The RILEM TC 281–CCC "Carbonation of concrete with supplementary cementitious materials" is studying the effect of supplementary cementitious materials (SCMs) on natural and accelerated carbonation of blended cements. In this context a large database with carbonation depths over time has been set-up with currently 910 concrete and mortar mixes, which have been tested at different curing conditions. The collected data includes information on chemical composition and physical properties of the raw materials, on mix-design, compressive strength, curing and carbonation testing conditions. Data for a large variety of binders (with up to 94 % SCMs) and mix designs (with w/b ratios ranging from 0.26 to 0.75) were collected from the literature and unpublished material testing projects. Natural carbonation was recorded for several years in many cases, and indoor as well as outdoor results are included. However, in this contribution only lab conditions are considered. Carbonation kinetics are investigated considering the binder composition and mix design. Furthermore, the accuracy of accelerated carbonation testing is evaluated. As described in literature, the w/CaOreactive-ratio is a decisive factor for carbonation resistance but curing and exposure conditions influence the results as well. Even with identical test conditions, the scatter is very large.
While calcined clays in general have been credited with a great potential to mitigate CO2 emissions related to cement production and consumption, calcined brick clays are currently understudied in this regard. In the present work, two brick clays, a low-grade kaolinitic clay, and a mixed clay composed of 50% brick clay and 50% low-grade kaolinitic clay were studied regarding transformations on calcination, and strength and durability performance as well as pore structure of mortars made with the blended cements. All calcined clays exhibited pozzolanic reactivity, with the performance of the brick clays inferior to the low-grade kaolinitic clay. However, the mixed clay performed very similar to the low-grade kaolinitic clay, which points to a viable option for optimal use of brick clays in cementitious systems. The carbonation resistance of the blended cement mortars was generally worse than that of the plain Portland cement mortar, as expected, but the former exhibited a significantly improved chloride penetration resistance. The latter improvement was due to pore structure refinement in the blended cement mortars, compared to the Portland cement mortar.
The use of calcined clays as supplementary cementitious materials (SCMs) has been identified as a viable option to decrease the CO2 emissions related to cement production. However, while extensive data is available about kaolinitic clays in this context, other clays such as illitic clays appear to be under-studied. Therefore, in the present study, two illitic clays were compared to two low-grade kaolinitic clays in terms of transformations in the calcination temperature range 650–900 °C, and performance of the calcined clays in blended cement pastes as measured by strength evolution, heat release, hydrated phase formation and portlandite consumption. The illitic clays required a higher calcination temperature for complete dehydroxylation of their illite than what is necessary for dehydroxylation of kaolinite. These higher calcination temperatures also led to particle sintering, significantly decreasing the specific surface area of the illitic clays, particularly for the clay with the higher Fe2O3 content. Nevertheless, while the kaolinitic clays generally exhibited the best performance as SCM, the illitic clay with lower Fe2O3 content performed similar to the kaolinitic clays when calcined at optimum temperature and applied at a moderate substitution rate. These findings demonstrate that several different clays have the potential to be used as SCM and indicate possible routes to identify suitable deposits for this purpose.
Calcined clays as supplementary cementitious materials (SCMs) have been identified and credited to be a viable solution in mitigating the CO2 emissions related to cement production and consumption. Calcined clays range from a variety of different clay types based on an assortment of varying minerals and compositions. While extensive data is available on kaolinitic clays (based on the 1:1 clay type), other clays such as brick clays (based on the 2:1 clay type) are currently understudied, although such clays are largely more available than the kaolinitic clays.
The aim of this thesis is to draw attention to the varying compositions present in two selected brick clays in Germany and elaborate on how such compositions affect their suitability to be used as SCMs in blended cement systems. The novelty of this thesis explains the relationship between the reactivity of the bricks to their varying compositions and their suitability for their employment as SCMs. This was based on their chemical and physical transformations in the calcination temperature range 650–900 or 950 °C, and the performance of the calcined brick clays in blended cement systems measured by their heat evolution, strength development and durability-related properties. The results of their performance were compared to two kaolinitic clays with varying compositions. While the kaolinitic clays generally exhibited the best performance as SCMs, the brick clay with a lower Fe2O3 content showed promising results similar to the kaolinitic clays when an optimum calcination temperature is applied and when substituted at a moderate cement substitution rate. Thus, this finding promoted further efforts made to improve the reactivity of the brick clay by producing a mixed clay composed of 50 % brick clay (with lower Fe2O3 content) and 50 % kaolinitic clay. The mixed clay was compared to the two individual brick clays and one kaolinitic clay, whereby optimum calcination conditions were performed in large-scale simulating an industrial-scale production of SCMs. All calcined clays exhibited pozzolanic reactivity, with the performance of the brick clays inferior to the kaolinitic clay, however, the mixed clay performed very similar to the kaolinitic clay.
At a similar degree of hydration compared to plain Portland cement, the good performance of the mixed clays was especially evident in the strength development and improved chloride penetration resistance, which was caused by a refinement in the pore structure in the cementitious systems. Moreover, it was deduced that not only the high surface area, but also, the solubility of Si and Al ions in the resulting calcinate of the mixed clays plays a significant role when calcined at ~600–700 °C, which points to viable options for optimal employment of brick clays in cementitious systems.
Ingress of moisture and harmful ions (e.g. Chloride, sulfate) into cementitious materials is one of the major factors in defining their durability. Modifications of building materials by targeted deposition of surface functional agents that make the surface hydro- and/or oleophobic aim to minimize moisture and ion ingress, and thus extend Service life of the cement based structures. Water repellent and easy-to-clean coatings for inorganic Substrates have gained strong attention during the last few years and various formulations based on silicones or alkylpolysiloxanes have been developed. Cementitious building materials are highly complex Systems with many components and changing properties in the course of a building’s Service life. The interactions between the Chemical agents and the cement based materials depend on many factors. The Chemical properties of the material Substrate appear to be the most important but in the context of their influence on the functionality of silanes and/or siloxanes these characteristics have not been well understood yet. The aim of this study was to evaluate the effect of different blended cements on water repellent agents’ performance. Two organosilicon compounds
were applied on fresh blended cements containing limestone (L), fly ash (F), slag (S) and trass (T), and investigated in terms of their functionality.
The surface properties of functionalized blended cements were studied based on wettability, i.e. contact angle measurements, before and after exposure to artificial and natural weathering. The first results indicate that slag and trass more distinctly affect the water repellent Surface performance after aging.
The paper presents the results of a study dealing with the performance of water repellents on hardened blended cement pastes. Since on the European market Portland cement does not play the dominant role anymore and due to the new national and European policies concerning Greenhouse Gases and sustainability, cement manufacturers produce more and more blended cements (CEM IICEM V). Nevertheless, the majority of experience concerning the efficacy of water repellents is gained from Portland cement; therefore knowledge in regard to the interactions of blended cement with water repellent agent is minimal. Two silane-based products were applied on 'fresh' and carbonated cement substrates containing limestone, fly ash, slag and trass, and were investigated in terms of their functionality. The evaluation of the treatments' performance and effectiveness were assessed using various laboratory measurements. Hydrophobicity, water absorption, colour changes and the penetration depth of silanes into the substrate were evaluated before and after artificial aging experiments. Moreover, the outdoor weathering test was performed to shed light on treated surface appearance in a 'real' outdoor environment. The results showed that surface wettability was independent on water ingress or colour variations, especially for cement specimens artificially aged by accelerated carbonation. Cement pastes containing slag and trass seemed to more distinctly affect the water repellents' surface performance.