazing-incidence x-ray reflectrometry (GIXRR), neutron reflectometry and transmission electron microscopy (TEM). The measurements are made on separate sets of 10 carefully prepared samples, all of which have been characterised by a combination of ellipsometry and XPS using carefully established reference conditions and reference parameters.
The results have been assessed against the National Physical Laboratory (NPL) data and all show excellent linearity. The remaining data sets correlate with the NPL data with average root-mean-square scatters of 0.15 nm, half being better than 0.1 nm and a few at or better than 0.05 nm. Each set of data allows a relative scaling constant and a zero thickness offset to be determined. Each method has an inherent zero thickness offset between 0 nm and 1 nm and it is these offsets, measured here for the first time, that have caused many problems in the past. There are three basic classes of offset: water and carbonadeous contamination equivalent to ~1 nm as seen by ellipsometry; adsorbed oxygen mainly from water at an equivalent thickness of 0.5 nm as seen by MEIS, NRA, RBS and possibly GIXRR; and no offset as seen by XPS using the Si 2p peaks. Each technique has a different uncertainty for the scaling constant and consistent results have been achieved. X-Ray photoelectron spectroscopy has large uncertainties for the scaling constant but a high precision and, critically, if used correctly, has zero offset. Thus, a combination of XPS and the other methods allows the XPS scaling constant to be determined with low uncertainty, traceable via the other methods. XPS laboratories returning results early were invited to test a new reference procedure. All showed very significant improvements. The reference attenuation lengths thus need scaling by 0.986 ± 0.009 (at an expansion factor of 2) deduced from the data for the other methods. Several other methods have small offsets and, to the extent that these can be shown to be constant or measurable, then these methods will also show low uncertainty. Recommendations are provided for parameters for XPS, MEIS, RBS and NRA to improve their accuracy.
Analysis methods and instrumentation for obtaining optical parameters and thickness profiles of thin-film samples from spectrophotometric and ellipsometric measurements are presented. Measured samples include thermally grown and evaporated SiO2 on a silicon substrate and a polymer photoresist layer on silicon. Experimental results at multiple sample positions give the thickness uniformity and optical constants of thin films. The thickness results obtained with spectrophotometry and ellipsometry agree within 1 nm for the 300 nm thick layer of SiO2 on silicon. For the 1600 nm thick resist sample the agreement of the measurement methods is within 8 nm. For the sample with a nominally 6000 nm thick layer of SiO2 on silicon, there is a deviation of ~100 nm between the spectrophotometry and ellipsometry results. As an application, the optical parameters of a SiO2 layer on an induced junction silicon photodiode are determined by spectrophotometry and are used to confirm earlier values and uncertainties of the SiO2 refractive index and layer thickness non-uniformity.
Effect of well dispersed amorphous silicon dioxide in flame retarded styrene butadiene rubber
(2013)
Spherically shaped amorphous silicon dioxide with broad size particle distribution was used in combination with aluminium trihydroxide (ATH) in styrene butadiene rubber composites. The pyrolysis, flammability, fire properties, flame spread and gas diffusion were investigated. The kind and amount of ATH, but in particular the fine silicon dioxide chosen as an additive, influenced the thermal decomposition and fire behaviour of styrene butadiene rubber composites. Gravimetric gas sorption measurements showed that the gas diffusion was systematically lower with silicon dioxide. The initial pyrolysis gas release was hindered, increasing the temperature at which decomposition begins as well as the ignition time in fire tests. During combustion, ATH and silicon dioxide accumulate on the surface of the specimen, forming a residual protective layer. A reduced peak heat release rate and fire spread were observed. The addition of a special kind of silicon dioxide is proposed to play a key role in optimising fire retardancy.
Integrated Coating System for Corrosion Protection of Carbon Steel in Artificial Geothermal Brine
(2022)
Corrosive geothermal brines are a major challenge to geothermal power-plants. For cost reasons, plant designers prefer to use carbon and low alloyed steels, which are susceptible to uniform and localized corrosion when exposed to geothermal brines having acidic and saline properties. To solve such problem, coatings or inhibitors would be a protective solution as an alternative to the use of high alloyed materials.
This study investigated a coating system consisting of polyaniline/silicon dioxide based on resources locally available in Indonesia. Protection against corrosion of carbon steel was shown by long-term (28 day) exposure and electrochemical tests of coated carbon steels, performed in an artificial acidic and saline geothermal brine, comparable to the conditions encountered at a site in Indonesia.
Therefore, an integrated coating system is proposed for corrosion protection, combining the electrochemical functionality of polyaniline and the physical advantages of silica.
The thickness measurement of transparent layers with optical techniques is very problematic. The observed deviations can easily reach 100% of the layer thickness to be measured. In order to analyse these deviations, tactile reference measurements have been developed. The proposed method is based on contact mode measurements with low contact pressure. With stylus instruments, this can be realized either by using the recommended tip radius of 2 µm and very small probing forces in the micronewton range (and low scanning speeds of 50 µm s-1) or by using the recommended probing force of 750 µN, but a large probing tip radius. Three metal layers on silicon or silicon dioxide and two polymer resist materials on a thin chromium adhesive layer on silicon are used as artefacts. The comparison of the optical measurements with the tactile reference values disclosed deviations of the optical measurements of up to 195% of the layer thickness. Layer thicknesses were between 200 nm and 4 µm. This paper analyses the deviations of two white light interference microscopes, one phase shift interference microscope, one confocal microscope, one autofocus sensor, a chromatic sensor, an interferometric film thickness sensor and one spectroscopic ellipsometer. Simple and well-known expressions for the description of the observed deviations are presented and discussed. The order of magnitude of the observed deviations can be described well by these correction formulas but further investigations are necessary in order to better understand the systematic deviations of optical surface measuring instruments on non-cooperating surfaces.
Integrated Coating System for Corrosion Protection of Carbon Steel in Artificial Geothermal Brine
(2022)
Corrosive geothermal brines are a major challenge to geothermal power-plants. For cost reasons, plant designers prefer to use carbon and low alloyed steels, which are susceptible to uniform and localized corrosion when exposed to geothermal brines having acidic and saline properties. To solve such problem, coatings or inhibitors would be a protective solution as an alternative to the use of high alloyed materials.
This study investigated a coating system consisting of polyaniline/silicon dioxide based on resources locally available in Indonesia. Protection against corrosion of carbon steel was shown by long-term (28 day) exposure and electrochemical tests of coated carbon steels, performed in an artificial acidic and saline geothermal brine, comparable to the conditions encountered at a site in Indonesia.
Therefore, an integrated coating system is proposed for corrosion protection, combining the electrochemical functionality of polyaniline and the physical advantages of silica.