The results of a collaborative research project on laser beam weldability of carbon steels of high sheet thickness are presented. That includes single and multiple pass welding of 16 mm and 20 mm thick plates, as well as the investigation of acceptable tolerances i.e. gap bridgeability and edge misalignment. For the welding experiments fibre lasers with 8 kW, 20 kW laser power and different GMAW-techniques were used in various applications. With the 20 kW fibre laser 16 mm plates could be welded with a single pass, 20 mm required a seam preparation or alternatively preheating of the material. For multi pass welding with 8 kW laser power a joint preparation with a single V-butt joint with a broad root face (Y-groove) was applied. The root pass was always welded with a hybrid process, the filler passes with a hybrid process as well as a GMAW process which produced the best results.
Life Cycle Assessment (LCA) is applied in evaluating environmental impacts of state-of-the-art welding technologies. Manual Metal Arc Welding (MMAW), Laser Arc-Hybrid Welding (LAHW) and two Gas Metal Arc Welding (GMAW) variants are used to join a plate of 20 mm thick structural steel. The LCA results indicate that for 1 m weld seam, MMAW causes the highest environmental impacts in global warming potential (GWP), eutrophication potential (EP), acidification potential (AP), and photochemical ozone creation potential (POCP) among the selected processes, and the LAHW variant performances the least. Filler material and electricity consumptions generally dominate the impacts and reach shares of up to 80% and 61% in the respective impact categories. However, electrode coating consumption in MMAW remarkably contributes impacts on AP and EP, for instance 52% of AP and 76% of EP. Strategies for improvement of the applied welding technologies are discussed.
Welding is the most important joining technology. In the steel construction
industry, e.g. production of windmill sections, welding accounts for a
main part of the manufacturing costs and resource consumption. Moreover, social
issues attached to welding involve working in dangerous environments. This aspect
has unfortunately been neglected so far, in light of a predominant focus on economics
combined with a lack of suitable assessment methods. In this chapter,
exemplary welding processes are presented that reduce the environmental and
social impacts of thick metal plate welding. Social and environmental Life Cycle
Assessments for a thick metal plate joint are conducted for the purpose of
expressing and analysing the social and environmental impacts of welding.
Furthermore, it is shown that state-of-the-art technologies like Gas Metal Arc
Welding with modified spray arcs and Laser Arc-Hybrid Welding serve to increase
social and environmental performance in contrast to common technologies, and
therefore offer great potential for sustainable manufacturing.
Life cycle assessment of fusion welding processes considering upstream and downstream process steps
(2023)
In manufacturing, fusion welding processes consume significant resources, presenting a significant opportunity for reducing environmental impact. Although there is a qualitative understanding of the environmental implications of these processes, a quantitative assessment of key parameters remains complex. This study introduces a welding-specific methodology that employs life cycle assessment (LCA) to quantitatively evaluate the environmental footprint of fusion welding technologies. Our approach identifies and analyses the principal parameters affecting the environmental performance of various welding techniques, including traditional joint welding and additive manufacturing via the Direct Energy Deposition-Arc (DED-Arc) process. Real-time resource usage data is integrated to offer an innovative framework for directly deriving environmental impacts. This research contributes to optimising welding processes by providing a precise and quantifiable measure of their ecological impact. This facilitates the advancement of sustainable manufacturing practices.
Hot crack prevention in materials production and processing is an essential prerequisite for welded component safety. The causes of hot cracking can ultimately be attributed to the occurrence of metallurgical effects and to structural loads. More than 140 hot cracking test procedures have hitherto been developed for determining the hot cracking resistance. In principle, they are divided in self-restraint and externally loaded hot cracking tests with diverse process variants. Only some of the hot cracking tests are international standardized. Although various factors are known that encourage or prevent hot cracking, it is often not possible even with defined welding conditions to draw immediate conclusions about the hot cracking resistance of a welded component alone from a metallurgical composition of the base and filler materials. Based on an evaluation of the existing theories relating to hot cracking susceptibility assessment, this study summarizes the major hot cracking test procedures and highlights the application limits of the test procedures by presenting overviews along with explanations. It shows that weld hot cracking tests can generally be used to rank materials, welding consumables, and welding conditions. The evaluation of hot cracking test results and of their transferability among one another and to real components always requires consideration of the close relationships between metallurgy, welding process, and parameters, respectively, and prevailing restraint conditions.
The talk gives an introduction into gas metal arc welding and its relation to plasma science as well as current challenges in welding research concerning research data management and the application of the FAIR principles.
The WelDX project is introduced and the main goals are discussed and contrasted with the current features of the weldx API.
Different internal and public facing use cases focusing on research data management and their implementation using weldx are presented.
The interactive part of the presentation displays some advanced multi layer use cases and data analysis using the weldx API as well as the integration of materials properties into weldx.
The presentation shows the current development status of the Welding Data Exchange (weldx) format based on the Advanced Scientific Data Format (ASDF).
The use of a complete single pass arc welding experiment example stored in a single weldx file and validated against a predefined schema definition is presented.
The example includes generic experimental metadata, the workpiece geometry and materials definition following associated standards, the weld process spatial movement description, the welding process parameter descriptions and welding process measurements. The inclusion of 3D scan data of the workpiece description is also included.
The full code and data is available on GitHub: https://github.com/BAMWelDX/IIW2021_AA_CXII
The presentation shows the current development status of the Welding Data Exchange (weldx) format based on the Advanced Scientific Data Format (ASDF).
The use of a complete single pass arc welding experiment example stored in a single weldx file and validated against a predefined schema definition is presented.
The example includes generic experimental metadata, the workpiece geometry and materials definition following associated standards, the weld process spatial movement description, the welding process parameter descriptions and welding process measurements. The inclusion of 3D scan data of the workpiece description is also included.
The full code and data is available on GitHub: https://github.com/BAMWelDX/IIW2021_joint_intermediate_CXII
The talk motivates and introduces the WelDX project and the proposed solutions for current challenges in the field of research data management and Open Science practices in welding research.
Using an exemplary welding dataset based on the joint and welding process design of offshore structures, advanced data fusion and analysis capabilities are demonstrated.
The dataset shown consists of a complex welding sequence covering multiple weld layers with varying process parameters and adaptive weaving motions to cover manufacturing tolerances. In the presentation, an interactive exploration of the dataset contents in the spatial domain is presented. Furthermore, transformation between spatial and time domain of the data is demonstrated.
In addition to data gathered during the welding process, the integration of downstream testing data and results is also explained. For demonstration, integration of weld seam cross section images and Vickers hardness mapping test results into the dataset are explained an demonstrated. The testing data is set into context with the welding process information.
Finally, implications for advancements in research data management for WAAM and AI applications are discussed.