Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (16)
- Beitrag zu einem Tagungsband (15)
- Dissertation (1)
- Posterpräsentation (1)
Schlagworte
- Geopolymers (10)
- Alkali-activated materials (8)
- Alkali-activation (3)
- Monitoring (3)
- One-part geopolymers (3)
- One-part mix (3)
- SealWasteSafe (3)
- Acid resistance (2)
- Blended cement (2)
- Brick clay (2)
- Brown Coal Fly Ash (2)
- Calcined clay (2)
- Evaporite rock (2)
- Hybrid cements (2)
- Lignite Coal (2)
- One-part formulation (2)
- Rice husk ash (2)
- Zeolite Na-A (2)
- Zeolites (2)
- 27Al MAS NMR (1)
- 29Si MAS NMR (1)
- AAM (1)
- Abwasserinfrastruktur (1)
- Acid-resistance (1)
- Acoustic emission (1)
- Additive manufacturing (1)
- Alkali activated materials (1)
- Alkali-activated binders (1)
- Alkali-activated mortars (1)
- Alkaliaktivierte Bindemittel (1)
- Aluminium hydroxide (1)
- Aluminosilicate inorganic polymers (1)
- Bio-based materials (1)
- Biogene Schwefelsäurekorrosion (1)
- Blended cements (1)
- Bond strength (1)
- Borehole probe (1)
- Calcined clays (1)
- Cement (1)
- Chemical durability (1)
- Coatings (1)
- Concrete (1)
- Corrosion (1)
- Degree of reaction (1)
- Dissolution (1)
- Drying (1)
- Embedded sensors (1)
- Engineered barrier (1)
- Engineered barriers (1)
- Fibre optic sensing (1)
- Fire protection (1)
- Fire resistance (1)
- Geopololymers (1)
- Heat-resistance (1)
- High-temperature resistance (1)
- High-temperature treatment (1)
- Hybrid alkaline cement (1)
- Hybride Zemente (1)
- Hydratationswärme (1)
- Hydration (1)
- Hygric deformations (1)
- Illite (1)
- Illitic clay (1)
- Intumescence (1)
- Kalorimetrie (1)
- Kaolinite (1)
- Laser-induced slip casting (1)
- Magnesium chloride (1)
- Magnesium chloride brine (1)
- Materials technology (1)
- NMR (1)
- Nepheline (1)
- Nuclear magnetic resonance (1)
- Nuclear waste repository (1)
- Nuclear waste storage (1)
- Passive sensor interface (1)
- Portland clinker (1)
- Provenancing (1)
- REDOR (1)
- RFID (1)
- RFID technology (1)
- Repair mortars (1)
- Reparatursysteme (1)
- Rheology (1)
- Salt attack (1)
- Sealing structures (1)
- Sewer repair (1)
- Silica (1)
- Smart structures (1)
- Solid-state NMR (1)
- Spectroscopy (1)
- Sr isotopes (1)
- Structural health monitoring (1)
- Strätlingite (1)
- Sulfuric acid resistance (1)
- Supplementary cementitious materials (1)
- Supplementary cementitous materials (1)
- Thermal behavior (1)
- Thermal properties (1)
- Thermodynamic modelling (1)
- Ultrasonic imaging (1)
- Ultrasound (1)
- Workability (1)
- alkali-activated material (1)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (19)
- 7.4 Baustofftechnologie (19)
- 6 Materialchemie (4)
- 6.3 Strukturanalytik (4)
- 8 Zerstörungsfreie Prüfung (4)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (3)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (3)
- 8.6 Faseroptische Sensorik (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.1 Anorganische Spurenanalytik (1)
Paper des Monats
- ja (2)
The passive fire protection of steel structures and other load-bearing components will continue to gain importance in future years. In the present contribution, novel intumescent aluminosilicate (geopolymer-bound) composites are proposed as fire-protective coatings on steel. Steel plates coated with these materials were exposed to the standard temperature-time curve as defined in ISO 834 – 1:1999. The coatings partially foamed during curing and expanded further during thermal exposure, demonstrating their intumescent characteristic.Thermogravimetryandoscillatory rheometry determined that the intumescent behavior is attributed to a transition to a viscous state (loss factor > 1) in the temperature range of major water release, differing from conventional geopolymers. XRD and SEM images showed that the coatings had characteristics of ceramic or glass-ceramic foams after fire resistance testing, suggesting superior performance under challenging conditions. The thickness of the coatings influenced their foaming and intumescent behavior and thus the time for the coated steel plates to reach 500 °C. A number of additives were also studied with the best performance obtained from samples containing sodium tetraborate.Acoating of just 6mmwas able to delay the time it takes for a steel substrate to reach 500 °C to more than 30 minutes.
Properties of alkali-activated mortars with salt aggregate for sealing structures in evaporite rock
(2021)
Concrete structures for sealing of tunnels in the host rock are an essential part of systems for nuclear waste storage. However, concretes based on blended cements or magnesium oxychloride cements, which are commonly considered for this application, can deteriorate severely due to a significant heat of hydration and associated deformation and cracking. Alkali-activated materials (AAMs) offer a potential solution to this problem because of their low heat release during hardening. To explore their suitability for the construction of sealing structures in evaporite rock, various AAMs with salt aggregate were studied regarding fresh properties, heat release, mechanical properties and microstructure. The heat of reaction of the AAMs was up to 55% lower than that of a blended cement designed for sealing structures, indicating significant benefits for the intended application. Other relevant properties such as mechanical strength and permeability depended strongly on the mix-design of the AAMs and curing conditions.
One-part geopolymers were synthesized from two different silica materials (a silica-rich residue from chlorosilane production and a commercial microsilica) and sodium aluminate at three different SiO2/Al2O3 ratios and a nominal water/solids ratio of 0.5. The degree of reaction of the silica in the cured geopolymers (i.e. the fraction of silica dissolved to form aluminosilicates and minor products) was determined using two different methods: chemical attack with HCl to dissolve the reaction products and evaluation of peak areas of 29Si MAS NMR spectra. It was found that the degree of reaction of the silica decreases with increasing the silica content of the starting mix, and that it is almost constant after 1 day of curing and almost independent from the kind of starting silica. From the results of the NMR-based method, the mean SiO2/Al2O3 ratio of the reaction products (aluminosilicates and minor products) can be estimated to be ca. 2.0, nearly independent of the starting composition of the geopolymers. The dissolution method is biased, but of sufficient precision to be useful for following changes of the degree of reaction. Major crystalline phases in the cured geopolymers are zeolite A and/or hydrosodalite. Depending on the starting composition, the relative amounts of these zeolites vary; additionally, sodalite (only for the residue from chlorosilane production with >1 wt% Cl-), faujasite, and zeolite EMT can appear in the geopolymers. The 29Si and 27Al MAS NMR results indicate mainly Si(4Al) and Al(4Si) sites, in line with the presence of zeolite A, hydrosodalite, sodalite, and geopolymeric gel of comparatively low SiO2/Al2O3 ratio.
This contribution presents the results of structural and compressive strength investigations on cured andhigh-temperature treated silica-based one-part geopolymer-zeolite composites. The specimens weresynthesized from two different silica sources, sodium aluminate and water. The phase content as well asthe compressive strength of the cured composites varied depending on the starting mix-design and thesilica feedstock. Besides geopolymeric gel, A-type zeolites and hydrosodalites were the major reactionproducts. One of the silica feedstocks yielded significantly higher compressive strength (19 MPa), whilethe other one appears to cause less variation in phase content. Strength testing indicated an improvementon heating up to
200–400 °C (28 MPa) followed by a moderate decrease up to 700 °C. Above 700 °C the sys-tems underwent new phase formation and shrinkage (volume decrease) deformations. After exposureat 1000 °C the different mixes consisted of a mix of several stuffed silica phases, almost pure hexago-nal nepheline or amorphous phase. Depending on the mix-design, the onset temperature of the hightemperature phase transformations varied.
One-part alkali-activated (geopolymer) mortars based on three different silica-rich starting materials and sodium aluminate, with and without ground granulated blast furnace slag (GGBFS) addition, were tested regarding sulfuric acid resistance according to DIN 19573:2016-03 (70 days at pH = 1). Corresponding pastes were characterized by XRD, SEM, chemical analysis, 29Si MAS NMR and 1H-29Si CPMAS NMR after water storage and after acid exposure. The mortars exhibited a high resistance against sulfuric acid attack, with the best ones conforming to the requirements of DIN 19573:2016-03. The analytical results showed that this was due to precipitation of silica gel at the acid-mortar interface, which formed a mechanically stable layer that protected the subjacent mortar and thus inhibited further degradation. The addition of GGBFS decreased the acid resistance via formation of expansive calcium sulfate phases.
One-part geopolymers, synthesized from three different silica sources and sodium aluminate, were investigated regarding their microstructure and the evolution of their compressive strength on curing at slightly elevated temperatures. The effect of thermal treatment was studied up to 1000 °C and for the investigation of the chemical durability specific samples were treated with sulfuric acid (H2SO4, pH = 1).
Depending on the silica feedstock, different degrees of reaction were observed. One of the silicas had a significantly higher reactivity. For two of the silicas, significant amounts of zeolites occurred as reaction products besides geopolymeric gel, whereas the more reactive silica source lead to the formation of a rather fully condensed geopolymeric network.
The composites indicated promising behavior on heating in so far as no distinct shrinkage step occurred in the temperature range of dehydration. Up to 400 °C the residual strength of those mixes increased. Above 800 °C the samples underwent new phase formation. After exposure to sulfuric acid (pH 1; 70 d) specimens showed a residual compressive strength of about 77 % of the reference, indicating high acid resistance.
One-part geopolymers offer advantages over conventional geopolymers with regard to handling and storage of feedstocks. However, they often suffer from a low degree of reaction, a high amount of crystalline byproducts, and consequently low strength. In this study, one-part geopolymers were produced from rice husk ash (RHA) and sodium aluminate, and investigated by XRD, ATR-FTIR, SEM and compressive strength testing. The compressive strength of the material was 30 MPa, i.e. significantly higher than for comparable one-part geopolymers. This is attributed to an almost complete reaction of the RHA and the absence of crystalline byproducts (zeolites) in the hardened geopolymer.
Geopolymers are promising alkali activated materials with a wide range of possible applications like heat-resistant coatings and adhesives or concretes with lower C02 emissions than conventional Portland cement-based systems. Conventional ("two-part") geopolymers are synthesized by an activation of aluminosilicate feedstocks like metakaolin or blast furnace slags with highly alkaline solutions like sodium hydroxide solutions and/or water glass solutions.
A more recent approach are so called one-part geopolymers, where the alkaline activator is provided in solid form, so that only water has to be added to initiate the geopolymerisation reaction. The handling of alkaline solutions is avoided, which possesses several advantages compared to conventional geopolymers, in particular regarding safety and health issues, and, thus, it improves economic and social acceptance of these binders. However, the new formulations are less exhaustively studied and the knowledge about conventional geopolymers cannot simply be transferred to this new class of binders.