Electrochromic thin films of metallo-supramolecular polyelectrolytes based on Fe(OAc)2 and 1,4-bis(2,2':6',2''-terpyridin-4'-yl)benzene are readily prepared by layer-by-layer (LbL) deposition or dip-coating on transparent conducting electrode surfaces. By applying a potential, we can switch the color of the films from blue to colorless. Because of the strong absorption and the fast switching speed, the color change can be observed with the eye. The devices show reversible switching and cycle stability.
Metal ion induced self-assembly of iron(II)-acetate with the rigid ditopic ligand 1,4-bis(2,2':6',2''-terpyridin-4'-yl)benzene results in a metallo-supramolecular coordination polyelectrolyte (Fe-MEPE). Fe-MEPE shows a strong absorption band in the visible region around 590 nm, attributed to a metal-to-ligand-charge-transfer (MLCT) transition, which is responsible for the deep blue colour. Large area thin films of high optical quality can be readily fabricated by a dip coating process on transparent conducting electrodes. The Fe-MEPE films have a temperature stability up to 80 °C, measured by optical spectroscopy and XAFS (x-ray absorption fine structure). The cathodically coloured Fe-MEPE shows outstanding electrochromic properties and can be reversibly switched from Fe(II) (blue) to Fe(III) (colourless) by applying a potential of 4.1 V vs. Li/Li+. A very high optical contrast ΔT of 71% at a wavelength of 590 nm and a colouration efficiency of around 525 cm² C-1 can be realized. The devices show a long-term stability about 10,000 cycles. Thus, Fe-MEPE is a very promising electrochromic material for future applications of smart windows.
First goal of this work was to produce thick fire-resistant coatings, which are able to withdraw the direct contact to flames. Preliminary tests had shown that thicknesses more than 10 μm are needed to measure effects on flammability. Here, 40 μm thick layers are prepared. The adhesion of such thick layers mainly depends on the use of surface treatment of polyolefin substrates. Plasma exposure and deposition of plasma polymer layers are easiest and most efficient methods to promote the adhesion of thick layers used for the fire protection of materials. Indeed, plasma processing doesn’t modify the intrinsic properties of materials such as the mechanical properties, easily processed, and can be applied over a wide range of materials even though for metals.
To achieve very high adhesion of such thick coatings to the polymer substrates it has to be considered that the chemical nature of coating and polymers is different, strong different thermal expansion coefficients exist and therefore adhesion was most oftenabsent.