FR additives were incorporated during tanning process. The mode of action of an intumescent system and each component individually, was methodically investigated in a semi-finished leather. Vertical flammability test results showed that the investigated semi-finished leather satisfies the regulations of the Federal Aviation Administration; in addition, afterglow time is strong minimized and forced fire behavior pointed out an important reduction on smoke production.
Flame retarded polymeric materials are used in various applications in which a certain fire behavior is demanded. Protection goals are defined, such as limited flammability in terms of hindered sustained ignition or limited contribution to a fire, and these protection levels are tested with defined specimens or components in defined fire scenarios, that is to say, different fire tests. Passing a specific fire test by meeting whatever its demands is often the most important development goal, so the parameters of the different fire tests vary widely to emphasize different fire properties. Some fire tests are used to screen or provide a general assessment of flame retardant polymers during development, while other fire tests and tailored experiments are performed to address special phenomena or understand the flame retardancy modes of action. For all fire testing, the devil is in the details – demanding know-how and crucial efforts to manage the quality of investigations and advanced interpretation. This chapter aims to offer a structured overview of all these aspects.
There is little consensus within the fire science community on interpretation of cone calorimeter data, but there is a significant need to screen new flammability modified materials using the cone calorimeter. This article is the result of several discussions aiming to provide guidance in the use and interpretation of cone calorimetry for those directly involved with such measurements. This guidance is essentially empirical, and is not intended to replace the comprehensive scientific studies that already exist. The guidance discusses the fire scenario with respect to applied heat flux, length scale, temperature, ventilation, anaerobic pyrolysis and set-up represented by the cone calorimeter. The fire properties measured in the cone calorimeter are discussed, including heat release rate and its peak, the mass loss and char yield, effective heat of combustion and combustion efficiency, time to ignition and CO and smoke production together with deduced quantities such as FIGRA and MARHE. Special comments are made on the use of the cone calorimeter relating to sample thickness, textiles, foams and intumescent materials, and the distance of the cone heater from the sample surface. Finally, the relationship between cone calorimetry data and other tests is discussed.
The main flame retardant modes of action are well known, but in practise the detailed scientific understanding usually falls short, when it comes to modern multicomponent systems, the important tiny optimizations, or quantifying in terms of specific fire properties. This talk delivers thought-provoking impulses, picking up some overseen details as well as raising basic questions. A detailed scientific insight in flame retardant modes of action much more than an overview is presented.
Melamine resins were used as 50-µm-thick fire retardant coatings for polypropylene (PP). Preceding deposition, low-pressure plasma polymer films of allyl alcohol were coated onto PP to improve the adhesion between PP and melamine resin coatings. The efficiency of such fire retardant coatings was confirmed by flame tests. The plasma-deposited polymer and the dip-coated melamine resin films were characterized by Fourier transform infrared-attenuated total reflectance spectroscopy and X-ray photoelectron spectroscopy (XPS). The adhesion of coatings was measured using a 90° peel test with a doubled-faced adhesive tape. To detect the locus of failure, the peeled layer surfaces were inspected using optical microscopy and XPS. Thermal properties of PP thick melamine resin-coated films were analyzed by thermogravimetric analysis.
Melamine and melamine resins are widely used as fire retardants for polymer materials used in pharmaceutical, plastic, textile, rubber, and construction industry. Melamine-based flame retardants act by blowing off intumescent layers, char formation, and emission of quenching ammonia gas and diluent molecular nitrogen. Special advantages are: low cost, low smoke density and toxicity, low corrosive activity, safe handling, and environmental friendliness. Methylated poly(melamine-co-formaldehyde) (mPMF) was used as thick (≥40 µm) fire-retardant coating for plasma pretreated polymers. A combined low-pressure plasma pretreatment consisting of oxygen plasma exposure followed by deposition of thin poly(allylamine) (ppAAm) and poly(allyl alcohol) (ppAAl) plasma polymers as adhesion promoters have improved the adhesion of thick mPMF coatings strongly. Chemical structure and composition of deposited polymer films were characterized by infrared-attenuated total reflectance and X-ray photoelectron spectroscopy (XPS). After peeling, the peeled layer surfaces were also investigated for identification of the locus of failure and their topography using optical microscopy and XPS. Often the adhesion promotion was so efficient that the peeling of coating was not possible. Thermal properties of plasma polymers and dip-coating films were analyzed by thermogravimetric analysis. Significant improvement of fire-retardant properties of coated polymers was confirmed by flame tests.
Melamine and melamine resins are widely used as fire-retardants for polymer building materials. Cured melamine systems are used in heat-sensitive items, such as furniture and window frames and sills. In this work, differently cured methylated poly(melamine-co-formaldehyde) (cmPMF) resins were used as fire-retardant coverage for poly(styrene) (PS) and poly(ethylene) (PE) building materials. Such polymer layers should have several tenths of micrometers thickness to produce sufficient fire retardancy. These thick layers were produced by dip-coating. To promote sufficient adhesion of such thick coating to the polyolefin substrates, also in the case of high temperatures occurring at fire exposure, the polymer substrates were firstly coated with a few hundred nanometer thick adhesion-promoting plasma polymer layer. Such thin plasma polymer layers were deposited by low-pressure plasma polymerization of allyl alcohol (ppAAl). It was assumed that the hydroxyl groups of ppAAl interact with the melamine resin; therefore, ppAAl was well suited as adhesion promoter for thick melamine resin coatings. Chemical structure and composition of polymer films were investigated using infrared-attenuated total reflectance and X-ray photoelectron spectroscopy (XPS). Peel strengths of coatings were measured. After peeling, the peeled polymer surfaces were also investigated using optical microscopy and XPS the layers for identification of the locus of peel front propagation. Thermal properties were analyzed using TGA (thermo-gravimetric analyses). Finally, the fire-retardant properties of such thick coated polymers were evaluated by exposure to flames.
First goal of this work was to produce thick fire-resistant coatings, which are able to withdraw the direct contact to flames. Preliminary tests had shown that thicknesses more than 10 μm are needed to measure effects on flammability. Here, 40 μm thick layers are prepared. The adhesion of such thick layers mainly depends on the use of surface treatment of polyolefin substrates. Plasma exposure and deposition of plasma polymer layers are easiest and most efficient methods to promote the adhesion of thick layers used for the fire protection of materials. Indeed, plasma processing doesn’t modify the intrinsic properties of materials such as the mechanical properties, easily processed, and can be applied over a wide range of materials even though for metals.
To achieve very high adhesion of such thick coatings to the polymer substrates it has to be considered that the chemical nature of coating and polymers is different, strong different thermal expansion coefficients exist and therefore adhesion was most oftenabsent.
Melt flow and dripping of the pyrolysing polymer melt can be both a benefit and a detriment during a fire. In several small-scale fire tests addressing the ignition of a defined specimen with a small ignition source, well-adjusted melt flow and dripping are usually beneficial to pass the test. The presence of flame retardants often changes the melt viscosity crucially. The influence of certain flame retardants on the dripping behaviour of four commercial polymers, poly(butylene terephthalate) (PBT), polypropylene (PP), polypropylene modified with ethylene-propylene rubber (PP-EP) and polyamide 6 (PA 6), is analysed based on an experimental monitoring of the mass loss due to melt dripping, drop size and drop temperature as a function of the furnace temperature applied to a rod-shaped specimen. Investigating the thermal transition (DSC), thermal and thermo-oxidative decomposition, as well as the viscosity of the polymer and collected drops completes the investigation. Different mechanisms of the flame retardants are associated with their influence on the dripping behaviour in the UL 94 test. Reduction in decomposition temperature and changed viscosity play a major role. A flow limit in flame-retarded PBT, enhanced decomposition of flame-retarded PP and PP-EP and the promotion of dripping in PA 6 are the salient features discussed.
Polyesters with DOPO substituents can be successfully synthesized with 10-[2,5-Bis(2-hydroxyethoxy)phenyl]-9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide(DOPO-HQ-glycolether) and DOPO-substituted dimethyl succinate (PIta). These polyester materials show an effective flame retardancy which can be fine-tuned by the chemical structure of the polyester backbone.