It has been shown that tetraethoxysilane-derived precursors are suitable solutions for impregnating pine sapwood to improve its dimensional stability. Tailored sol–gel syntheses result in precursors with nano-scaled silica species which are able to penetrate into the cell walls of wood. The physical fixation of those species inside the cell walls was verified by ESEM/EDX investigations. There is evidence that the silica species are chemically bonded to wood components. Nonreacted alkoxy groups can exist in the wood composites after impregnation. The amount of these organic residues depends on the composition of the precursors, especially their condensation degree and reactivity. Treatments for finishing the composites after the impregnation step to get clean products and stable properties are discussed in this context. An explanation of the complex relationship between solids content in the impregnation solutions and percentage weight gain and bulking of the composites is given. It can be demonstrated that high WPG values (>20 %) are pre-conditions for an effective protection of the resulting composites but they only guarantee efficient improvements if connected with the incorporation of the inorganic component inside the cell walls. Therefore, the sol–gel syntheses have to be carried out in such a manner that very small (<2 nm) as well as reactive species are sufficiently available. This demands syntheses using sub-stoichiometric water contents (H2O/TEOS <4, better <2).
Thermosetting materials are gaining increasing attention in many structural composite applications. However, the incorporation of inorganic nanoparticles (NPs) into polymer matrix is a promising approach to enhance their functional characteristics, and thus, to enable the development of thermosets advanced application. It has been shown that Boehmite Alumina (BA) used as nanofillers can improve different parameters of polymers. This NPs can be easily tailored enabling desirable interactions with a big range of polymers. However, the overall effect of nanofiller depends on many factors, therefore, making it hard to predict the resulted performance of nanocomposites. In the current contribution we would like to discuss the impact of Boehmite NPs on two different epoxy resin nanocomposite systems with the focus on the possible influence mechanisms of this nanofiller.
As the first system, UV curable Cycloaliphatic-Epoxy Oligosiloxane (CEOS) resin/Boehmite nanocomposites were investigated by FTIR, TGA, DSC and T-SEM. It was observed that incorporation of BA leads to the reinforcement of glass transition (Tg) and overall thermal stability indicating the attractive interactions between BA and CEOS network. In addition, an increase in epoxy conversion of CEOS was concluded for nanocomposites assuming that particles are involved in UV polymerisation processes.
The second epoxy/Boehmite nanocomposite is based on the bisphenol-A-diglycidyl ether (DGEBA) cured with methyl tetrahydrophtalic acid anhydride (MTHPA). Thermomechanical as well as nanomechanical properties of this material were investigated by DMTA and IR spectroscopy and the advanced Intermodulation AFM, respectively. In contrast to the first system, it was found that BA leads to a decrease of Tg and crosslink density of the polymer while the young’s modulus of the composite and local stiffness of polymer matrix increase significantly.
As a result, the versatile role of Boehmite was detected depending on the investigated systems. Based on the obtained results, the parameters indicating property-efficient epoxy/Boehmite system are suggested.
Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon-fibre fabric impregnated with reactive epoxy resin. DMA measurements under temperature conditions similar to an autoclave programme were carried out using commercially available prepreg material with a high glass transition temperature. The characteristic of the temperature programme was a dynamic heating segment at 1.5 K/min followed by a longer isothermal segment at 180 °C. The courses of the storage modulus E', loss modulus E'' and tanδ were recorded. The measuring frequency was varied between 1 Hz and 33.3 Hz. Gelation and vitrification are assigned. The influence of the measuring frequency on the time to vitrification and the correlation with DSC are discussed. The reaction does not end even after 10 h curing at 180 °C, which is interpreted as the slow cessation of the reaction caused by vitrification.
Non-destructive evaluation (NDE) of composites: using ultrasound to monitor the curing of composites
(2013)
Typical composite materials for lightweight construction consist of a fibre (glass or carbon) reinforced thermosetting matrix. The impregnation of the fabric is made with liquid resin – usually epoxy resin or unsaturated polyester resin are used. The main processing methods are resin transfer moulding (RTM) and prepreg technology often used in combination with autoclave curing. After shaping, the resin must be cured. The final properties of the produced parts depend on the curing degree and the final glass transition temperature. Analytical methods and the use of ultrasound for online cure monitoring in the manufacturing process are introduced. Examples for the application of ultrasonic cure monitoring for the production of composite parts for traffic systems are also covered.
Melamine resins were used as 50-µm-thick fire retardant coatings for polypropylene (PP). Preceding deposition, low-pressure plasma polymer films of allyl alcohol were coated onto PP to improve the adhesion between PP and melamine resin coatings. The efficiency of such fire retardant coatings was confirmed by flame tests. The plasma-deposited polymer and the dip-coated melamine resin films were characterized by Fourier transform infrared-attenuated total reflectance spectroscopy and X-ray photoelectron spectroscopy (XPS). The adhesion of coatings was measured using a 90° peel test with a doubled-faced adhesive tape. To detect the locus of failure, the peeled layer surfaces were inspected using optical microscopy and XPS. Thermal properties of PP thick melamine resin-coated films were analyzed by thermogravimetric analysis.
Melamine and melamine resins are widely used as fire-retardants for polymer building materials. Cured melamine systems are used in heat-sensitive items, such as furniture and window frames and sills. In this work, differently cured methylated poly(melamine-co-formaldehyde) (cmPMF) resins were used as fire-retardant coverage for poly(styrene) (PS) and poly(ethylene) (PE) building materials. Such polymer layers should have several tenths of micrometers thickness to produce sufficient fire retardancy. These thick layers were produced by dip-coating. To promote sufficient adhesion of such thick coating to the polyolefin substrates, also in the case of high temperatures occurring at fire exposure, the polymer substrates were firstly coated with a few hundred nanometer thick adhesion-promoting plasma polymer layer. Such thin plasma polymer layers were deposited by low-pressure plasma polymerization of allyl alcohol (ppAAl). It was assumed that the hydroxyl groups of ppAAl interact with the melamine resin; therefore, ppAAl was well suited as adhesion promoter for thick melamine resin coatings. Chemical structure and composition of polymer films were investigated using infrared-attenuated total reflectance and X-ray photoelectron spectroscopy (XPS). Peel strengths of coatings were measured. After peeling, the peeled polymer surfaces were also investigated using optical microscopy and XPS the layers for identification of the locus of peel front propagation. Thermal properties were analyzed using TGA (thermo-gravimetric analyses). Finally, the fire-retardant properties of such thick coated polymers were evaluated by exposure to flames.